enweghị nkebi ji esi mmiri ọkụ alloy ígwè ọkpọkọ ala mgbali Ọkara mgbali
| Ọkọlọtọ:GB/T3087-2008 | Alloy Ma ọ bụ Ọ bụghị: carbon steel enweghị nkebi |
| Otu ọkwa: 10#,20# | Ngwa: Ọkpụkpọ ọkpọkọ |
| Ọkpụrụkpụ: 1-100 mm | Ọgwụgwọ dị n'elu: Dị ka ihe ndị ahịa chọrọ |
| Dayameta dị n'èzí (Gburugburu): 10 - 1000 mm | Usoro: Hot Rolled/ oyi sere |
| Ogologo: Ogologo ogologo ma ọ bụ ogologo enweghị usoro | Ọgwụgwọ okpomọkụ: Normalizing |
| Ụdị ngalaba: Gburugburu | Ọkụ Pụrụ Iche: Ọkụ Mgbidi |
| Ebe Mmalite: China | Ojiji: Mwube, Ụgbọ njem mmiri, Igwe ọkụ na ihe ngbanwe ọkụ |
| Asambodo: ISO9001:2008 | Nnwale: ET/UT |
A na-eji ya eme ihe dị elu nke carbon structural steel, ọkpọkọ mmiri ọkụ dị ala, nnukwu uzuoku uzuoku enweghị nkebi carbon steel pipe.
Ọkwa nke elu-edu carbon structural ígwè: 10#,20#
| Ọkọlọtọ | Ọkwa | Ngwakọta kemịkalụ(%) | |||||||
| C | Si | Mn | P | S | Cr | Cu | Ni | ||
| GB3087 | 10 | 0.07 ~ 0.13 | 0.17 ~ 0.37 | 0.38 ~ 0.65 | ≤0.030 | ≤0.030 | 0.3 ~ 0.65 | ≤0.25 | ≤0.30 |
| 20 | 0.17 ~ 0.23 | 0.17 ~ 0.37 | 0.38 ~ 0.65 | ≤0.030 | ≤0.030 | 0.3 ~ 0.65 | ≤0.25 | ≤0.30 | |
| Ọkọlọtọ | Ọkpụkpụ ígwè | Ọkpụrụkpụ mgbidi | Ike ọdụdọ | Mpụta Ike | Ogologo oge |
| GB3087 | (mm) | (MPa) | (MPa) | % | |
| ≥ | |||||
| 10 | / | 335 ~ 475 | 195 | 24 | |
| 20 | 15 | 410 ~ 550 | 245 | 20 | |
| ≥15 | 225 | ||||
Ikwenye ngbanwe nke dayameta mpụta nke tubes ígwè
| Ụdị tube ígwè | Ngbanwe ekwe omume | ||||||
| Hot akpọrepu (extruded, gbasaa) ígwè tube | ± 1.0% D ma ọ bụ ± 0.50, were ọnụ ọgụgụ ka ukwuu | ||||||
| Oyi adọtara (akpọrela) ígwè tube | ± 1.0% D ma ọ bụ ± 0.30, were ọnụ ọgụgụ ka ukwuu | ||||||
Ikwenye iche iche nke mgbidi ọkpụrụkpụ nke na-ekpo ọkụ akpọrepu (extrusion, mgbasa) ígwè tubes
Nkeji: mm
| Ụdị tube ígwè | Dayameta dị n'èzí nke tube ígwè | S / D | Ngbanwe ekwe omume | ||||||
| na-ekpo ọkụ akpọrepu (extruded) ígwè tube | ≤ 102 | - | ± 12.5% S ma ọ bụ ± 0.40, were ọnụ ọgụgụ ka ukwuu | ||||||
| > 102 | ≤ 0.05 | ± 15% S ma ọ bụ ± 0.40, were ọnụ ọgụgụ ka ukwuu | |||||||
| > 0.05 ~ 0.10 | ± 12.5% S ma ọ bụ ± 0.40, were ọnụ ọgụgụ ka ukwuu | ||||||||
| > 0.10 | + 12.5% S | ||||||||
| -10% S | |||||||||
| na-ekpo ọkụ ịgbasa ígwè tube | + 15% S | ||||||||
Ikwenye iche iche nke mgbidi ọkpụrụkpụ oyi adọta (akpọrela) ígwè tubes
Nkeji: mm
| Ụdị tube ígwè | Ọkpụrụkpụ mgbidi | Ngbanwe ekwe omume | ||||||
| Oyi adọtara (akpọrela) ígwè tube | ≤ 3 | 15-10 % S ma ọ bụ ± 0.15, were ọnụ ọgụgụ ka ukwuu | ||||||
| > 3 | + 12.5% S | |||||||
| -10% S | ||||||||
Nnwale ire ụtọ
Ọkpụkpụ ígwè nwere dayameta dị n'èzí karịa 22 mm na ruo 400 mm, na ọkpụrụkpụ mgbidi karịrị 10 mm kwesịrị ịnwale ule ncha. Mgbe ihe atụ na-agbadata
Nnwale ịgbagọ
Ọkpụkpụ ígwè nwere dayameta dị n'èzí na-erughị 22 mm kwesịrị ịnwale ule ịgbagọ. Nkuku na-ehulata bụ 90o. Oghere nke na-ehulata bụ okpukpu 6 dị n'èzí nke tube ígwè. Mgbe ị na-ehulata ihe nlele ahụ, a naghị ekwe ka ọkpụkpụ ma ọ bụ mgbawa na-apụta na ihe nlele ahụ.
Nyocha macroscopic
N'ihi na ígwè tubes kpọmkwem mere site na mgbe na-awụpụ billets ma ọ bụ nchara ingots, ndị na-eweta kwesịrị ekwe nkwa na ọ dịghị ọcha ntụpọ, adịghị ọcha, sub-elu elu ikuku egosipụta, okpokoro isi ma ọ bụ layering na cross-section acid pickled macroscopic anụ ahụ nke billet ma ọ bụ. ígwè tube.
Nyocha na-adịghị emebi emebi
Dị ka arịrịọ nke onye ahụ na-achọsi ike, nke a na-emekọrịta n'etiti ndị na-enye ihe na ndị na-achọsi ike ma gosipụta na nkwekọrịta ahụ, enwere ike ịchọta ntụpọ ultrasonic n'otu n'otu maka tubes ígwè. Njọ akwụkwọ ntuziaka ogologo nke tube sample kwesịrị iru ihe achọrọ maka ọkwa nnabata post-elele C8 akọwapụtara na GB/T 5777-1996.