Uruganda rugurisha neza Umuyoboro wicyuma Cyangwa Umuyoboro Kubyuka
Twifashishije porogaramu yuzuye yubumenyi yo mu rwego rwo hejuru, ireme ryiza kandi ryizera risumba ayandi, twamamaye cyane kandi twigaruriye inganda zuruganda rugurisha cyane Umuyoboro udafite ibyuma cyangwa Umuyoboro wa Pressure Boiler, Turabikuye ku mutima kandi turakinguye. Dutegereje uruzinduko rwawe no gushiraho umubano wizewe kandi wigihe kirekire.
Twifashishije porogaramu yuzuye ya siyansi yuzuye yo gucunga neza, ireme ryiza kandi ryizera cyane, turabona izina ryiza kandi twigaruriye ingandaUmuyoboro utagira ibyuma, umuyoboro w'icyuma, Isosiyete yacu yakira ibitekerezo bishya, kugenzura ubuziranenge bukomeye, urwego rwuzuye rwa serivisi ikurikirana, kandi yubahiriza gukora ibicuruzwa byiza. Ubucuruzi bwacu bugamije "kuba inyangamugayo kandi zizewe, igiciro cyiza, umukiriya mbere", nuko twatsindiye ikizere cyabakiriya benshi! Niba ushishikajwe nibicuruzwa na serivisi byacu, nyamuneka ntutindiganye kutwandikira!
Incamake
Gusaba
Ikoreshwa cyane cyane mugukora ibyuma byujuje ubuziranenge bwa karubone, ibyuma byubatswe byubatswe hamwe nicyuma kitarwanya ubushyuheumuyoboro w'icyumas kumuvuduko mwinshi no hejuru ya pompe yamashanyarazi.
Icyiciro rusange
Urwego rwicyuma cyiza cya karubone cyiza: 20g 、 20mng 、 25mng
Urwego rwibyuma byubaka ibyuma 15mog 、 20mog 、 12crmog 、 15crmog 、 12cr2mog 、 12crmovg 、 12cr3movsitib, nibindi
Urwego rwicyuma cyihanganira ubushyuhe1cr18ni9 1cr18ni11nb
Ibigize imiti
| 牌号 | 质量 等级 | 化学成分 (质量分数广小 /% | ||||||||||||||
| C | Si | Mn | P | S | Nb | V | Ti | Cr | Ni | Cu | Nd | Mo | B | Als ” | ||
| 不大于 | 不小于 | |||||||||||||||
| Q345 | A | 0.20 | 0.50 | 1.70 | 0.035 | 0.035 | 0.30 | 0.50 | 0.20 | 0.012 | 0.10 | —— | - | |||
| B | 0.035 | 0.035 | ||||||||||||||
| C | 0.030 | 0.030 | 0.07 | 0.15 | 0.20 | 0.015 | ||||||||||
| D | 0.18 | 0.030 | 0.025 | |||||||||||||
| E | 0.025 | 0.020 | ||||||||||||||
| Q390 | A | 0.20 | 0.50 | 1.70 | 0.035 | 0.035 | 0.07 | 0.20 | 0.20 | 0.3。 | 0.50 | 0.20 | 0.015 | 0.10 | - | - |
| B | 0.035 | 0.035 | ||||||||||||||
| C | 0.030 | 0.030 | 0,015 | |||||||||||||
| D | 0.030 | 0.025 | ||||||||||||||
| E | 0.025 | 0.020 | ||||||||||||||
| Q42O | A | 0.20 | 0.50 | 1.70 | 0.035 | 0.035 | 0.07 | 0.2。 | 0.20 | 0.30 | 0.80 | 0.20 | 0.015 | 0.20 | —— | —— |
| B | 0.035 | 0.035 | ||||||||||||||
| C | 0.030 | 0.030 | 0.015 | |||||||||||||
| D | 0.030 | 0.025 | ||||||||||||||
| E | 0.025 | 0.020 | ||||||||||||||
| Q46O | C | 0.20 | 0.60 | 1.80 | 0.030 | 0.030 | 0.11 | 0.20 | 0.20 | 0.30 | 0.80 | 0.20 | 0.015 | 0.20 | 0.005 | 0.015 |
| D | 0.030 | 0.025 | ||||||||||||||
| E | 0.025 | 0.020 | ||||||||||||||
| Q500 | C | 0J8 | 0.60 | 1.80 | 0.025 | 0.020 | 0.11 | 0.20 | 0.20 | 0.60 | 0.80 | 0.20 | 0.015 | 0.20 | 0.005 | 0.015 |
| D | 0.025 | 0.015 | ||||||||||||||
| E | 0.020 | 0.010 | ||||||||||||||
| Q550 | C | 0.18 | 0.60 | 2.00 | 0.025 | 0,020 | 0.11 | 0.20 | 0.20 | 0.80 | 0.80 | 0.20 | 0.015 | 0.30 | 0.005 | 0.015 |
| D | 0.025 | 0,015 | ||||||||||||||
| E | 0.020 | 0.010 | ||||||||||||||
| Q62O | C | 0.18 | 0.60 | 2.00 | 0.025 | 0.020 | 0.11 | 0.20 | 0.20 | 1.00 | 0.80 | 0.20 | 0.015 | 0.30 | 0.005 | 0.015 |
| D | 0.025 | 0.015 | ||||||||||||||
| E | 0.020 | 0.010 | ||||||||||||||
| 1除 Q345A 、 Q345B 牌号外，钢中应至少含有细化晶粒元素 Al 、 Nb 、 V 、 Ti 中的一种，根据需要，供方可添加其中 一种或几种细化晶粒元素，最大值应符合表中规定。组合加入时， Nb + V + Ti <0.22% ° * 对于 Q345 、 Q390 、 Q420 和 Q46O 牌号， Mo + Cr <0,30%o ° 各牌号的 Cr 、 Ni 作为残余元素时， Cr 、 Ni 含量应各不大于 0,30% ；当需要加入时，其含量应符合表中规定或由 供需双方协商确定。 JAl 、 Nb 、 V 、 Ti 等具有固氮作用 的合金元素，氮元素含量不作限制，固氮元素含量应在质量证明书中注明. '当采用全铝时，全铝含量 AIt ^ 0.020%B | ||||||||||||||||
Umutungo wa mashini
| No | Icyiciro | Umutungo wa mashini | ||||
|
|
| Umuhengeri | Tanga umusaruro | Kwagura | Tekereza (J) | Ukuboko |
| 1 | 20G | 410- | ≥ | 24/22% | 27/27 | - |
| 2 | 20MnG | 415- | ≥ | 22/20% | 27/27 | - |
| 3 | 25MnG | 485- | ≥ | 20/18% | 27/27 | - |
| 4 | 15MoG | 450- | ≥ | 22/20% | 27/27 | - |
| 6 | 12CrMoG | 410- | ≥ | 21/19% | 27/27 | - |
| 7 | 15CrMoG | 440- | ≥ | 21/19% | 27/27 | - |
| 8 | 12Cr2MoG | 450- | ≥ | 22/20% | 27/27 | - |
| 9 | 12Cr1MoVG | 470- | ≥ | 21/19% | 27/27 | - |
| 10 | 12Cr2MoWVTiB | 540- | ≥ | 18 / -% | 40 / - | - |
| 11 | 10Cr9Mo1VNbN | ≥ | ≥ | 20/16% | 27/27 | ≤ |
| 12 | 10Cr9MoW2VNbBN | ≥ | ≥ | 20/16% | 27/27 | ≤ |
Ibisabwa
Usibye kwemeza imiterere yimiti nubukanishi, ibizamini bya hydrostatike bikorwa umwe umwe, kandi hakorwa ibizamini byo gutwika no gusibanganya. . Mubyongeyeho, haribisabwa bimwe na microstructure, ingano yingano, hamwe na decarburisation yumuringoti urangiye.
Gutanga Ubushobozi
Ubushobozi bwo gutanga: Toni 2000 buri kwezi Kumurongo wa GB / T5310-2017 Umuyoboro wibyuma
Gupakira
Muri Bundles No Mubisanduku Bikomeye
Gutanga
Iminsi 7-14 niba mububiko, iminsi 30-45 yo gutanga
Kwishura
30% kubitsa, 70% L / C cyangwa B / L kopi cyangwa 100% L / C ukireba
Ibicuruzwa birambuye
Imiyoboro idafite ibyuma kubitutu byumuvuduko mwinshi
GB / T5310-2017
ASME SA-106 / SA-106M-2015
ASTMA210 (A210M) -2012
ASME SA-213 / SA-213M