API 5L vasega X52 (L360)PSL1, vasega X52N (L360N) PSL2 Su'ega vaila'au, mea fa'amalosi ma fa'apalepale puipui mafiafia o fafo.

API 5Lpaipa uamea paipa

Vasega uamea: L360 poʻo le X52 (PSL1)

Mana'oga tu'ufa'atasiga vaila'au:

C: ≤0.28(seamless) ≤0.26(uelo)

Mn: ≤1.40

P: ≤0.030

S: ≤0.030

Cu: 0.50 pe itiiti

Ni: ≤0.50

Cr: ≤0.50

Mo: ≤0.15

*V+Nb+Ti: ≤0.15

* E mafai ona fa'atuputeleina le manganese i le 0.05% mo 0.01% fa'aitiitiga uma o le carbon content, e o'o atu i le maualuga o le 1.65%

Manaoga o mea tau masini:

Malosiaga maua: ≥360Mpa

Malosiaga tensile: ≥460Mpa

Weld tensile malosi o paipa uamea uelo: ≥460Mpa

Elongation: ≥1940* AXC0.2/4600.9 , lea o le AXC o le vaega faʻasolosolo o le faʻataʻitaʻiga tensile

Fa'apalepale pito i fafo o paipa u'amea:

I fafo D mm Fa'ai'u i fafo va'aiga mamao mm
paipa u'amea lamolemole Uila paipa uamea
<60.3 -0.8, +0.4
60.3 D pe itiiti ifo 168.3 pe itiiti -0.4, +1.6
168.3 < D≤610 ±0.005D, ae maualuga ±1.6
610 < D≤1422 + / - 2.0 + / - 1.6
> 1422 I le maliliega

 

Pa puipui mafiafia faapalepale of uamea paipa:

Mafiafia puipui t mm Fa'apalepale mm
paipa u'amea lamolemole
4.0 pe itiiti +0.6, -0.5
4 < t < 25 +0.150t, -0.125t
25 pe sili atu +3.7 poʻo le +0.1t, poʻo fea lava e sili atu -3.0 poʻo -0.1t, ave le tele
Fa'apa'au fa'apau
5.0 pe itiiti + / - 0.5
5.0 <t < 15 Fa'aopoopo pe to'ese 0.1 t
15 pe sili atu + / - 1.5

 

API 5L paipa paipa

Uamea vasega: L360N or X52N(PSL2)

Kemisi fatuga mana'oga:

C: ≤0.24

Si: ≤0.45

Mn: ≤1.40

P: ≤0.025

S: ≤0.015

V: ≤0.10

Nb:≤0.05

Ti: ≤0.04

Ku: ≤0.50

Ni: ≤0.30

Cr: ≤0.30

Mo: ≤0.15

V+Nb+Ti: ≤0.15

* E mafai ona fa'atuputeleina le manganese i le 0.05% mo 0.01% uma fa'aitiitiga o le kaponi, e o'o atu i le maualuga o le 1.65%.

* E leai se fa'aopoopoga fa'amoemoeina ole boron e fa'atagaina, o totoe B≤0.001%

kaponi tutusa:

CEP cm : ≤0.25

CEIIW : ≤0.43

* Fa'aaoga le CE pe a sili atu le kaponi i le 0.12%, ma fa'aaoga le CE IIW pe aP cm le kaponi e la'ititi ifo pe tutusa ma le 0.12%.

CEP cm = C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+5B

Afai o le taunuuga o le smelting auiliiliga o B e itiiti ifo i le 0.0005%, e leai se manaʻoga e aofia ai le auiliiliga o elemene B i le auiliiliga o oloa, ma o le B anotusi e mafai ona togafitia e pei o le zero i le carbon equivalent CEP cm fuafuaina.

CEIIW =C+Mn/6 (C+Mo+V)/5+(Ni+Cu)/ 15

Fa'ainisinia meatotino mana'oga:

Malosiaga maua: 360-530Mpa

Malosiaga Tensile: 460-760Mpa

Fuafua fua faatatau: ≤0.93 (na'o le D> 323.9mm paipa uamea)

Weld tensile malosi o paipa uamea uelo: ≥460Mpa

Fa'aumiumi maualalo: = 1940* AXC0.2/4600.9 , lea o le AXC o le vaega fa'alava o le fa'ata'ita'iga tensile.

Su'ega a'afiaga CVN ole paipa

Su'ega vevela 0 .C

Fa'ailoa le lautele i fafo o le D mm CVN tetele atoaMalosi maiKVJ
508 pe itiiti ifo 27
> 508 i le 762 27
> 762 i le 914 40
> 914 i le 1219 40
> 1219 i le 1422 40
> 1422 i le 2134 40

fafo lautele faapalepale of uamea paipa:

I fafo D mm Fa'ai'u ese'ese le lautele o fafo
paipa u'amea lamolemole Uila paipa uamea
<60.3 -0.4, +0.8
60.3 D pe itiiti ifo 168.3 pe itiiti -0.4, +1.6
168.3 < D=610 ±0.005D, ae maualuga ±1.6
610 < D=1422 + / - 2.0 + / - 1.6
> 1422 I le maliliega

Pa puipui mafiafia faapalepale of uamea paipa:

Mafiafia puipui t mm Fa'apalepale
paipa u'amea lamolemole
4.0 pe itiiti +0.6, -0.5
4 < t < 25 +0.150t, -0.125t
25 pe sili atu +3.7 po o le +0.1t, po o fea lava e telē atu

-3.0 poʻo -0.1t, ave tele

Paipa uelo
5.0 pe itiiti + / - 0.5
5.0 <t <15 Fa'aopoopo pe to'ese 0.1 t
15 pe sili atu + / - 1.5

Taimi meli: Sep-26-2023