abide ku kontrak", conforms kana sarat pasar, ngagabung dina kompetisi pasar ku kualitas luhur na ogé nyadiakeun layanan leuwih komprehensif sarta alus teuing pikeun klien pikeun ngidinan aranjeunna jadi juara badag. The ngudag pausahaan, nyaéta kapuasan klien 'pikeun Factory disadiakeun Api Lsaw Pipe Karbon Steel Pipe / tube Minyak Gas Minyak Seamless Tube, Produk kami anu rutin disadiakeun pikeun loba Grup sarta kavling Pabrik. Samentara éta, produk urang dijual ka AS, Italia, Singapura, Malaysia, Rusia, Polandia, jeung Wétan Tengah.
abide ku kontrak", conforms kana sarat pasar, ngagabung dina kompetisi pasar ku kualitas luhur na ogé nyadiakeun layanan leuwih komprehensif sarta alus teuing pikeun klien pikeun ngidinan aranjeunna jadi juara badag. The ngudag pausahaan, nyaeta kapuasan klien 'pikeunLsaw Pipe Karbon Steel Pipe, Tabung Minyak Gas Minyak, Tube Petroleum Gas Minyak Seamless Tube, Kami geus persisting dina hakekat bisnis "Kualitas Kahiji, Ngahormatan Kontrak jeung Nangtung ku Reputations, nyadiakeun konsumén jeung item satisfying sarta jasa. ” Babaturan boh di bumi sareng di luar negeri wilujeng sumping pikeun ngadegkeun hubungan bisnis anu langgeng sareng urang.
Tinjauan
Aplikasi
Tabung baja Seamless pikeun cracking minyak bumi anu lumaku pikeun tabung baja seamless pikeun tabung tungku, tabung bursa panas sarta pipa tekanan dina industri pétrokimia.
Kelas Utama
Kelas baja struktural karbon kualitas luhur: 10 #, 20 #
Komponén Kimia
| No | Kelas | Komponén Kimia% | ||||||||||||
| C | Si | Mn | Cr | Mo | Ni | Nb | Ti | V | Cu | P | S | |||
| ≤ | ||||||||||||||
| baja struktural karbon kualitas luhur | 10 | 0. 07-0.13 | 0.17 -0. 37 | 0.35 - 0.65 | <0.15 | <0.15 | <0. 25 | — | — | <0. 08 | <0. 20 | 0. 025 | 0. 015 | |
| 20 | 0.17-0. 23 | 0.17 -0. 37 | 0.35 - 0.65 | <0. 25 | <0.15 | <0. 25 | — | — | <0. 08 | <0. 20 | 0. 025 | 0. 015 | ||
| Baja struktural alloy | 12CrMo | 0. 08-0.15 | 0.17 - 0.37 | 0. 40-0. 70 | 0. 40-0. 70 | 0. 40 -0.55 | <0. 30 | — | — | 一 | <0. 20 | 0. 025 | 0. 015 | |
| 15CrMo | 0.12 - 0.18 | 0.17-0. 37 | 0.40 -0. 70 | 0. 80-1.1 | 0. 40-0.55 | <0. 30 | — | — | 一 | <0. 20 | 0. 025 | 0. 015 | ||
| 12CrlMo | 0. 08 - 0.15 | 0.50 -1. 00 | 0. 30-0.6 | 1.00-1. 50 | 0,45 - 0,65 | <0. 30 | — | — | — | <0, 20 | 0. 025 | 0. 015 | ||
| 12CrlMoV | 0. 08-0.15 | 0.17-0. 37 | 0. 40-0. 70 | 0.90-1.2 | 0. 25 - 0.35 | <0. 30 | — | — | 0.15 -0. 30 | <0. 20 | 0,025 | 0. 010 | ||
| 12Cr2Mo | 0.08-0.15 | <0. 50 | 0. 40-0. 60 | 2. 00-2. 50 | 0. 90-1.13 | <0. 30 | — | — | 一 | <0. 20 | 0. 025 | 0. 015 | ||
| 12Cr5MoI | <0.15 | <0. 50 | 0.30-0.6 | 4. 00-6 | 0. 45 -0. 60 | <0. 60 | — | — | <0. 20 | 0. 025 | 0. 015 | |||
| 12Cr5Bulan | ||||||||||||||
| 12Cr9MoI | <0.15 | 0. 25-1. 00 | 0. 30-0. 60 | 8.00 - 10. 00 | 0. 90-1.1 | <0. 60 | — | — | — | <0. 20 | 0. 025 | 0, 015 | ||
| 12Cr9MoNT | ||||||||||||||
| Stainless steel tahan panas | 07Crl9Nil0 | 0. 04-0.1 | <1. 00 | <2. 00 | 18. 00-20. 00 | — | 8. 00-11 | — | — | — | — | 0. 030 | 0. 015 | |
| 07Crl8NillNb | 0. 04-0.1 | <1. 00 | <2. 00 | 17. 00-19. 00 | — | 9.00-12. 00 | 8C-1.1 | — | — | — | 0. 030 | 0. 015 | ||
| 07Crl9NillTi | 0. 04-0.1 | <0. 75 | <2. 00 | 17.00-20. 00 | — | 9. 00~13. 00 | — | 4C-0. 60 | 一 | 一 | 0.03 | 0. 015 | ||
| 022Crl7Nil2Mo2 | <0. 030 | <1. 00 | <2. 00 | 16. 00-18. 00 | 2. 00-3. 00 | 10. 00 - 14. 00 | — | 一 | 一 | — | 0.03 | 0. 015 | ||
Milik mékanis
| No | Tensile MPa | Hasil MPa | Elong sanggeus narekahan A/% | Énergi nyerep Shork kv2/j | Jumlah karasa Brinell | ||
| potrét | transver | potrét | transver | ||||
| teu kurang ti | teu leuwih ti | ||||||
| 10 | 335-475 | 205 | 25 | 23 | 40 | 27 | |
| 20 | 410-550 | 245 | 24 | 22 | 40 | 27 | |
| 12CrMo | 410 nepi ka 560 | 205 | 21 | 19 | 40 | 27 | 156 HBW |
| 15CrMo | 440 nepi ka 640 | 295 | 21 | 19 | 40 | 27 | 170 HBW |
| 12CrlMo | 415 nepi ka 560 | 205 | 22 | 20 | 40 | 27 | 163 HBW |
| 12CrlMoV | 470-640 | 255 | 21 | 19 | 40 | 27 | 179 HBW |
| 12Cr2Mo | 450~600 | 280 | 22 | 20 | 40 | 27 | 163 HBW |
| 12Cr5MoI | 415-590 | 205 | 22 | 20 | 40 | 27 | 163 HBW |
| 12Cr5Bulan | 480 nepi ka 640 | 280 | 20 | 18 | 40 | 27 | — |
| 12Cr9MoI | 460 nepi ka 640 | 210 | 20 | 18 | 40 | 27 | 179 HBW |
| 12Cr9MoNT | 590—740 | 390 | 18 | 16 | 40 | 27 | |
| O7Crl9NilO | 2520 | 205 | 35 | 187 HBW | |||
| 07Crl8NillNb | >520 | 205 | 35 | — | 187 HBW | ||
| 07Crl9NillTi | >520 | 205 | 35 | — | — | 187 HBW | |
| 022Crl7Nil2Mo2 | >485 | 170 | 35 | 一 | — | 187 HBW | |
| Pikeun baja kalayan ketebalan témbok kirang ti 5mm tube ulah nyieun percobaan karasa | |||||||
Syarat Test
Salian mastikeun komposisi kimia sareng sipat mékanis, uji hidrolik kedah dilaksanakeun hiji-hiji, pamariksaan kakuatan rendah kedah dilaksanakeun pikeun pipa baja langsung digulung sareng ingot, sareng uji korosi intergranular kedah dilakukeun pikeun stainless (tahan panas). ) pipa baja.
Kamampuhan suplai
Kamampuhan suplai: 2000 Ton Per Bulan Per Kelas tina minyak bumi cracking pipa baja seamless
Bungkusan
Dina Bungkusan Jeung Dina Kotak Kayu Kuat
Pangiriman
7-14 poé lamun di stock, 30-45 poé pikeun ngahasilkeun
pangmayaran
30% depsoit, 70% L/C atawa salinan B/L atawa 100% L/C dina tetempoan
Rincian produk
mékanis / Kimia & Pupuk Pipa
GB / T8162-2008
ASTM_A519-2006
BS EN 10210-1-2006
ASTM A53A53M-2012
GB9948-2006
GB6479-2013