Kugabanuka Kinini ASTM A335 P91 Uruganda rukora imiyoboro itagira ingano mu Bushinwa
Incamake
Ubucuruzi bwacu bushimangira ubuyobozi, gushyiraho abakozi bafite impano, hiyongereyeho kubaka amatsinda, kugerageza cyane kuzamura imyumvire n’uburyozwe bw’abakiriya. Isosiyete yacu yatsindiye neza IS9001 Icyemezo hamwe nu Burayi CE Icyemezo cyumuringoti wibyuma. Tuzakomeza gukora cyane kandi mugihe tugerageza uko dushoboye kugirango dutange ibicuruzwa byiza, igiciro cyapiganwa cyane na serivisi nziza kuri buri mukiriya. Ukunyurwa kwawe, icyubahiro cyacu !!! Umusaruro wacu woherejwe mu bihugu n’uturere birenga 30 nkisoko yambere yintoki hamwe nigiciro gito. Twakiriye neza abakiriya baturutse mu gihugu ndetse no hanze kugirango baze kuganira natwe ubucuruzi.
Gusaba
Ikoreshwa cyane cyane mugukora ibyuma byujuje ubuziranenge byibyuma, ibyuma bihinduranya ubushyuhe, umuyoboro mwinshi wumuvuduko wa peteroli ninganda
Icyiciro rusange
Urwego rwumuyoboro mwiza wo mu rwego rwo hejuru: P1, P2, P5, P9, P11, P22, P91, P92 nibindi
Ibigize imiti
Icyiciro | UN | C≤ | Mn | P≤ | S≤ | Si≤ | Cr | Mo |
Urukurikirane. | ||||||||
P1 | K11522 | 0.10 ~ 0.20 | 0.30 ~ 0.80 | 0.025 | 0.025 | 0.10 ~ 0.50 | - | 0.44 ~ 0.65 |
P2 | K11547 | 0.10 ~ 0.20 | 0.30 ~ 0.61 | 0.025 | 0.025 | 0.10 ~ 0.30 | 0.50 ~ 0.81 | 0.44 ~ 0.65 |
P5 | K41545 | 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 4.00 ~ 6.00 | 0.44 ~ 0.65 |
P5b | K51545 | 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 1.00 ~ 2.00 | 4.00 ~ 6.00 | 0.44 ~ 0.65 |
P5c | K41245 | 0.12 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 4.00 ~ 6.00 | 0.44 ~ 0.65 |
P9 | S50400 | 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.50 ~ 1.00 | 8.00 ~ 10.00 | 0.44 ~ 0.65 |
P11 | K11597 | 0.05 ~ 0.15 | 0.30 ~ 0.61 | 0.025 | 0.025 | 0.50 ~ 1.00 | 1.00 ~ 1.50 | 0.44 ~ 0.65 |
P12 | K11562 | 0.05 ~ 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 0.80 ~ 1.25 | 0.44 ~ 0.65 |
P15 | K11578 | 0.05 ~ 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 1.15 ~ 1.65 | - | 0.44 ~ 0.65 |
P21 | K31545 | 0.05 ~ 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 2.65 ~ 3.35 | 0.80 ~ 1.60 |
P22 | K21590 | 0.05 ~ 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 1.90 ~ 2.60 | 0.87 ~ 1.13 |
P91 | K91560 | 0.08 ~ 0.12 | 0.30 ~ 0.60 | 0.02 | 0.01 | 0.20 ~ 0.50 | 8.00 ~ 9.50 | 0.85 ~ 1.05 |
P92 | K92460 | 0.07 ~ 0.13 | 0.30 ~ 0.60 | 0.02 | 0.01 | 0.5 | 8.50 ~ 9.50 | 0.30 ~ 0.60 |
Izina rishya ryashyizweho hakurikijwe imyitozo E 527 na SAE J1086, Imyitozo yo Kubara Ibyuma na Alloys (UNS). B Urwego P 5c rugomba kuba rufite titanium itarenze inshuro 4 ibirimo karubone kandi ntibirenze 0,70%; cyangwa columbium ikubiyemo inshuro 8 kugeza 10 zirimo karubone.
Umutungo wa mashini
Ibikoresho bya mashini | P1, P2 | P12 | P23 | P91 | P92, P11 | P122 |
Imbaraga zingana | 380 | 415 | 510 | 585 | 620 | 620 |
Tanga imbaraga | 205 | 220 | 400 | 415 | 440 | 400 |
Kuvura Ubushuhe
Icyiciro | Ubwoko bwo Kuvura Ubushuhe | Guhindura Ubushyuhe Urwego F [C] | Subcritical Annealing cyangwa Ubushyuhe |
P5, P9, P11, na P22 | Ikirere cy'ubushyuhe F [C] | ||
A335 P5 (b, c) | Byuzuye cyangwa Isothermal Anneal | ||
Ubusanzwe n'ubushyuhe | ***** | 1250 [675] | |
Anneal Subcritical Anneal (P5c gusa) | ***** | 1325 - 1375 [715 - 745] | |
A335 P9 | Byuzuye cyangwa Isothermal Anneal | ||
Ubusanzwe n'ubushyuhe | ***** | 1250 [675] | |
A335 P11 | Byuzuye cyangwa Isothermal Anneal | ||
Ubusanzwe n'ubushyuhe | ***** | 1200 [650] | |
A335 P22 | Byuzuye cyangwa Isothermal Anneal | ||
Ubusanzwe n'ubushyuhe | ***** | 1250 [675] | |
A335 P91 | Ubusanzwe n'ubushyuhe | 1900-1975 [1040 - 1080] | 1350-1470 [730 - 800] |
Kuzimya no kurakara | 1900-1975 [1040 - 1080] | 1350-1470 [730 - 800] |
Ibisabwa
Usibye kwemeza imiterere yimiti nubukanishi, ibizamini bya hydrostatike bikorwa umwe umwe, Ikizamini kidahwitse, Isesengura ryibicuruzwa, Imiterere yicyuma hamwe nibizamini bya Etching, Ikizamini cya Flattening nibindi.
Gutanga Ubushobozi
Ubushobozi bwo gutanga: Toni 2000 buri kwezi Kumurongo wa ASTM A335 Umuyoboro wibyuma
Gupakira
Muri Bundles No Mubisanduku Bikomeye
Gutanga
Iminsi 7-14 niba mububiko, iminsi 30-45 yo gutanga
Kwishura
30% kubitsa, 70% L / C cyangwa B / L kopi cyangwa 100% L / C ukireba