China A106/A53/Asme Sa106 Sa53 - Seamless Medium carbon steel boiler and Superheat tubes ASTM A210 standard – Sanonpipe Manufacturer and Supplier

A106/A53/Asme Sa106 Sa53 - Seamless Medium carbon steel boiler and Superheat tubes ASTM A210 standard – Sanonpipe

Short Description:

Product Detail

Product Tags

Feedback (2)

With state-of-the-art technologies and facilities, strict good quality regulate, reasonable cost, exceptional assistance and close co-operation with prospects, we're devoted to supplying the top benefit for our customers for Lloy Steel Pipe A335 P5 , Gb/T8162 , Alloy Pipe P11 , It can be our wonderful honor to meet your requires.We sincerely hope we can cooperate along with you inside the around long term.

A106/A53/Asme Sa106 Sa53 - Seamless Medium carbon steel boiler and Superheat tubes ASTM A210 standard – Sanonpipe Detail:

Overview

Application

It is mainly used to make high-quality seamless carbon steel, for boiler pipes, super heat pipes

for bolier industry , heat changer pipe etc. With difference sizes and thickness

Main Grade

Grade of high-quality carbon boiler steel: GrA, GrC

Chemical Component

Element	Grade A	Grade C
C	≤0.27	≤0.35
Mn	≤0.93	0.29-1.06
P	≤0.035	≤0.035
S	≤0.035	≤0.035
Si	≥ 0.1	≥ 0.1

A For each reduction of 0.01 % below the specified carbon maximum, an increase of 0.06 % manganese above the specified maximum will be permitted up to a maximum of 1.35 %.

Mechanical Property

	Grade A	Grade C
Tensile Strength	≥ 415	≥ 485
Yield Strength	≥ 255	≥ 275
Elongation rate	≥ 30	≥ 30

Test Requirement

Hydraustatic Test:

The Steel Pipe Should Be Tested Hydraulically One By One. The Maximum Test Pressure Is 20 MPa. Under The Test Pressure, The Stabilization Time Should Be Not Less Than 10 S, And The Steel Pipe Should Not Leak.

After The User Agrees, The Hydraulic Test Can Be Replaced By Eddy Current Testing Or Magnetic Flux Leakage Testing.

Flattening Test：

Tubes With An Outer Diameter Greater Than 22 Mm Shall Be Subjected To A Flattening Test. No Visible Delamination, White Spots, Or Impurities Should Occur During The Entire Experiment.

Flaring Test:

According To The Requirements Of The Purchaser And Stated In The Contract, The Steel Pipe With Outer Diameter ≤76mm And Wall Thickness ≤8mm Can Be Done Flaring Test . The Experiment Was Performed At Room Temperature With A Taper Of 60 °. After The Flaring, The Flaring Rate Of The Outer Diameter Should Meet The Requirements Of The Following Table, And The Test Material Must Not Show Cracks Or Rips

Hardness Test:

Brinell or Rockwell hardness tests shall be made on specimens from two tubes from each lot

Product Detail

Boiler Tube

GB/T5310-2017

A106 Boiler Pipe

ASME SA-106/SA-106M-2015

ASTMA210(A210M)-2012

ASME SA-213/SA-213M

ASTM A335/A335M-2018

Product detail pictures:

Related Product Guide:

We always continually offer you by far the most conscientious customer service, and the widest variety of designs and styles with finest materials. These attempts include the availability of customized designs with speed and dispatch for A106/A53/Asme Sa106 Sa53 - Seamless Medium carbon steel boiler and Superheat tubes ASTM A210 standard – Sanonpipe , The product will supply to all over the world, such as: Kuala Lumpur , South Korea , Denver , We insist on the principle of "Credit being primary, Customers being the king and Quality being the best", we are looking forward to the mutual cooperation with all friends at home and abroad and we will create a bright future of business.

12crlmov Alloy Steel Pipe