seamless alloy, irin pipe ASTM A335 P5
Akopọ
Standard: ASTM A335
Ẹgbẹ Ite: P5,P9,P11,P22,P91,P92 ati be be lo.
Sisanra: 1 - 100 mm
Ode opin (Yika): 10 - 1000 mm
Ipari: Gigun ti o wa titi tabi ipari laileto
Apẹrẹ Abala: Yika
Ibi ti Oti: China
Iwe eri: ISO9001:2008
Alloy Tabi Ko: Alloy
Ohun elo: igbomikana Pipe
Itọju Ilẹ: Bi ibeere alabara
Ilana: Gbona Yiyi / Tutu Fa
Itọju igbona: Annealing/normalizing/Tempering
Paipu Pataki: Nipọn Wall Pipe
Lilo: paipu ategun titẹ giga, igbomikana ati Oluyipada Ooru
Idanwo: ET/UT
Ohun elo
O ti wa ni o kun lo lati ṣe ga-didara alloy irin igbomikana pipe, ooru paarọ paipu, ga titẹ nya paipu fun Epo ilẹ ati kemikali ile ise
Akọkọ ite
Ite ti ga-didara alloy pipe: P1, P2, P5, P9, P11, P22, P91, P92 ati be be lo
Ohun elo Kemikali
| Ipele | UN | C≤ | Mn | P≤ | S≤ | Si≤ | Cr | Mo |
| Sequiv. | ||||||||
| P1 | K11522 | 0.10 ~ 0.20 | 0.30 ~ 0.80 | 0.025 | 0.025 | 0.10 ~ 0.50 | – | 0.44 ~ 0.65 |
| P2 | K11547 | 0.10 ~ 0.20 | 0.30 ~ 0.61 | 0.025 | 0.025 | 0.10 ~ 0.30 | 0.50 ~ 0.81 | 0.44 ~ 0.65 |
| P5 | K41545 | 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 4.00 ~ 6.00 | 0.44 ~ 0.65 |
| P5b | K51545 | 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 1.00 ~ 2.00 | 4.00 ~ 6.00 | 0.44 ~ 0.65 |
| P5c | K41245 | 0.12 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 4.00 ~ 6.00 | 0.44 ~ 0.65 |
| P9 | S50400 | 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.50 ~ 1.00 | 8.00 ~ 10.00 | 0.44 ~ 0.65 |
| P11 | K11597 | 0.05 ~ 0.15 | 0.30 ~ 0.61 | 0.025 | 0.025 | 0.50 ~ 1.00 | 1.00 ~ 1.50 | 0.44 ~ 0.65 |
| P12 | K11562 | 0.05 ~ 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 0.80 ~ 1.25 | 0.44 ~ 0.65 |
| P15 | K11578 | 0.05 ~ 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 1.15 ~ 1.65 | – | 0.44 ~ 0.65 |
| P21 | K31545 | 0.05 ~ 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 2.65 ~ 3.35 | 0.80 ~ 1.60 |
| P22 | K21590 | 0.05 ~ 0.15 | 0.30 ~ 0.60 | 0.025 | 0.025 | 0.5 | 1.90 ~ 2.60 | 0.87 ~ 1.13 |
| P91 | K91560 | 0.08 ~ 0.12 | 0.30 ~ 0.60 | 0.02 | 0.01 | 0.20 ~ 0.50 | 8.00 ~ 9.50 | 0.85 ~ 1.05 |
| P92 | K92460 | 0.07 ~ 0.13 | 0.30 ~ 0.60 | 0.02 | 0.01 | 0.5 | 8.50 ~ 9.50 | 0.30 ~ 0.60 |
Apejuwe Tuntun ti iṣeto ni ibamu pẹlu Iwa E 527 ati SAE J1086, Iṣe fun Nọmba Awọn irin ati Alloys (UNS). B Grade P 5c yoo ni akoonu titanium ti ko kere ju awọn akoko 4 akoonu erogba ko si ju 0.70%; tabi akoonu columbium ti 8 si 10 ni igba akoonu erogba.
Mechanical Ini
| Darí-ini | P1,P2 | P12 | P23 | P91 | P92,P11 | P122 |
| Agbara fifẹ | 380 | 415 | 510 | 585 | 620 | 620 |
| Agbara ikore | 205 | 220 | 400 | 415 | 440 | 400 |
Ooru Itọju
| Ipele | Ooru Itọju Iru | Didara Iwọn Iwọn F [C] | Subcritical Annealing tabi tempering |
| P5, P9, P11, ati P22 | Iwọn otutu F [C] | ||
| A335 P5 (b,c) | Kikun tabi Isothermal Anneal | ||
| Normalize ati Ibinu | ***** | 1250 [675] | |
| Anneal Subcritical (P5c nikan) | ***** | 1325 – 1375 [715-745] | |
| A335 P9 | Kikun tabi Isothermal Anneal | ||
| Normalize ati Ibinu | ***** | 1250 [675] | |
| A335 P11 | Kikun tabi Isothermal Anneal | ||
| Normalize ati Ibinu | ***** | 1200 [650] | |
| A335 P22 | Kikun tabi Isothermal Anneal | ||
| Normalize ati Ibinu | ***** | 1250 [675] | |
| A335 P91 | Normalize ati Ibinu | Ọdun 1900-1975 [1040 - 1080] | 1350-1470 [730 - 800] |
| Quench ati Ibinu | Ọdun 1900-1975 [1040 - 1080] | 1350-1470 [730 - 800] |
Ifarada
Fun paipu ti a paṣẹ si inu iwọn ila opin, iwọn ila opin inu ko ni yatọ ju 6 1% lati inu iwọn ila opin ti a pato
Awọn iyatọ ti o gba laaye ni Ode Iwọn
| NPS onise | in | mm | in | mm |
| 1⁄8to 11⁄2, pẹlu | 1⁄64 (0.015) | 0.4 | 1⁄64 (0.015) | 0.4 |
| Ju 11⁄2 si 4, pẹlu. | 1⁄32 (0.031) | 0.79 | 1⁄32 (0.031) | 0.79 |
| Ju 4 si 8, pẹlu | 1⁄16 (0.062) | 1.59 | 1⁄32 (0.031) | 0.79 |
| Ju 8 si 12, pẹlu. | 3⁄32 (0.093) | 2.38 | 1⁄32 (0.031) | 0.79 |
| Ju 12 lọ | 6 1% ti pato ita opin |
Ibeere idanwo
Idanwo Hydraustatic:
Paipu Irin yẹ ki o ṣe idanwo Hydraulically Ọkan Nipa Ọkan. Iwọn Idanwo ti o pọju jẹ 20 MPa. Labẹ Ipa Igbeyewo, Akoko Imuduro yẹ ki o Ko kere ju 10 S, Ati Pipe Irin ko yẹ ki o jo.
Lẹhin ti Olumulo Gba, Idanwo Hydraulic le Rọpo nipasẹ Idanwo Eddy lọwọlọwọ Tabi Idanwo Leakage Flux oofa.
Idanwo ti ko ni iparun:
Awọn paipu ti o nilo Ayẹwo diẹ sii yẹ ki o ṣe ayẹwo Ultrasonically Ọkan nipasẹ Ọkan. Lẹhin Idunadura Nbeere Gbigbanilaaye ti Ẹka Ati Ti Ni pato ninu Adehun naa, Idanwo miiran ti kii ṣe iparun le ṣe afikun.
Idanwo fifẹ:
Awọn Tubes Pẹlu Iwọn Iwọn Ita Ti o tobi ju 22 mm yoo wa labẹ Idanwo Filati kan. Ko si Delamination ti o han, awọn aaye funfun, tabi awọn aimọ yẹ ki o waye lakoko idanwo gbogbo.
Idanwo Lile:
Fun paipu ti Awọn giredi P91, P92, P122, ati P911, Brinell, Vickers, tabi Rockwell awọn idanwo lile ni ao ṣe lori apẹrẹ lati ọpọlọpọ kọọkan
Idanwo tẹ:
Fun paipu ti iwọn ila opin rẹ kọja NPS 25 ati iwọn ila opin rẹ si ipin sisanra ogiri jẹ 7.0 tabi kere si ni yoo tẹriba idanwo tẹ dipo idanwo fifẹ. Paipu miiran ti iwọn ila opin rẹ dọgba tabi ju NPS 10 lọ ni a le fun ni idanwo tẹ ni aaye ti idanwo fifẹ koko ọrọ si ifọwọsi ti olura.
Alaye ọja
ASTM A335 P5 jẹ ohun elo alloy, irin ti ko ni ailopin ferritic paipu otutu giga ti boṣewa Amẹrika. Alloy tube jẹ iru tube irin ti ko ni idọti, iṣẹ rẹ ga julọ ju ọpọn irin ti o wọpọ lọ, nitori iru tube irin yii ni diẹ sii C, iṣẹ naa kere ju tube irin-irin ti o wọpọ, nitorina tube alloy ti wa ni lilo pupọ. ni Epo ilẹ, Aerospace, kemikali, ina mọnamọna, igbomikana, ologun ati awọn ile-iṣẹ miiran.
Alloy Steel pipe ni awọn iwọn idaran ti awọn eroja miiran yatọ si erogba gẹgẹbi nickel, chromium, silikoni, manganese, tungsten, molybdenum, vanadium ati awọn iye to lopin ti awọn eroja miiran ti a gba nigbagbogbo gẹgẹbi manganese, sulfur, silicon, and phosphorous
Ibamu irin alloy abele: 1Cr5Mo GB 9948-2006 “Iwọn Pipe Irin Pipe fun Gbigbọn Epo”
- Isanwo: 30% Idogo, 70% L/C Tabi B/L Daakọ Tabi 100% L/C Ni Oju
- Min.Order Opoiye: 1 PC
- Agbara Ipese: Ọdọọdun 20000 Tọnu Oja Ti Pipe Irin
- Akoko asiwaju: Awọn ọjọ 7-14 Ti o ba wa ni Iṣura, Awọn ọjọ 30-45 Lati Ṣejade
- Iṣakojọpọ: Black Vanishing, Bevel Ati fila Fun Gbogbo Pipe Kan; OD Ni isalẹ 219mm Nilo Lati Ṣe akopọ Ni Lapapo, Ati Lapapo kọọkan Ko kọja Awọn Toonu 2.
Akopọ
| Standard: ASTM A335 | Alloy Tabi Ko: Alloy |
| Ẹgbẹ ipele: P5 | Ohun elo: igbomikana Pipe |
| Sisanra: 1 - 100 mm | Itọju Ilẹ: Bi Ibeere Onibara |
| Iwọn Ode (Yika): 10 - 1000 mm | Ilana: Gbona Yiyi / Tutu Fa |
| Ipari: Ipari Ti o wa titi Tabi Ipari Laileto | Itọju Ooru: Annealing/Normalizing/Tempering |
| Apẹrẹ Abala: Yika | Paipu Pataki: Nipọn Wall Pipe |
| Ibi ti Oti: China | Lilo: Paipu Nya Titẹ Ga, igbomikana Ati Oluyipada Ooru |
| Iwe eri: ISO9001:2008 | Idanwo: ET/UT |
Ohun elo
O ti wa ni akọkọ Lo Lati Ṣe Didara Aloy Alloy Steel Boiler Pipe, Ooru Paṣipaapa Pipa, Giga Titẹ Nya Pipe Fun Epo ati Kemikali ile ise
Ohun elo Kemikali
| Awọn akojọpọ | Data |
| UNS Designa-iṣẹ | K41545 |
| Erogba (o pọju) | 0.15 |
| Manganese | 0.30-0.60 |
| Fọsifọọsi (o pọju) | 0.025 |
| Silikoni (ti o pọju) | 0.50 |
| Chromium | 4.00-6.00 |
| Molybdenum | 0.45-0.65 |
| Awọn eroja miiran | … |
Mechanical Ini
| Awọn ohun-ini | Data |
| Agbara Fifẹ, Min, (MPa) | 415 Mpa |
| Agbara ikore, Min, (MPa) | 205 Mpa |
| Ilọsiwaju, Min, (%), L/T | 30/20 |
Ooru Itọju
| Ipele | Ooru Itọju Iru | Didara Iwọn Iwọn F [C] | Subcritical Annealing Tabi tempering |
| P5, P9, P11, Ati P22 | Iwọn otutu F [C] | ||
| A335 P5 (B,C) | Full Tabi isothermal Anneal | ||
| A335 P5b | Normalize Ati Ibinu | ***** | 1250 [675] |
| A335 P5c | Subcritical Anneal | ***** | 1325 – 1375 [715-745] |
Ifarada
Fun Pipe Paapu Si Inu Inu, Iwọn Inu Ko Ni Yato Diẹ sii ju ± 1% Lati Iwọn Inu Inu Ti pato
Awọn iyatọ ti o gba laaye Ni Ode Iwọn
| NPS onise | Ifarada to dara | odi ifarada | ||
| In | Mm | In | Mm | |
| 1⁄8to 11⁄2, Incl | 1⁄64 (0.015) | 0.4 | 1⁄64 (0.015) | 0.4 |
| Ju 11⁄2 Si 4, Incl. | 1⁄32 (0.031) | 0.79 | 1⁄32 (0.031) | 0.79 |
| Ju 4 Si 8, Incl | 1⁄16 (0.062) | 1.59 | 1⁄32 (0.031) | 0.79 |
| Ju 8 Si 12, Incl. | 3⁄32 (0.093) | 2.38 | 1⁄32 (0.031) | 0.79 |
| Ju 12 lọ | ± 1% Ti pato Ita Iwọn opin | |||
Ibeere idanwo
Idanwo Hydraustatic:
Paipu Irin yẹ ki o ṣe idanwo Hydraulically Ọkan Nipa Ọkan. Iwọn Idanwo ti o pọju jẹ 20 MPa. Labẹ Ipa Igbeyewo, Akoko Imuduro yẹ ki o Ko kere ju 10 S, Ati Pipe Irin ko yẹ ki o jo.
Lẹhin ti Olumulo Gba, Idanwo Hydraulic le Rọpo nipasẹ Idanwo Eddy lọwọlọwọ Tabi Idanwo Leakage Flux oofa.
Idanwo ti ko ni iparun:
Awọn paipu ti o nilo Ayẹwo diẹ sii yẹ ki o ṣe ayẹwo Ultrasonically Ọkan nipasẹ Ọkan. Lẹhin Idunadura Nbeere Gbigbanilaaye ti Ẹka Ati Ti Ni pato ninu Adehun naa, Idanwo miiran ti kii ṣe iparun le ṣe afikun.
Idanwo fifẹ:
Awọn Tubes Pẹlu Iwọn Iwọn Ita Ti o tobi ju 22 mm yoo wa labẹ Idanwo Filati kan. Ko si Delamination ti o han, awọn aaye funfun, tabi awọn aimọ yẹ ki o waye lakoko idanwo gbogbo.
Idanwo Lile:
Fun Pipe ti Awọn gilaasi P91, P92, P122, Ati P911, Brinell, Vickers, Tabi Awọn Idanwo Lile Rockwell yoo ṣee ṣe Lori Apeere Lati Ọpọ kọọkan
Idanwo tẹ:
Fun Paipu Ti Iwọn Rẹ Tayọ NPS 25 Ati Iwọn Rẹ Si Iwọn Sisanra Odi Jẹ 7.0 Tabi Kere Ni Yoo Wa labẹ Idanwo Titẹ Dipo Ti Idanwo Filati. Paipu Omiiran Ti Iwọn Rẹ dọgba tabi O kọja NPS 10 Ṣe O le Fun Idanwo Titẹ Ni aaye Ti Idanwo Fifẹ Koko-ọrọ si Ifọwọsi ti Olura.
Ohun elo & iṣelọpọ
Paipu le jẹ boya ti pari gbona tabi iyaworan tutu pẹlu itọju ooru ipari ti a ṣe akiyesi ni isalẹ.
Ooru Itọju
- A/N+T
- N+T/Q+T
- N+T
Mechanical Igbeyewo Pato
- Idanwo Ẹdọfu Iyipada tabi Gigun ati Idanwo Fifẹ, Idanwo Lile, tabi Idanwo Titẹ
- Fun ooru ohun elo ti a tọju ni ileru iru ipele, awọn idanwo yoo ṣee ṣe lori 5% paipu lati ibi itọju kọọkan. Fun ọpọlọpọ kekere, o kere ju paipu kan ni a gbọdọ ṣe idanwo.
- Fun ooru ohun elo ti a tọju nipasẹ ilana lilọsiwaju, awọn idanwo yoo ṣee ṣe lori nọmba pipe ti paipu lati jẹ 5% ti Pupo, ṣugbọn ni ọran ko kere ju paipu 2.
Awọn akọsilẹ fun Idanwo Titẹ:
- Fun paipu ti iwọn ila opin rẹ kọja NPS 25 ati iwọn ila opin rẹ si ipin sisanra ogiri jẹ 7.0 tabi kere si ni yoo tẹriba idanwo tẹ dipo idanwo fifẹ.
- Paipu miiran ti iwọn ila opin rẹ dọgba tabi ju NPS 10 lọ ni a le fun ni idanwo tẹ ni aaye ti idanwo fifẹ koko ọrọ si ifọwọsi ti olura.
- Awọn apẹẹrẹ idanwo tẹ ni yoo tẹ ni iwọn otutu yara nipasẹ 180 laisi fifọ ni ita ti ipin ti tẹ.
ASTM A335 P5 awọn tubes irin alailẹgbẹ jẹ o dara fun omi, nya, hydrogen, epo ekan, bbl Ti a ba lo fun oru omi, iwọn otutu ti o pọ julọ jẹ 650℃; Nigbati a ba lo ni alabọde ṣiṣẹ gẹgẹbi epo ekan, o ni ipata ipata imi-ọjọ ti o dara, ati pe a lo nigbagbogbo ni awọn ipo ipata imi-ọjọ otutu ti 288 ~ 550.℃.
Ilana iṣelọpọ:
1. Yiyi gbigbona (irin tube ti a ko ni itọlẹ) : yika tube billet → alapapo → perforation → yiyi agbelebu mẹta-yiyi, yiyi lilọsiwaju tabi extrusion → yiyọ tube → iwọn (tabi dinku) → itutu → taara → idanwo titẹ omi (tabi wiwa abawọn abawọn). ) → isamisi → ibi ipamọ
2. Tutu iyaworan (yiyi) tube irin ti ko ni alaini: yika tube billet → alapapo → perforation → akọle → annealing → pickling → oiling (fifun bàbà) → iyaworan tutu-ọpọlọpọ (yiyi tutu) → tube òfo → itọju ooru → taara → omi idanwo titẹ (wiwa abawọn) → isamisi → ibi ipamọ
Awọn oju iṣẹlẹ elo:
Ni oju aye ati awọn ẹrọ igbale fun sisẹ epo robi efin giga-giga, ASTM A335 P5 awọn tubes irin ti ko ni ailagbara ni a lo ni akọkọ fun awọn opo gigun ti isalẹ ti oju aye ati awọn ile-iṣọ igbale, awọn tubes ileru ti oju aye ati awọn ileru igbale, awọn apakan iyara giga ti oju aye ati iyipada epo igbale awọn ila ati awọn epo-iwọn otutu miiran ati awọn opo gigun ti gaasi ti o ni imi-ọjọ.
Ni awọn ẹya FCC, ASTM A335 P5 awọn tubes irin alailẹgbẹ ni a lo ni akọkọ ni slurry otutu otutu, ayase ati awọn opo gigun ti isọdọtun, ati diẹ ninu awọn epo imi-ọjọ otutu giga miiran ati awọn opo gigun ti gaasi.
Ni ẹyọ coking idaduro, ASTM A335 P5 paipu irin ti ko ni alaini ti a lo ni akọkọ fun paipu ifunni iwọn otutu giga ni isalẹ ile-iṣọ coke ati epo otutu giga ati paipu gaasi ni oke ile-iṣọ coke, paipu ileru ni isalẹ ileru coke, pipe ni isalẹ ti fracking ile-iṣọ ati diẹ ninu awọn miiran ga otutu epo ati gaasi paipu ti o ni imi-ọjọ.