ASTM SA 213 tabung penukar panas
| Standar:ASTM SA 213 | Alloy Utawa Ora: Alloy |
| Kelompok kelas: T5, T9, T11, T22 lsp | Aplikasi: Pipa Boiler/pipa penukar panas |
| Ketebalan: 0,4-12,7 mm | Perawatan lumahing: Minangka kabutuhan customer |
| Diameter njaba (Babak): 3.2-127 mm | Teknik: Hot Rolled |
| Dawane: dawa tetep utawa dawa acak | Perawatan panas: Normalisasi / Tempering / Anil |
| Wangun bagean: bunder | Pipa Khusus: Pipa Tembok Tebal |
| Panggonan Asal: China | Dianggo: Super panas, Boiler lan Heat Exchanger |
| Sertifikasi: ISO 9001:2008 | Tes: ECT/UT |
Utamane digunakake kanggo nggawe pipa baja campuran berkualitas tinggi kanggo pipa ketel tekanan tinggi, pipa penukar panas lan pipa panas super.
Kelas saka baja paduan kualitas dhuwur: T2, T12, T11, T22, T91, T92 etc.
| Kelas Baja | Komposisi kimia% | ||||||||||
| C | Si | Mn | P, S Maks | Cr | Mo | Ni Max | V | Al Max | W | B | |
| T2 | 0.10~0.20 | 0.10~0.30 | 0.30~0.61 | 0,025 | 0.50~0.81 | 0.44~0.65 | – | – | – | – | – |
| T11 | 0.05~0.15 | 0.50~1.00 | 0.30~0.60 | 0,025 | 1.00~1.50 | 0.44~0.65 | – | – | – | – | – |
| T12 | 0.05~0.15 | Max 0,5 | 0.30~0.61 | 0,025 | 0.80~1.25 | 0.44~0.65 | – | – | – | – | – |
| T22 | 0.05~0.15 | Max 0,5 | 0.30~0.60 | 0,025 | 1.90~2.60 | 0.87~1.13 | – | – | – | – | – |
| T91 | 0.07~0.14 | 0.20~0.50 | 0.30~0.60 | 0.02 | 8.0~9.5 | 0.85~1.05 | 0.4 | 0.18~0.25 | 0.015 | – | – |
| T92 | 0.07~0.13 | Max 0,5 | 0.30~0.60 | 0.02 | 8.5~9.5 | 0.30~0.60 | 0.4 | 0.15~0.25 | 0.015 | 1.50~2.00 | 0,001~0,006 |
Kanggo T91 liyane saka ndhuwur uga kalebu Nikel 0,4, Va 0,18-0,25, Ni 0,06-0,10, Ni 0,03-0,07, Al 0,02, Ti 0,01, Zr 0,01. A Maksimum, kajaba sawetara utawa minimal dituduhake. Ing endi elips (...) katon ing tabel iki, ora ana syarat, lan analisis kanggo unsur kasebut ora kudu ditemtokake utawa dilapurake. B Diijini pesen T2 lan T12 kanthi kandungan sulfur maksimal 0,045. C Utawa, tinimbang rasio minimal iki, materi kasebut kudu nduweni kekerasan minimal 275 HV ing kondisi hardened, ditetepake minangka sawise austenitizing lan cooling kanggo suhu kamar nanging sadurunge tempering. Pengujian kekerasan kudu ditindakake ing tengah-tengah kekandelan produk. Frekuensi uji kekerasan kudu rong conto produk saben lot perawatan panas lan asil uji kekerasan kudu dilaporake ing laporan uji materi.
| Kelas Baja | Sifat Mekanik | |||
| T. S | Y. P | Elongation | Kekerasan | |
| T2 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
| T11 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
| T12 | ≥ 415MPa | ≥ 220MPa | ≥ 30% | 163HBW(85HRB) |
| T22 | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) |
| T91 | ≥ 585MPa | ≥ 415MPa | ≥ 20% | 250HBW(25HRB) |
| T92 | ≥ 620MPa | ≥ 440MPa | ≥ 20% | 250HBW(25HRB) |
Variasi sing diidini ing ketebalan Tembok
| Kekandelan % | |||||
| njaba diameteripun ing. mm | 0.095 2.4 lan ngisor | liwat 0,095 kanggo 0.15 2.4-3.8 kalebu. | liwat 0,15 kanggo 0.18 3.8-4.6 kalebu | liwat 0.18 kanggo 4.6 | |
| liwat ngisor liwat ngisor liwat ngisor liwat ngisor | |||||
| mulus, panas rampung | |||||
| 4inch lan ngisor 40 0 35 0 33 0 28 0 | |||||
| luwih saka 4 inci .. .. 35 0 33 0 28 0 | |||||
| mulus, kadhemen rampung | |||||
| liwat ngisor | |||||
| 11/2 lan ngisor | 20 0 | ||||
| liwat 11/2 | 22 0 | ||||
Variasi kekandelan tembok sing diidinake mung ditrapake kanggo tabung, kajaba tabung internal-upset, minangka digulung utawa kadhemen rampung.
lan sadurunge swaging, ngembangaken, mlengkung, polishing, utawa operasi fabricating liyane
Variasi sing diidini ing Diameter njaba
| diameteripun njaba (mm) | Variasi sing diidini (mm) | |
| panas rampung tabung rapi | liwat | ing ngisor |
| 4" (100mm) lan ngisor | 0.4 | 0.8 |
| 4-71/2" (100-200mm) | 0.4 | 1.2 |
| 71/2-9"(200-225) | 0.4 | 1.6 |
| tabung gandheng lan kadhemen rampung tabung rapi | ||
| ngisor 1" (25mm) | 0.1 | 0.11 |
| 1-11/2" (25-40mm) | 0.15 | 0.15 |
| 11/2-2" (40-50mm) | 0.2 | 0.2 |
| 2-21/2" (50-65mm) | 0.25 | 0.25 |
| 21/2-3" (65-75mm) | 0.3 | 0.3 |
| 3-4" (75-100mm) | 0.38 | 0.38 |
| 4-71/2" (100-200mm) | 0.38 | 0.64 |
| 71/2-9"(200-225) | 0.38 | 1.14 |
Tes hidrostatik:
Pipa Baja Kudu Diuji Hidrolik Siji Babakan. Tekanan Tes Maksimum 20 MPa. Ing Tekanan Test, Wektu Stabilisasi Aja Kurang Saka 10 S, Lan Pipa Baja Ora Bocor. Utawa Tes Hidrolik Bisa Diganti Kanthi Tes Eddy Saiki Utawa Tes Kebocoran Fluks Magnetik.
Tes ora ngrusak:
Pipa sing Mbutuhake Inspeksi Luwih Perlu Dipriksa kanthi Ultrasonik Siji Bareng. Sawise Negosiasi Mbutuhake Persetujuan Pihak Lan Ditemtokake Ing Kontrak, Pengujian Non-Ngrusak Liyane Bisa Ditambahake.
Tes Flattening:
Tabung Kanthi Dhiameter Njaba Luwih saka 22 Mm Bakal Ditampa Tes Flattening. Ora ana delaminasi sing katon, bintik putih, utawa rereged sing kudu kedadeyan sajrone kabeh eksperimen.
Tes kekerasan:
Kanggo Pipa Gelar P91, P92, P122, Lan P911, Brinell, Vickers, Utawa Tes Kekerasan Rockwell Bakal Digawe Ing Spesimen Saka Saben Lot