ASTM SA 213 Tib echanjeur chalè
| Estanda:ASTM SA 213 | Alloy or Not: Alloy |
| Gwoup Klas: T5, T9, T11, T22 elatriye | Aplikasyon: Tiyo chodyè / tiyo echanjeur chalè |
| Epesè: 0.4-12.7 mm | Sifas Tretman: Kòm kondisyon kliyan an |
| Eksteryè Dyamèt (Round): 3.2-127 mm | Teknik: Woule cho |
| Longè: Longè fiks oswa longè o aza | Tretman chalè: Nòmalizasyon / Tanperaman / Annealing |
| Fòm seksyon: wonn | Tiyo espesyal: tiyo epè mi |
| Kote ki gen orijin: Lachin | Itilizasyon: Super chalè, chodyè ak echanjeur chalè |
| Sètifikasyon: ISO9001:2008 | Tès: ECT/UT |
Li se sitou itilize fè tiyo asye alyaj kalite siperyè pou tiyo chodyè presyon wo, tiyo echanjeur chalè ak tiyo chalè super.
Klas bon jan kalite asye alyaj: T2, T12, T11, T22, T91, T92 elatriye.
| Steel Klas | Konpozisyon chimik% | ||||||||||
| C | Si | Mn | P, S Max | Cr | Mo | Ni Max | V | Al Max | W | B | |
| T2 | 0.10 ~ 0.20 | 0.10 ~ 0.30 | 0.30 ~ 0.61 | 0.025 | 0.50 ~ 0.81 | 0.44 ~ 0.65 | – | – | – | – | – |
| T11 | 0.05 ~ 0.15 | 0.50 ~ 1.00 | 0.30 ~ 0.60 | 0.025 | 1.00 ~ 1.50 | 0.44 ~ 0.65 | – | – | – | – | – |
| T12 | 0.05 ~ 0.15 | Maksimòm 0.5 | 0.30 ~ 0.61 | 0.025 | 0.80 ~ 1.25 | 0.44 ~ 0.65 | – | – | – | – | – |
| T22 | 0.05 ~ 0.15 | Maksimòm 0.5 | 0.30 ~ 0.60 | 0.025 | 1.90 ~ 2.60 | 0.87 ~ 1.13 | – | – | – | – | – |
| T91 | 0.07 ~ 0.14 | 0.20 ~ 0.50 | 0.30 ~ 0.60 | 0.02 | 8.0 ~ 9.5 | 0.85 ~ 1.05 | 0.4 | 0.18 ~ 0.25 | 0.015 | – | – |
| T92 | 0.07 ~ 0.13 | Maksimòm 0.5 | 0.30 ~ 0.60 | 0.02 | 8.5 ~ 9.5 | 0.30 ~ 0.60 | 0.4 | 0.15 ~ 0.25 | 0.015 | 1.50 ~ 2.00 | 0.001 ~ 0.006 |
Pou T91 lòt pase pi wo a gen ladan tou Nikèl 0.4, Va 0.18-0.25, Ni 0.06-0.10, Ni 0.03-0.07, Al 0.02, Ti 0.01, Zr 0.01. Yon Maksimòm, sof si yo endike ranje oswa minimòm. Kote elips (...) parèt nan tablo sa a, pa gen okenn kondisyon, epi analiz pou eleman an pa bezwen detèmine oswa rapòte. B Li se akseptab bay lòd T2 ak T12 ak yon kontni souf nan 0.045 max. C Altènativman, nan plas minimòm rapò sa a, materyèl la dwe gen yon dite minimòm de 275 HV nan kondisyon an fè tèt di toujou, defini kòm apre ostenitize ak refwadisman nan tanperati chanm men anvan tanperaman. Tès dite yo dwe fèt nan mitan epesè pwodwi a. Frekans tès dite yo dwe de echantiyon pwodwi pou chak lo tretman chalè ak rezilta tès dite yo dwe rapòte sou rapò tès materyèl la.
| Steel Klas | Pwopriyete mekanik | |||
| T. S | Y.P | Elongasyon | Dite | |
| T2 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
| T11 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
| T12 | ≥ 415MPa | ≥ 220MPa | ≥ 30% | 163HBW(85HRB) |
| T22 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
| T91 | ≥ 585MPa | ≥ 415MPa | ≥ 20% | 250HBW (25HRB) |
| T92 | ≥ 620MPa | ≥ 440MPa | ≥ 20% | 250HBW (25HRB) |
Varyasyon otorize nan epesè miray la
| Epesè mi | |||||
| deyò dyamèt nan. mm | 0.095 2.4 ak anba | plis pase 0.095 rive 0.15 2.4-3.8 incl. | plis pase 0.15 rive 0.18 3.8-4.6 incl | plis pase 0.18 rive 4.6 | |
| over under over under over under over under | |||||
| san pwoblèm, cho fini | |||||
| 4pous ak anba 40 0 35 0 33 0 28 0 | |||||
| plis pase 4 pous .. .. 35 0 33 0 28 0 | |||||
| san pwoblèm, frèt fini | |||||
| sou anba | |||||
| 11/2 ak anba | 200 | ||||
| plis pase 11/2 | 220 | ||||
Varyasyon yo pèmèt nan epesè miray yo aplike sèlman nan tib, eksepte tib entèn-fache, jan woule oswa frèt fini.
epi anvan swaging, agrandi, koube, polisaj, oswa lòt operasyon fabrike
Varyasyon ki otorize nan dyamèt deyò
| deyò dyamèt (mm) | Varyasyon pèmèt (mm) | |
| cho fini tib san pwoblèm | sou | anba |
| 4" (100mm) ak anba | 0.4 | 0.8 |
| 4-71/2 "(100-200mm) | 0.4 | 1.2 |
| 71/2-9 "(200-225) | 0.4 | 1.6 |
| Tib soude ak frèt fini tib san pwoblèm | ||
| anba 1 "(25mm) | 0.1 | 0.11 |
| 1-11/2 "(25-40mm) | 0.15 | 0.15 |
| 11/2-2 "(40-50mm) | 0.2 | 0.2 |
| 2-21/2 "(50-65mm) | 0.25 | 0.25 |
| 21/2-3 "(65-75mm) | 0.3 | 0.3 |
| 3-4 "(75-100mm) | 0.38 | 0.38 |
| 4-71/2 "(100-200mm) | 0.38 | 0.64 |
| 71/2-9 "(200-225) | 0.38 | 1.14 |
Tès idwostatik:
Yo ta dwe teste tiyo asye a idwolik youn pa youn. Presyon maksimòm tès la se 20 MPa. Anba presyon tès la, tan estabilizasyon an ta dwe pa mwens pase 10 S, epi tiyo asye a pa ta dwe koule. Oswa tès idwolik la ka ranplase pa tès aktyèl Eddy oswa tès flit mayetik.
Tès nondestriktif:
Tiyo ki mande plis enspeksyon ta dwe enspekte ultrasons youn pa youn. Apre negosyasyon an mande konsantman pati a epi li espesifye nan kontra a, yo ka ajoute lòt tès ki pa destriktif.
Tès aplati:
Tib ki gen yon dyamèt ekstèn ki pi gran pase 22 mm yo pral sibi yon tès plati. Pa gen okenn delaminasyon vizib, tach blan, oswa enpurte ki ta dwe rive pandan tout eksperyans la.
Tès dite:
Pou tiyo nan klas P91, P92, P122, ak P911, Brinell, Vickers, oswa tès dite Rockwell dwe fèt sou yon echantiyon nan chak lo.