Chinese wholesale ASTM A213 Alloy High Pressure Seamless Steel Grade T11 T12 T13 Tubing / Pipe
It really is a good way to further improve our goods and service. Our mission would be to acquire inventive items to buyers with a very good encounter for Chinese wholesale ASTM A213 Alloy High Pressure Seamless Steel Grade T11 T12 T13 Tubing / Pipe, Our items are regularly supplied to lots of Groups and lots of Factories. Meanwhile, our products are sold to the USA, Italy, Singapore, Malaysia, Russia, Poland, plus the Middle East.
It really is a good way to further improve our goods and service. Our mission would be to acquire inventive items to buyers with a very good encounter for Astm A213, High Pressure Pipe, High Pressure Tube, Seamless Pipe, Seamless Tube, Our mission is “Provide Products with Reliable Quality and Reasonable Prices”. We welcome customers from every corner of the world to contact us for future business relationships and achieving mutual success!
Overview
Application
It is mainly used to make high-quality alloy steel pipe for high pressure boiler pipe, heat exchanger pipe and super heat pipe
Main Grade
Grade of high-quality Alloy steel: T2,T12,T11,T22, T91, T92 etc.
Chemical Component
| Steel Grade | Chemical Composition% | ||||||||||
| C | Si | Mn | P, S Max | Cr | Mo | Ni Max | V | Al Max | W | B | |
| T2 | 0.10~0.20 | 0.10~0.30 | 0.30~0.61 | 0.025 | 0.50~0.81 | 0.44~0.65 | – | – | – | – | – |
| T11 | 0.05~0.15 | 0.50~1.00 | 0.30~0.60 | 0.025 | 1.00~1.50 | 0.44~0.65 | – | – | – | – | – |
| T12 | 0.05~0.15 | Max 0.5 | 0.30~0.61 | 0.025 | 0.80~1.25 | 0.44~0.65 | – | – | – | – | – |
| T22 | 0.05~0.15 | Max 0.5 | 0.30~0.60 | 0.025 | 1.90~2.60 | 0.87~1.13 | – | – | – | – | – |
| T91 | 0.07~0.14 | 0.20~0.50 | 0.30~0.60 | 0.02 | 8.0~9.5 | 0.85~1.05 | 0.4 | 0.18~0.25 | 0.015 | – | – |
| T92 | 0.07~0.13 | Max 0.5 | 0.30~0.60 | 0.02 | 8.5~9.5 | 0.30~0.60 | 0.4 | 0.15~0.25 | 0.015 | 1.50~2.00 | 0.001~0.006 |
For T91 other than above also includes Nickel 0.4, Va 0.18-0.25, Ni 0.06-0.10, Ni 0.03-0.07, Al 0.02, Ti 0.01, Zr 0.01. A Maximum, unless range or minimum is indicated. Where ellipses (…) appear in this table, there is no requirement, and analysis for the element need not be determined or reported. B It is permissible to order T2 and T12 with a sulfur content of 0.045 max. C Alternatively, in lieu of this ratio minimum, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering. Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per heat treatment lot and the hardness testing results shall be reported on the material test report.
Mechanical Property
| Steel Grade | Mechanical Properties | |||
| T. S | Y. P | Elongation | Hardness | |
| T2 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
| T11 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
| T12 | ≥ 415MPa | ≥ 220MPa | ≥ 30% | 163HBW(85HRB) |
| T22 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
| T91 | ≥ 585MPa | ≥ 415MPa | ≥ 20% | 250HBW(25HRB) |
| T92 | ≥ 620MPa | ≥ 440MPa | ≥ 20% | 250HBW(25HRB) |
Tolerance
Permitted Variations in Wall thickness
| Wallthickess % | |||||
| outside diameter in. mm |
0.095 2.4 and under |
over0.095 to 0.15 2.4-3.8 incl. |
over 0.15 to 0.18 3.8-4.6 incl |
over 0.18 to 4.6 |
|
| over under over under over under over under | |||||
| seamless, hot finished | |||||
| 4inch and under 40 0 35 0 33 0 28 0 | |||||
| over 4 inch .. .. 35 0 33 0 28 0 | |||||
| seamless, cold finished | |||||
| over under | |||||
| 11/2 and under | 20 0 | ||||
| over 11/2 | 22 0 | ||||
The permitted variations in wall thickness apply only to tube , except internal-upset tubes, as rolled or cold finished
and before swaging,expanding ,bending,polishing,or other fabricating operations
Permitted Variations in Outside Diameter
| outside diameter （mm) | Pemitted Variation( mm) | |
| hot finished seamless tube | over | under |
| 4″ (100mm)and under | 0.4 | 0.8 |
| 4-71/2″(100-200mm） | 0.4 | 1.2 |
| 71/2-9“（200-225） | 0.4 | 1.6 |
| Welded tubes and cold finished seamless tubes | ||
| under1″(25mm) | 0.1 | 0.11 |
| 1-11/2″(25-40mm) | 0.15 | 0.15 |
| 11/2-2″(40-50mm) | 0.2 | 0.2 |
| 2-21/2″(50-65mm) | 0.25 | 0.25 |
| 21/2-3″(65-75mm) | 0.3 | 0.3 |
| 3-4″(75-100mm) | 0.38 | 0.38 |
| 4-71/2″(100-200mm） | 0.38 | 0.64 |
| 71/2-9“（200-225） | 0.38 | 1.14 |
Test Requirement
Hydraustatic Test:
The Steel Pipe Should Be Tested Hydraulically One By One. The Maximum Test Pressure Is 20 MPa. Under The Test Pressure, The Stabilization Time Should Be Not Less Than 10 S, And The Steel Pipe Should Not Leak. Or The Hydraulic Test Can Be Replaced By Eddy Current Testing Or Magnetic Flux Leakage Testing.
Nondestructive Test：
Pipes That Require More Inspection Should Be Ultrasonically Inspected One By One. After The Negotiation Requires The Consent Of The Party And Is Specified In The Contract, Other Non-Destructive Testing Can Be Added.
Flattening Test：
Tubes With An Outer Diameter Greater Than 22 Mm Shall Be Subjected To A Flattening Test. No Visible Delamination, White Spots, Or Impurities Should Occur During The Entire Experiment.
Hardness Test:
For Pipe Of Grades P91, P92, P122, And P911, Brinell, Vickers, Or Rockwell Hardness Tests Shall Be Made On A Specimen From Each Lot
Product Detail
Boiler Tube
GB/T5310-2017
ASME SA-106/SA-106M-2015
ASTMA210(A210M)-2012
ASME SA-213/SA-213M