Overview
Application
It is mainly used to make high-quality alloy steel pipe for high pressure boiler pipe, heat exchanger pipe and super heat pipe
Main Grade
Grade of high-quality Alloy steel: T2,T12,T11,T22, T91, T92 etc.
Chemical Component
Steel Grade | Chemical Composition% | ||||||||||
C | Si | Mn | P, S Max | Cr | Mo | Ni Max | V | Al Max | W | B | |
T2 | 0.10~0.20 | 0.10~0.30 | 0.30~0.61 | 0.025 | 0.50~0.81 | 0.44~0.65 | – | – | – | – | – |
T11 | 0.05~0.15 | 0.50~1.00 | 0.30~0.60 | 0.025 | 1.00~1.50 | 0.44~0.65 | – | – | – | – | – |
T12 | 0.05~0.15 | Max 0.5 | 0.30~0.61 | 0.025 | 0.80~1.25 | 0.44~0.65 | – | – | – | – | – |
T22 | 0.05~0.15 | Max 0.5 | 0.30~0.60 | 0.025 | 1.90~2.60 | 0.87~1.13 | – | – | – | – | – |
T91 | 0.07~0.14 | 0.20~0.50 | 0.30~0.60 | 0.02 | 8.0~9.5 | 0.85~1.05 | 0.4 | 0.18~0.25 | 0.015 | – | – |
T92 | 0.07~0.13 | Max 0.5 | 0.30~0.60 | 0.02 | 8.5~9.5 | 0.30~0.60 | 0.4 | 0.15~0.25 | 0.015 | 1.50~2.00 | 0.001~0.006 |
For T91 other than above also includes Nickel 0.4, Va 0.18-0.25, Ni 0.06-0.10, Ni 0.03-0.07, Al 0.02, Ti 0.01, Zr 0.01. A Maximum, unless range or minimum is indicated. Where ellipses (…) appear in this table, there is no requirement, and analysis for the element need not be determined or reported. B It is permissible to order T2 and T12 with a sulfur content of 0.045 max. C Alternatively, in lieu of this ratio minimum, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering. Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per heat treatment lot and the hardness testing results shall be reported on the material test report.
Mechanical Property
Steel Grade | Mechanical Properties | |||
T. S | Y. P | Elongation | Hardness | |
T2 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
T11 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
T12 | ≥ 415MPa | ≥ 220MPa | ≥ 30% | 163HBW(85HRB) |
T22 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
T91 | ≥ 585MPa | ≥ 415MPa | ≥ 20% | 250HBW(25HRB) |
T92 | ≥ 620MPa | ≥ 440MPa | ≥ 20% | 250HBW(25HRB) |
Tolerance
Permitted Variations in Wall thickness
Wallthickess % | |||||
outside diameter in. mm |
0.095 2.4 and under |
over0.095 to 0.15 2.4-3.8 incl. |
over 0.15 to 0.18 3.8-4.6 incl |
over 0.18 to 4.6 |
|
over under over under over under over under | |||||
seamless, hot finished | |||||
4inch and under 40 0 35 0 33 0 28 0 | |||||
over 4 inch .. .. 35 0 33 0 28 0 | |||||
seamless, cold finished | |||||
over under | |||||
11/2 and under | 20 0 | ||||
over 11/2 | 22 0 |
The permitted variations in wall thickness apply only to tube , except internal-upset tubes, as rolled or cold finished
and before swaging,expanding ,bending,polishing,or other fabricating operations
Permitted Variations in Outside Diameter
outside diameter (mm) | Pemitted Variation( mm) | |
hot finished seamless tube | over | under |
4″ (100mm)and under | 0.4 | 0.8 |
4-71/2″(100-200mm) | 0.4 | 1.2 |
71/2-9“(200-225) | 0.4 | 1.6 |
Welded tubes and cold finished seamless tubes | ||
under1″(25mm) | 0.1 | 0.11 |
1-11/2″(25-40mm) | 0.15 | 0.15 |
11/2-2″(40-50mm) | 0.2 | 0.2 |
2-21/2″(50-65mm) | 0.25 | 0.25 |
21/2-3″(65-75mm) | 0.3 | 0.3 |
3-4″(75-100mm) | 0.38 | 0.38 |
4-71/2″(100-200mm) | 0.38 | 0.64 |
71/2-9“(200-225) | 0.38 | 1.14 |
Test Requirement
Hydraustatic Test:
The Steel Pipe Should Be Tested Hydraulically One By One. The Maximum Test Pressure Is 20 MPa. Under The Test Pressure, The Stabilization Time Should Be Not Less Than 10 S, And The Steel Pipe Should Not Leak. Or The Hydraulic Test Can Be Replaced By Eddy Current Testing Or Magnetic Flux Leakage Testing.
Nondestructive Test:
Pipes That Require More Inspection Should Be Ultrasonically Inspected One By One. After The Negotiation Requires The Consent Of The Party And Is Specified In The Contract, Other Non-Destructive Testing Can Be Added.
Flattening Test:
Tubes With An Outer Diameter Greater Than 22 Mm Shall Be Subjected To A Flattening Test. No Visible Delamination, White Spots, Or Impurities Should Occur During The Entire Experiment.
Hardness Test:
For Pipe Of Grades P91, P92, P122, And P911, Brinell, Vickers, Or Rockwell Hardness Tests Shall Be Made On A Specimen From Each Lot
Product Detail
Boiler Tube
GB/T5310-2017
ASME SA-106/SA-106M-2015
ASTMA210(A210M)-2012
ASME SA-213/SA-213M
ASTM A335/A335M-2018
Product detail pictures:
Related Product Guide:
We constantly function like a tangible group to ensure that we can give you the very best high-quality and also the very best cost for Erw Tube Sch 120 - Seamless Alloy Steel Boiler Pipes Superheater alloy pipes Heat Exchanger Tubes – Sanonpipe , The product will supply to all over the world, such as: Latvia , Uruguay , Mexico , We solution have passed through the national skilled certification and been well received in our key industry. Our specialist engineering team will often be ready to serve you for consultation and feedback. We've been able to also provide you with no cost samples to meet your needs. Best efforts are going to be produced to supply you the very best service and solutions. For anyone who is considering our business and solutions, please speak to us by sending us emails or get in touch with us right away. As a way to know our items and enterprise. lot more, you'll be able to come to our factory to find out it. We'll constantly welcome guests from around the globe to our firm. o build enterprise. elations with us. You should really feel absolutely free to make contact with us for small business and we believe we'll share the top trading practical experience with all our merchants.
By Yannick Vergoz from Afghanistan - 2018.11.22 12:28
This supplier offers high quality but low price products, it is really a nice manufacturer and business partner.
By Paula from Japan - 2017.11.11 11:41