Low MOQ for Alloy Steel Pipe - Seamless steel tubes for normal structure – Sanonpipe
Low MOQ for Alloy Steel Pipe - Seamless steel tubes for normal structure – Sanonpipe Detail:
Overview
Application
It Is Mainly Used To Make Carbon Structural Steel, Alloy Structural Steel and mechanical structures.
Main Grade
Grade Of Carbon Structural Steel: 10,20,35, 45,Q345,Q460,Q490,Q620,, Etc
Grade Of Alloy Structural Steel: 42CrMo,35CrMo, Etc
Chemical Component
Steel Grade |
Quality level |
Chemical composition |
||||||||||||||
C |
Si |
Mn |
P |
S |
Nb |
V |
Ti |
Cr |
Ni |
Cu |
Nd |
Mo |
B |
Als” |
||
no greater than |
not less than |
|||||||||||||||
Q345 | A |
0.20 |
0.50 |
1.70 |
0.035 | 0.035 |
0.30 |
0.50 |
0.20 |
0.012 |
0.10 |
—— | — | |||
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 |
0.07 |
0.15 |
0.20 |
0.015 |
||||||||||
D |
0.18 |
0.030 | 0.025 | |||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q390 | A |
0.20 |
0.50 |
1.70 |
0.035 | 0.035 |
0.07 |
0.20 |
0.20 |
0.3 |
0.50 |
0.20 |
0.015 |
0.10 |
— | — |
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 |
0,015 |
|||||||||||||
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q42O | A |
0.20 |
0.50 |
1.70 |
0.035 | 0.035 |
0.07 |
0.2 |
0.20 |
0.30 |
0.80 |
0.20 |
0.015 |
0.20 |
—— |
—— |
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 |
0.015 |
|||||||||||||
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q46O | C |
0.20 |
0.60 |
1.80 |
0.030 | 0.030 |
0.11 |
0.20 |
0.20 |
0.30 |
0.80 |
0.20 |
0.015 |
0.20 |
0.005 |
0.015 |
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q500 | C |
0J8 |
0.60 |
1.80 |
0.025 | 0.020 |
0.11 |
0.20 |
0.20 |
0.60 |
0.80 |
0.20 |
0.015 |
0.20 |
0.005 |
0.015 |
D | 0.025 | 0.015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
Q550 | C |
0.18 |
0.60 |
2.00 |
0.025 | 0,020 | 0.11 |
0.20 |
0.20 |
0.80 |
0.80 |
0.20 |
0.015 |
0.30 |
0.005 |
0.015 |
D | 0.025 | 0,015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
Q62O | C |
0.18 |
0.60 |
2.00 |
0.025 | 0.020 |
0.11 |
0.20 |
0.20 |
1.00 |
0.80 |
0.20 |
0.015 |
0.30 |
0.005 |
0.015 |
D | 0.025 | 0.015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
a. In addition to Q345A and Q345B grades, the steel should contain at least one of the refined grain elements Al, Nb, V, and Ti. According to the needs, the supplier can add one or more refined grain elements. The maximum value shall be as specified in the table. When combined, Nb + V + Ti is not more than 0.22%b. For Q345, Q390, Q420 and Q46O grades, Mo + Cr is not greater than 0.30%c. When Cr and Ni of each grade are used as residual elements, the content of Cr and Ni should not be greater than 0.30%; when it is necessary to add, the content should meet the requirements in the table or be determined by the supplier and the buyer through consultation.d. If the supplier can ensure that the nitrogen content meets the requirements in the table, the nitrogen content analysis may not be performed. If Al, Nb, V, Ti and other alloy elements with nitrogen fixation are added to the steel, the nitrogen content is not limited. The nitrogen fixation content should be specified in the quality certificate.
e. When using full aluminum, the total aluminum content Alt ≥ 0020%. |
Grade |
Carbon equivalent CEV (mass fraction) /% |
|||||
Nominal wall thickness s≤ 16mm |
Nominal wall thickness S2>16 mm〜30 mm |
Nominal wall thickness S>30mm |
||||
Hot rolled or normalized normalized |
Quenching +tempering |
Hot rolled or normalized |
Quenching +tempering |
Hot rolled or normalized |
Quenching +tempering |
|
Q345 |
<0.45 |
— |
<0.47 |
— |
<0.48 |
一 |
Q390 |
<0.46 |
一 |
W0.48 |
— |
<0.49 |
— |
Q420 |
<0.48 |
一 |
<0.50 |
<0.48 |
<0.52 |
<0,48 |
Q460 |
<0.53 |
<0.48 |
W0.55 |
<0.50 |
<0.55 |
W0.50 |
Q500 |
一 |
<0.48 |
一 |
<0.50 |
一 |
W0.50 |
Q550 |
— |
<0.48 |
.一 |
<0.50 |
一 |
<0.50 |
Q62O |
— |
<0.50 |
— |
<0.52 |
— |
W0.52 |
Q690 |
— |
<0.50 |
— |
<0.52 |
— |
W0.52 |
Mechanical Property
Mechanical properties of high-quality carbon steel structural steel and low-alloy high-strength structural steel pipes
Grade | Quality level | Yield Strength | Lower yield strength | Elongation after breaking | Impact test | |||
Nominal wall thickness | temperature | Absorb energy | ||||||
<16 mm | >16 mm〜 | 〉30 mm | ||||||
30 mm | ||||||||
not less than | not less than | |||||||
10 | — | >335 | 205 | 195 | 185 | 24 | — | — |
15 | — | >375 | 225 | 215 | 205 | 22 | — | 一 |
20 | —— | >410 | 245 | 235 | 225 | 20 | — | — |
25 | — | >450 | 275 | 265 | 255 | 18 | — | — |
35 | — | >510 | 305 | 295 | 285 | 17 | 一 | — |
45 | — | 2590 | 335 | 325 | 315 | 14 | — | — |
20Mn | —• | >450 | 275 | 265 | 255 | 20 | — | 一 |
25Mn | — | >490 | 295 | 285 | 275 | 18 | — | — |
Q345 | A | 470—630 | 345 | 325 | 295 | 20 | — | 一 |
B | 4~20 | 34 | ||||||
C | 21 | 0 | ||||||
D | -20 | |||||||
E | -40 | 27 | ||||||
Q39O | A | 490—650 | 390 | 370 | 350 | 18 | ||
B | 20 | 34 | ||||||
C | 19 | 0 | ||||||
D | -20 | |||||||
E | -40 | 27 | ||||||
Q42O | A | 520〜680 | 420 | 400 | 380 | 18 | ||
B | 20 | 34 | ||||||
C | 19 | 0 | ||||||
D | -20 | |||||||
E | -40 | 27 | ||||||
Q46O | C | 550〜720 | 460 | 440 | 420 | 17 | 0 | 34 |
D | -20 | |||||||
E | -40 | 27 | ||||||
Q500 | C | 610〜770 | 500 | 480 | 440 | 17 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 | ||||||
Q550 | C | 670〜830 | 550 | 530 | 490 | 16 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 | ||||||
Q62O | C | 710〜880 | 620 | 590 | 550 | 15 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 | ||||||
Q690 | C | 770〜94。 | 690 | 660 | 620 | 14 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 |
Mechanical properties of alloy steel pipes
NO | Grade | Recommended heat treatment regime | Tensile properties | Annealed or high temperature tempered steel pipe Delivery condition Brinell hardness HBW | ||||||
Quenching (normalizing) | Tempering | Yield StrengthMPa | Tensile Strength MPa | Elongation after breaking A% | ||||||
temperature | Coolant | Temperature | Coolant | |||||||
Frirst | Second | not less than | no greater than | |||||||
1 | 40Mn2 | 840 | Water, oil | 540 | Water, oil | 885 | 735 | 12 | 217 | |
2 | 45Mn2 | 840 | Water,oil | 550 | Water, oil | 885 | 735 | 10 | 217 | |
3 | 27SiMn | 920 | Water | 450 | Water, oil | 980 | 835 | 12 | 217 | |
4 | 40MnBc | 850 | oil | 500 | Water, oil | 980 | 785 | 10 | 207 | |
5 | 45MnBc | 840 | oil | 500 | Water, oil | 1 030 | 835 | 9 | 217 | |
6 | 20Mn2Bc’f | 880 | oil | 200 | Water, air | 980 | 785 | 10 | 187 | |
7 | 20CrdJ | 880 | 800 | Water,oil | 200 | Water, air | 835 | 540 | 10 | 179 |
785 | 490 | 10 | 179 | |||||||
8 | 30Cr | 860 | oil | 500 | Water, oil | 885 | 685 | 11 | 187 | |
9 | 35Cr | 860 | oil | 500 | Water, oil | 930 | 735 | 11 | 207 | |
10 | 40Cr | 850 | oil | 520 | Water, oil | 980 | 785 | 9 | 207 | |
11 | 45Cr | 840 | oil | 520 | Water, oil | 1 030 | 835 | 9 | 217 | |
12 | 50Cr | 830 | oil | 520 | Water, oil | 1 080 | 930 | 9 | 229 | |
13 | 38CrSi | 900 | oil | 600 | Water, oil | 980 | 835 | 12 | 255 | |
14 | 20CrModJ | 880 | Water,oil | 500 | Water, oil | 885 | 685 | 11 | 197 | |
845 | 635 | 12 | 197 | |||||||
15 | 35CrMo | 850 | oil | 550 | Water, oil | 980 | 835 | 12 | 229 | |
16 | 42CrMo | 850 | oil | 560 | Water, oil | 1 080 | 930 | 12 | 217 | |
17 | 38CrMoAld | 940 | Water, oil | 640 | Water, oil | 980 | 835 | 12 | 229 | |
930 | 785 | 14 | 229 | |||||||
18 | 50CrVA | 860 | oil | 500 | Water, oil | 1 275 | 1 130 | 10 | 255 | |
19 | 2OCrMn | 850 | oil | 200 | Water、air | 930 | 735 | 10 | 187 | |
20 | 20CrMnSif | 880 | oil | 480 | Water, oil | 785 | 635 | 12 | 207 | |
21 | 3OCrMnSif | 880 | oil | 520 | Water, oil | 1 080 | 885 | 8 | 229 | |
980 | 835 | 10 | 229 | |||||||
22 | 35CrMnSiA£ | 880 | oil | 230 | Water、air | 1 620 | 9 | 229 | ||
23 | 20CrMnTie-f | 880 | 870 | oil | 200 | Water、air | 1 080 | 835 | 10 | 217 |
24 | 30CrMnTie*f | 880 | 850 | oil | 200 | Water、air | 1 470 | 9 | 229 | |
25 | 12CrNi2 | 860 | 780 | Water,oil | 200 | Water、air | 785 | 590 | 12 | 207 |
26 | 12CrNi3 | 860 | 780 | oil | 200 | Water、air | 930 | 685 | 11 | 217 |
27 | 12Cr2Ni4 | 860 | 780 | oil | 200 | Water、air | 1 080 | 835 | 10 | 269 |
28 | 40CrNiMoA | 850 | —— | oil | 600 | Water、air | 980 | 835 | 12 | 269 |
29 | 45CrNiMoVA | 860 | — | oil | 460 | oil | 1 470 | 1 325 | 7 | 269 |
a. Allowable adjustment range of heat treatment temperature listed in the table: quenching ± 15 ℃, low temperature tempering ± 20 ℃, high temperature tempering soil 50 ℃.b. In the tensile test, transverse or longitudinal samples can be taken. In case of disagreement, the longitudinal sample is used as the basis for arbitration.c. Boron-containing steel can be normalized before quenching, and the normalizing temperature should not be higher than its quenching temperature.
d. Delivery according to a set of data specified by the demander. When the demander has not specified, delivery can be made according to any of the data. e. The first quenching of titanium steel with Ming Meng can be replaced by normalizing. f. Isothermal quenching at 280 C ~320 C. g. In the tensile test, if Rel cannot be measured, Rp0.2 can be measured instead of Rel. |
Test Requirement
Chemical composition,Stretch,Hardness,Shock,Squash,Bending,Ultrasonic testing,Eddy current,detection,Leak detection,Galvanized
Supply Ability
Supply Ability: 2000 Tons Per Month Per Grade Of GB/T8162-2008 Steel Pipe
Packaging
In Bundles And In Strong Wooden Box
Delivery
7-14 days if in stock, 30-45 days to produce
Payment
30% depsoit, 70% L/C or B/L copy or 100% L/C at sight
Product Detail
Mechanical/Chemical&Fertilizer Pipes
GB/T 8162-2008
ASTM A519-2006
BS EN 10210-1-2006
ASTM A53/A53M-2012
GB 9948-2006
GB 6479-2013
GB/T 17396-2009
Product detail pictures:
Related Product Guide:
We take "customer-friendly, quality-oriented, integrative, innovative" as objectives. "Truth and honesty" is our administration ideal for Low MOQ for Alloy Steel Pipe - Seamless steel tubes for normal structure – Sanonpipe , The product will supply to all over the world, such as: Sri Lanka , Romania , Qatar , The company attaches great importance to product quality and service quality, based on the business philosophy "good with people, genuine to whole world, your satisfaction is our pursuit". we design products, According to customer's sample and requirements, to meet the needs of the market and offer different customers with personalized service. Our company warmly welcomes friends at home and abroad to visit, to discuss cooperation and seek common development!
By Faithe from Luxemburg - 2018.06.26 19:27
Staff is skilled, well-equipped, process is specification, products meet the requirements and delivery is guaranteed, a best partner!
By Elaine from United States - 2017.05.02 11:33