2019 High quality Chemical Composition - Seamless, welded and hot-dip galvanized pipe – Sanonpipe
2019 High quality Chemical Composition - Seamless, welded and hot-dip galvanized pipe – Sanonpipe Detail:
Overview
Application
It Is Mainly Used for force and pressure parts, and for general purpose steam, water, gas and air pipes.
Main Grade
GR.A, GR.B
Chemical Component
|
Grade |
Component %，≤ | ||||||||
| C | Mn | P | S |
CuA |
NiA |
CrA |
MoA | VA | |
| S type（seamless pipe） | |||||||||
| GR.A | 0.25B | 0.95 | 0.05 | 0.045 |
0.40 |
0.40 |
0.40 |
0.15 | 0.08 |
| GR.B | 0.30C | 1.20 | 0.05 | 0.045 |
0.40 |
0.40 |
0.40 |
0.15 | 0.08 |
| E type（Resistance welded pipe） | |||||||||
| GR.A | 0.25B | 0.95 | 0.05 | 0.045 |
0.40 |
0.40 |
0.40 |
0.15 | 0.08 |
| GR.B | 0.30C | 1.20 | 0.05 | 0.045 |
0.40 |
0.40 |
0.40 |
0.15 | 0.08 |
| F type（Furnace Welded Pipe） | |||||||||
| A | 0.30B | 1.20 | 0.05 | 0.045 |
0.40 |
0.40 |
0.40 |
0.15 | 0.08 |
A The sum of these five elements must not be greater than 1.00%。
B For every 0.01% decrease in the maximum carbon content, the maximum manganese content is allowed to increase by 0.06%, but the maximum cannot exceed 1.35%.
C Each 0.01% decrease in the maximum carbon content will allow the maximum manganese content to increase by 0.06%, but the maximum must not exceed 1.65%.
Mechanical Property
| item | GR.A | GR.B |
|
tensile strength, ≥, psi [MPa] Yield Strength, ≥, psi [MPa] Gauge 2in.or 50mm elongation |
48 000 [330]30 000 [205]A,B | 60 000 [415]35 000 [240]A,B |
A The minimum elongation of gauge length 2in. (50mm) shall be determined by the following formula：
e=625000(1940)A0.2/U0.9
e = the minimum elongation of the gauge 2in. (50mm), the percentage rounded to the nearest 0.5%;
A = Calculated according to the specified outer diameter of the nominal tube or the nominal width of the tensile sample and its specified wall thickness, and rounded to the nearest cross-sectional area of the tensile sample of 0.01 in.2 (1 mm2), and It is compared with 0.75in.2 (500mm2), whichever is smaller.
U = specified minimum tensile strength, psi (MPa).
B For various combinations of different sizes of tensile test specimens and prescribed minimum tensile strength, the required minimum elongation is shown in Table X4.1 or Table X4.2, according to its applicability.
Test Requirement
Tensile test, bending test, hydrostatic test, nondestructive electrical test of welds.
Supply Ability
Supply Ability: 2000 Tons Per Month Per Grade Of ASTM A53/A53M-2012 Steel Pipe
Packaging
In Bundles And In Strong Wooden Box
Delivery
7-14 days if in stock, 30-45 days to produce
Payment
30% depsoit, 70% L/C or B/L copy or 100% L/C at sight
Product Detail
Boiler Tube
GB/T 8162-2008
ASTM A519-2006
BS EN10210-1-2006
ASTM A53/A53M-2012
GB9948-2006
GB6479-2013
GB/T 17396-2009
Product detail pictures:
Related Product Guide:
Our crew through skilled training. Skilled skilled knowledge, strong sense of company, to meet the company wants of customers for 2019 High quality Chemical Composition - Seamless, welded and hot-dip galvanized pipe – Sanonpipe , The product will supply to all over the world, such as: belarus , Cape Town , Accra , Our advantages are our innovation, flexibility and reliability which have been built during last 20 years. We focus on providing service for our clients as a key element in strengthening our long-term relationships. The continual availability of high grade products in combination with our excellent pre- and after-sales service ensures strong competitiveness in an increasingly globalized market.
By mary rash
from Senegal
- 2018.02.12 14:52
The customer service staff is very patient and has a positive and progressive attitude to our interest, so that we can have a comprehensive understanding of the product and finally we reached an agreement, thanks!
By Heloise
from Austria
- 2018.12.11 14:13