China [Copy] GB 3087 ọkọlọtọ enweghị nkebi ji esi mmiri ọkụ alloy ígwè ọkpọkọ ala mgbali Ọkara mgbali emeputa na Supplier

[Detuo] GB 3087 ọkọlọtọ enweghị nkebi na-esi esi mmiri ọkụ alloy ígwè ọkpọkọ obere nrụgide Ọkara

[Detuo] GB 3087 ọkọlọtọ enweghị enweghị nkebi na-esi esi mmiri ọkụ alloy ígwè ọkpọkọ obere nrụgide Ọkara egosipụtara

Nkọwa dị mkpirikpi:

GB T3087-2008

obere nrụgide Ọkara mmiri ọkụ ọkpọkọ ibu kpụ ọkụ n'ọnụ uzuoku ọkpọkọ elu àgwà enweghị nkebi carbon ígwè anwụrụ

tumadi maka ahịa India nwere asambodo IBR

GB 3087-2008 ″ tube nchara na-enweghị ntụpọ maka igwe ọkụ ọkụ dị ala na nke ọkara” yana GB5310-2008 ″ tube nchara na-enweghị ntụpọ maka ihe ọkụkụ dị elu. Ọdịdị ọdịdị: cracks, mpịachi, Rolling,scarring, nkewa na wrinkles adịghị ekwe na n'ime na n'èzí elu nke ígwè ọkpọkọ.Ndị a ntụpọ kwesịrị ikpochapụ kpamkpam.The mkpochapụ omimi agaghị gafere ọjọọ deviation nke nominal mgbidi ọkpụrụkpụ, na n'ezie ọkpụrụkpụ mgbidi na mkpochapụ agaghị abụ ihe na-erughị opekempe kacha ekwe ọkpụrụkpụ mgbidi.

Ụgwọ:30% nkwụnye ego, 70% L / C ma ọ bụ B / L oyiri ma ọ bụ 100% L / C na anya

Ọnụ ọgụgụ nke Min.1 PC

Ikike inye:Ndepụta Tọn 20000 kwa afọ nke ọkpọ ígwè

Etiti oge:7-14 ụbọchị ma ọ bụrụ na ngwaahịa, 30-45 ụbọchị na-emepụta

Nkwakọ ngwaahịa:Black Vanishing, bevel na okpu maka otu ọkpọkọ ọ bụla; OD n'okpuru 219mm kwesịrị ịkwakọ na ngwugwu, na ngwugwu ọ bụla agaghị agafe tọn 2.

Zitere anyị email Budata dị ka PDF

Nkọwa ngwaahịa

Mkpado ngwaahịa

Nchịkọta

Ọkọlọtọ: GB/T3087-2008

Otu ọkwa: 10#,20#

Ọkpụrụkpụ: 1 - 100 mm

Dayameta dị n'èzí (Gburugburu): 10 - 1000 mm

Ogologo: Ogologo ogologo ma ọ bụ ogologo enweghị usoro

Ụdị ngalaba: Gburugburu

Ebe Mmalite: China

Asambodo: ISO9001:2008

Alloy Ma ọ bụ Ọ bụghị: carbon steel enweghị nkebi

Ngwa: Ọkpụkpọ ọkpọkọ

Ọgwụgwọ dị n'elu: Dị ka ihe ndị ahịa chọrọ

Usoro: Hot Rolled/ oyi sere

Ọgwụgwọ okpomọkụ: Normalizing

Ọkụ Pụrụ Iche: Ọkụ Mgbidi

Ojiji: Mwube, Ụgbọ njem mmiri, Igwe ọkụ na ihe ngbanwe ọkụ

Nnwale: ET/UT

Ngwa

A na-eji ya eme ihe dị elu nke carbon structural steel, ọkpọkọ mmiri ọkụ dị ala, nnukwu uzuoku uzuoku enweghị nkebi carbon steel pipe.

Isi ọkwa

Ọkwa nke elu-edu carbon structural ígwè: 10#,20#

Ngwakọta kemịkalụ

Ọkọlọtọ	Ọkwa	Ngwakọta kemịkalụ(%)
		C	Si	Mn	P	S	Cr	Cu	Ni
GB3087	10	0.07 ~ 0.13	0.17 ~ 0.37	0.38 ~ 0.65	≤0.030	≤0.030	0.3 ~ 0.65	≤0.25	≤0.30
	20	0.17 ~ 0.23	0.17 ~ 0.37	0.38 ~ 0.65	≤0.030	≤0.030	0.3 ~ 0.65	≤0.25	≤0.30

Ngwongwo igwe

Ọkọlọtọ	Ọkpụkpụ ígwè	Ọkpụrụkpụ mgbidi	Ike ọdụdọ	Mpụta Ike	Ogologo oge
GB3087		(mm)	(MPa)	(MPa)	%
				≥
	10	/	335 ~ 475	195	24
	20	15	410 ~ 550	245	20
	20	≥15	410 ~ 550	225	20

Ndidi

Ikwenye ngbanwe nke dayameta mpụta nke tubes ígwè

Ụdị tube ígwè				Ngbanwe ekwe omume
Hot akpọrepu (extruded, gbasaa) ígwè tube				± 1.0% D ma ọ bụ ± 0.50, were ọnụ ọgụgụ ka ukwuu
Oyi adọtara (akpọrela) ígwè tube				± 1.0% D ma ọ bụ ± 0.30, were ọnụ ọgụgụ ka ukwuu

Ikwenye iche iche nke mgbidi ọkpụrụkpụ nke na-ekpo ọkụ akpọrepu (extrusion, mgbasa) ígwè tubes

Nkeji: mm

Ụdị tube ígwè	Dayameta dị n'èzí nke tube ígwè	S/D	Ngbanwe ekwe omume
na-ekpo ọkụ akpọrepu (extruded) ígwè tube	≤ 102	-	± 12.5% S ma ọ bụ ± 0.40, were ọnụ ọgụgụ ka ukwuu
	> 102	≤ 0.05	± 15% S ma ọ bụ ± 0.40, were ọnụ ọgụgụ ka ukwuu
		> 0.05 ~ 0.10	± 12.5% S ma ọ bụ ± 0.40, were ọnụ ọgụgụ ka ukwuu
		> 0.10	+ 12.5% S
			-10% S
na-ekpo ọkụ ịgbasa ígwè tube	+ 15% S

Ikwenye iche iche nke mgbidi ọkpụrụkpụ oyi adọta (akpọrela) ígwè tubes

Nkeji: mm

Ụdị tube ígwè	Ọkpụrụkpụ mgbidi	Ngbanwe ekwe omume
Oyi adọtara (akpọrela) ígwè tube	≤ 3	15-10 % S ma ọ bụ ± 0.15, were ọnụ ọgụgụ ka ukwuu
	> 3	+ 12.5% S
		-10% S

Achọrọ nnwale

Nnwale ire ụtọ

Ọkpụkpụ ígwè nwere dayameta dị n'èzí karịa 22 mm na ruo 400 mm, na ọkpụrụkpụ mgbidi karịrị 10 mm kwesịrị ịnwale ule ncha. Mgbe ihe atụ na-agbadata

Nnwale ịgbagọ

Ọkpụkpụ ígwè nwere dayameta dị n'èzí na-erughị 22 mm kwesịrị ịnwale ule ịgbagọ. Nkuku na-ehulata bụ 90o. Oghere nke na-ehulata bụ okpukpu 6 dị n'èzí nke tube ígwè. Mgbe ị na-ehulata ihe nlele ahụ, a naghị ekwe ka ọkpụkpụ ma ọ bụ mgbawa na-apụta na ihe nlele ahụ.

Nyocha macroscopic

N'ihi na ígwè tubes kpọmkwem mere site na mgbe na-awụpụ billets ma ọ bụ nchara ingots, ndị na-eweta kwesịrị ekwe nkwa na ọ dịghị ọcha ntụpọ, adịghị ọcha, sub-elu elu ikuku egosipụta, okpokoro isi ma ọ bụ layering na cross-section acid pickled macroscopic anụ ahụ nke billet ma ọ bụ. ígwè tube.

Nyocha na-adịghị emebi emebi

Dị ka arịrịọ nke onye ahụ na-achọsi ike, nke a na-emekọrịta n'etiti ndị na-enye ihe na ndị na-achọsi ike ma gosipụta na nkwekọrịta ahụ, enwere ike ịchọta ntụpọ ultrasonic n'otu n'otu maka tubes ígwè. Njọ akwụkwọ ntuziaka ogologo nke tube sample kwesịrị iru ihe achọrọ maka ọkwa nnabata post-elele C8 akọwapụtara na GB/T 5777-1996.