Seamless steel pipe for high temperature operation ASTM A106, suitable for high temperature

Product Detail

Product Tags

Tianjin Gold Sanon Internation Co,.Ltd company engaged in steel pipe export business. Our advantages: Processing Equipment-We have our own factory, and we can produce steel pipes with OD up to 914 mm. Stockist-our steel pipes from Large steel mills (HENGYANG, LONTRIN, TIANDA, CHENGDE). 5000 tons per month in stock. Other services- We can find for customers steel pipes that are not in our warehouses. Dedicated to strict quality control and thoughtful customer service, our experienced staff members are always available to discuss your requirements and ensure full customer satisfaction for Stokist astm sa-106 carbon steel seamless pipe, We honor our core principal of Honesty in business, priority in company and will do our greatest to provide our customers with high-quality goods and fantastic provider.

Dedicated to strict quality control and thoughtful customer service, our experienced staff members are always available to discuss your requirements and ensure full customer satisfaction for carbon pipe, carbon pipe ASME, carbon pipe asme sa-106, carbon pipe sa-106, carbon seamless pipe, Carbon Steel Pipe, Carbon Steel Seamless Pipe, steel seamless pipe, We provide good quality but unbeatable low price and the best service. We are going to produce the items according to your request. If you are interested in any items we offer, please feel free to contact us directly by mail, fax, telephone or internet. We’ve been here to answer your questions from Monday to Saturday and looking forward to cooperating with you.

Overview

Application

Seamless steel pipe for high temperature operation ASTM A106, suitable for high temperature

Main Grade

Grade of high-quality carbon structural steel: GR.A,GR.B,GR.C

Chemical Component

	Composition, ％
	Grade A	Grade B	Grade C
Carbon, max	0.25A	0.3B	0.35B
Manganese	0.27-0.93	0.29-1.06	0.29-1.06
Phosphorus, max	0.035	0.035	0.035
Sulfur, max	0.035	0.035	0.035
Silicon, min	0.10	0.10	0.10
Chrome, maxC	0.40	0.40	0.40
Copper, maxC	0.40	0.40	0.40
Molybdenum, maxC	0.15	0.15	0.15
Nickel, maxC	0.40	0.40	0.40
Vanadium, maxC	0.08	0.08	0.08
A For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%.
B Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%.
C These five elements combined shall not exceed 1%.

Mechanical Property

	Grade A		Grade B		Grade C
Tensile strength, min, psi(MPa)	48 000(330)		60 000(415)		70 000(485)
Yield strength, min, psi(MPa)	30 000(205)		35 000(240)		40 000(275)
	Longitudinal	Transverse	Longitudinal	Transverse	Longitudinal	Transverse
Elongation in 2 in. (50 mm), min, % Basic minimum elongation transverse strip tests, and for all small sizes tested in full section	35	25	30	16.5	30	16.5
When standard round 2-in. (50-mm) gauge length test specimen is used	28	20	22	12	20	12
For longitudinal strip tests	A		A		A
For transverse strip tests, a deduction for each 1/32-in. (0.8-mm) decrease in wall thickness below 5/16 in. (7.9 mm) from the basic minimum elongation of the following percentage shall be made		1.25		1.00		1.00
A The minimum elongation in 2 in. (50 mm) shall be determined by the following equation:
e=625000A 0.2 / U 0.9
for inch-pound units, and
e=1940A 0.2 / U 0.9
for SI units,
where: e = minimum elongation in 2 in. (50 mm), %, rounded to the nearest 0.5%, A = cross-sectional area of the tension test specimen, in.2 (mm2), based upon specified outside diameter or nominal specified outside diameter or nominal specimen width and specified wall thickness, rounded to the nearest 0.01 in.2 (1 mm2). (If the area thus calculated is equal to or greater than 0.75 in.2 (500 mm2), then the value 0.75 in.2 (500 mm2) shall be used.), and U = specified tensile strength, psi (MPa).

Test Requirement

In addition to ensuring chemical composition and mechanical properties, hydrostatic tests are performed one by one, and flaring and flattening tests are performed. . In addition, there are certain requirements for the microstructure, grain size, and decarburization layer of the finished steel pipe.