pipa baja paduan mulus ASTM A335 P5
Ringkesan
Standar: ASTM A335
Kelompok kelas: P5, P9, P11, P22, P91, P92 etc.
Ketebalan: 1 - 100 mm
Dhiameter njaba (Bander): 10 - 1000 mm
Dawane: dawa tetep utawa dawa acak
Wangun bagean: bunder
Panggonan Asal: China
Sertifikasi: ISO 9001:2008
Alloy Utawa Ora: Alloy
Aplikasi: Pipa Boiler
Perawatan lumahing: Minangka kabutuhan customer
Teknik: Hot Rolled / Cold Drawn
Perawatan panas: Annealing / normalisasi / Tempering
Pipa Khusus: Pipa Tembok Tebal
Dianggo: pipa uap tekanan dhuwur, Boiler lan Penukar Panas
Tes: ET/UT
Aplikasi
Utamane digunakake kanggo nggawe pipa ketel baja campuran berkualitas tinggi, pipa sing diijolke panas, pipa uap tekanan dhuwur kanggo industri minyak lan kimia.
Kelas Utama
Pipa paduan kualitas dhuwur: P1, P2, P5, P9, P11, P22, P91, P92 etc
Komponen Kimia
| sasmita | UN | C≤ | Mn | P≤ | S≤ | Si≤ | Cr | Mo |
| Sequiv. | ||||||||
| P1 | K11522 | 0.10~0.20 | 0.30~0.80 | 0,025 | 0,025 | 0.10~0.50 | – | 0.44~0.65 |
| P2 | K11547 | 0.10~0.20 | 0.30~0.61 | 0,025 | 0,025 | 0.10~0.30 | 0.50~0.81 | 0.44~0.65 |
| P5 | K41545 | 0.15 | 0.30~0.60 | 0,025 | 0,025 | 0.5 | 4.00-6.00 | 0.44~0.65 |
| P5b | K51545 | 0.15 | 0.30~0.60 | 0,025 | 0,025 | 1.00~2.00 | 4.00-6.00 | 0.44~0.65 |
| P5c | K41245 | 0.12 | 0.30~0.60 | 0,025 | 0,025 | 0.5 | 4.00-6.00 | 0.44~0.65 |
| P9 | S50400 | 0.15 | 0.30~0.60 | 0,025 | 0,025 | 0.50~1.00 | 8.00-10.00 | 0.44~0.65 |
| P11 | K11597 | 0.05~0.15 | 0.30~0.61 | 0,025 | 0,025 | 0.50~1.00 | 1.00~1.50 | 0.44~0.65 |
| P12 | K11562 | 0.05~0.15 | 0.30~0.60 | 0,025 | 0,025 | 0.5 | 0.80~1.25 | 0.44~0.65 |
| P15 | K11578 | 0.05~0.15 | 0.30~0.60 | 0,025 | 0,025 | 1.15~1.65 | – | 0.44~0.65 |
| P21 | K31545 | 0.05~0.15 | 0.30~0.60 | 0,025 | 0,025 | 0.5 | 2.65~3.35 | 0.80~1.60 |
| P22 | K21590 | 0.05~0.15 | 0.30~0.60 | 0,025 | 0,025 | 0.5 | 1.90~2.60 | 0.87~1.13 |
| P91 | K91560 | 0.08~0.12 | 0.30~0.60 | 0.02 | 0.01 | 0.20~0.50 | 8.00-9.50 | 0.85~1.05 |
| P92 | K92460 | 0.07~0.13 | 0.30~0.60 | 0.02 | 0.01 | 0.5 | 8.50~9.50 | 0.30~0.60 |
A sebutan anyar ditetepake miturut Practice E 527 lan SAE J1086, Practice for Numbering Metals and Alloys (UNS). B Grade P 5c kudu isi titanium ora kurang saka 4 kaping isi karbon lan ora luwih saka 0,70%; utawa kandungan columbium 8 nganti 10 kaping isi karbon.
Properti Mekanik
| Sifat mekanik | P1, P2 | P12 | P23 | P91 | P92, P11 | P122 |
| Kekuwatan tensile | 380 | 415 | 510 | 585 | 620 | 620 |
| kekuatan ngasilaken | 205 | 220 | 400 | 415 | 440 | 400 |
Perawatan panas
| sasmita | Jinis Perawatan Panas | Normalisasi Rentang Suhu F [C] | Subcritical Annealing utawa Tempering |
| P5, P9, P11, lan P22 | Rentang Suhu F [C] | ||
| A335 P5 (b,c) | Full utawa Isothermal Anneal | ||
| Normalisasi lan Temper | ***** | 1250 [675] | |
| Anil Subkritis (mung P5c) | ***** | 1325 – 1375 [715 – 745] | |
| A335 P9 | Full utawa Isothermal Anneal | ||
| Normalisasi lan Temper | ***** | 1250 [675] | |
| A335 P11 | Full utawa Isothermal Anneal | ||
| Normalisasi lan Temper | ***** | 1200 [650] | |
| A335 P22 | Full utawa Isothermal Anneal | ||
| Normalisasi lan Temper | ***** | 1250 [675] | |
| A335 P91 | Normalisasi lan Temper | 1900-1975 [1040-1080] | 1350-1470 [730 - 800] |
| Ngilangi lan Temper | 1900-1975 [1040-1080] | 1350-1470 [730 - 800] |
Toleransi
Kanggo pipe dhawuh kanggo diameteripun nang, diameteripun nang ora bakal beda-beda luwih saka 6 1% saka diameteripun nang kasebut
Variasi sing diidini ing Diameter njaba
| NPS Designator | in | mm | in | mm |
| 1⁄8 nganti 11⁄2, kalebu | 1⁄64 (0,015) | 0.4 | 1⁄64(0.015) | 0.4 |
| Luwih saka 11⁄2 nganti 4, kalebu. | 1⁄32(0.031) | 0.79 | 1⁄32(0.031) | 0.79 |
| Swara 4 kanggo 8, kalebu | 1⁄16(0.062) | 1.59 | 1⁄32(0.031) | 0.79 |
| Swara 8 kanggo 12, kalebu. | 3⁄32(0.093) | 2.38 | 1⁄32(0.031) | 0.79 |
| Luwih saka 12 | 6 1 % saka sing ditemtokake njaba diameteripun |
Syarat Test
Tes hidrostatik:
Pipa Baja Kudu Diuji Hidrolik Siji Babakan. Tekanan Tes Maksimum 20 MPa. Ing Tekanan Test, Wektu Stabilisasi Aja Kurang Saka 10 S, Lan Pipa Baja Ora Bocor.
Sawise Pangguna Sarujuk, Tes Hidrolik Bisa Diganti Kanthi Tes Eddy Saiki Utawa Tes Kebocoran Fluks Magnetik.
Tes ora ngrusak:
Pipa sing Mbutuhake Inspeksi Luwih Perlu Dipriksa kanthi Ultrasonik Siji Bareng. Sawise Negosiasi Mbutuhake Persetujuan Pihak Lan Ditemtokake Ing Kontrak, Pengujian Non-Ngrusak Liyane Bisa Ditambahake.
Tes Flattening:
Tabung Kanthi Dhiameter Njaba Luwih saka 22 Mm Bakal Ditampa Tes Flattening. Ora ana delaminasi sing katon, bintik putih, utawa rereged sing kudu kedadeyan sajrone kabeh eksperimen.
Tes kekerasan:
Kanggo pipa Grades P91, P92, P122, lan P911, tes kekerasan Brinell, Vickers, utawa Rockwell kudu digawe ing spesimen saka saben lot.
Tes Bend:
Kanggo pipe kang diameteripun ngluwihi NPS 25 lan diameteripun kanggo rasio kekandelan tembok punika 7,0 utawa kurang bakal subjected kanggo test bend tinimbang test flattening. Pipa liyane sing diametere padha utawa ngluwihi NPS 10 bisa uga diwenehi tes bend tinimbang tes flattening tundhuk persetujuan panuku.
Detail Produk
ASTM A335 P5 minangka pipa suhu dhuwur feritik baja campuran standar Amerika. Tabung paduan minangka jinis tabung baja sing mulus, kinerjae luwih dhuwur tinimbang tabung baja sing umum, amarga tabung baja iki ngemot luwih akeh C, kinerja kurang saka tabung baja sing biasa, mula tabung campuran digunakake akeh. ing petroleum, aerospace, kimia, daya listrik, boiler, militèr lan industri liyane.
Pipa Baja Paduan ngemot jumlah unsur liyane saliyane karbon kayata nikel, kromium, silikon, mangan, tungsten, molibdenum, vanadium lan jumlah winates saka unsur liyane sing umum ditampa kayata mangan, belerang, silikon, lan fosfor.
Baja paduan domestik sing cocog: 1Cr5Mo GB 9948-2006 "Standar Pipa Baja Seamless kanggo Retak Petroleum"
- Pembayaran: 30% Deposit, 70% L/C Utawa B/L Copy Utawa 100% L/C At Sight
- Min.Pesanan Jumlah: 1 PC
- Kemampuan Sumber: Inventarisasi 20000 Ton Tahunan Pipa Baja
- Lead Time: 7-14 Dina Yen Ing Simpenan, 30-45 Dina Kanggo Ngasilake
- Packing: Black Vanishing, Bevel lan Cap Kanggo Saben Pipa Tunggal; OD Ngisor 219mm Perlu Pack ing Bundle, Lan Saben Bundle Ora ngluwihi 2 Ton.
Ringkesan
| Standar: ASTM A335 | Alloy Utawa Ora: Alloy |
| Klompok Kelas: P5 | Aplikasi: Pipa Boiler |
| Ketebalan: 1 – 100 mm | Perawatan lumahing: Minangka Requirement Customer |
| Dhiameter njaba (Bander): 10 – 1000 Mm | Teknik: Hot Rolled / Cold Drawn |
| Dawane: dawa tetep utawa dawa acak | Perawatan panas: Annealing / Normalizing / Tempering |
| Wangun bagean: bunder | Pipa Khusus: Pipa Tembok Tebal |
| Panggonan Asal: China | Dianggo: Pipa Uap Tekanan Tinggi, Boiler lan Penukar Panas |
| Sertifikasi: ISO 9001:2008 | Tes: ET/UT |
Aplikasi
Utamane Digunakake Kanggo Nggawe Pipa Boiler Baja Alloy Berkualitas Tinggi, Pipa Ditukar Panas, Pipa Uap Tekanan Tinggi Kanggo Industri Minyak lan Kimia
Komponen Kimia
| Komposisi | data |
| Penetapan UNS | K41545 |
| Karbon (maks.) | 0.15 |
| Mangan | 0.30-0.60 |
| Fosfor (maks.) | 0,025 |
| Silikon (maks.) | 0.50 |
| Kromium | 4.00-6.00 |
| Molybdenum | 0.45-0.65 |
| Unsur liyane | … |
Properti Mekanik
| Properti | data |
| Kekuatan Tarik, Min, (MPa) | 415 Mpa |
| Kekuwatan Ngasilake, Min, (MPa) | 205 Mpa |
| Elongasi, Min, (%), L/T | 30/20 |
Perawatan panas
| sasmita | Jinis Perawatan Panas | Normalisasi Rentang Suhu F [C] | Subcritical Annealing Utawa Tempering |
| P5, P9, P11, lan P22 | Rentang Suhu F [C] | ||
| A335 P5 (B,C) | Full utawa Isothermal Anneal | ||
| A335 P5b | Normalisasi lan Temper | ***** | 1250 [675] |
| A335 P5c | Anneal Subkritis | ***** | 1325 – 1375 [715 – 745] |
Toleransi
Kanggo Pipa Didhawuhi Diameter Nang, Diameter Nang Ora Bakal Luwih Luwih Saka ±1 % Saka Diameter Nang Ditemtokake
Variasi sing diidini ing diameter njaba
| NPS Designator | Toleransi positif | toleransi negatif | ||
| In | Mm | In | Mm | |
| 1⁄8 nganti 11⁄2, Incl | 1⁄64 (0,015) | 0.4 | 1⁄64(0.015) | 0.4 |
| Swara 11⁄2 Kanggo 4, Incl. | 1⁄32(0.031) | 0.79 | 1⁄32(0.031) | 0.79 |
| Swara 4 Kanggo 8, Incl | 1⁄16(0.062) | 1.59 | 1⁄32(0.031) | 0.79 |
| Swara 8 Kanggo 12, Incl. | 3⁄32(0.093) | 2.38 | 1⁄32(0.031) | 0.79 |
| Luwih saka 12 | ± 1 % Saka Ditemtokake Njaba Dhiameter | |||
Syarat Test
Tes hidrostatik:
Pipa Baja Kudu Diuji Hidrolik Siji Babakan. Tekanan Tes Maksimum 20 MPa. Ing Tekanan Test, Wektu Stabilisasi Aja Kurang Saka 10 S, Lan Pipa Baja Ora Bocor.
Sawise Pangguna Sarujuk, Tes Hidrolik Bisa Diganti Kanthi Tes Eddy Saiki Utawa Tes Kebocoran Fluks Magnetik.
Tes ora ngrusak:
Pipa sing Mbutuhake Inspeksi Luwih Perlu Dipriksa kanthi Ultrasonik Siji Bareng. Sawise Negosiasi Mbutuhake Persetujuan Pihak Lan Ditemtokake Ing Kontrak, Pengujian Non-Ngrusak Liyane Bisa Ditambahake.
Tes Flattening:
Tabung Kanthi Dhiameter Njaba Luwih saka 22 Mm Bakal Ditampa Tes Flattening. Ora ana delaminasi sing katon, bintik putih, utawa rereged sing kudu kedadeyan sajrone kabeh eksperimen.
Tes kekerasan:
Kanggo Pipa Gelar P91, P92, P122, Lan P911, Brinell, Vickers, Utawa Tes Kekerasan Rockwell Bakal Digawe Ing Spesimen Saka Saben Lot
Tes Bend:
Kanggo Pipa sing diametere ngluwihi NPS 25 lan rasio kekandelan tembok diameteripun 7,0 utawa kurang, bakal dileksanakake ing Test Bend tinimbang Test Flattening. Pipa liyane sing diametere padha utawa ngluwihi NPS 10 Bisa Diwenehi Tes Bend Ing Panggonan Tes Flattening Tunduk Persetujuan Pembeli
Bahan & Pabrik
Pipa bisa dadi panas rampung utawa kadhemen digambar kanthi perawatan panas pungkasan sing dicathet ing ngisor iki.
Perawatan panas
- A / N+T
- N+T / Q+T
- N+T
Tes Mekanik Ditemtokake
- Tes Ketegangan Transversal utawa Longitudinal lan Tes Flattening, Tes Kekerasan, utawa Tes Bend
- Kanggo bahan panas sing diolah ing tungku jinis batch, tes kudu ditindakake ing 5% pipa saka saben lot sing dirawat. Kanggo lot cilik, paling ora siji pipa kudu diuji.
- Kanggo bahan panas sing diolah kanthi proses terus-terusan, tes kudu ditindakake ing jumlah pipa sing cukup kanggo 5% saka lot, nanging ora kurang saka 2 pipa.
Cathetan kanggo Tes Bend:
- Kanggo pipe kang diameteripun ngluwihi NPS 25 lan diameteripun kanggo rasio kekandelan tembok punika 7,0 utawa kurang bakal subjected kanggo test bend tinimbang test flattening.
- Pipa liyane sing diametere padha utawa ngluwihi NPS 10 bisa uga diwenehi tes bend tinimbang tes flattening sing disetujoni saka panuku.
- Spesimen uji bend kudu ditekuk ing suhu kamar nganti 180 tanpa retak ing njaba bagean sing bengkok.
Tabung baja mulus ASTM A335 P5 cocog kanggo banyu, uap, hidrogen, lenga asem, lsp. Yen digunakake kanggo uap banyu, suhu operasi maksimal yaiku 650℃; Nalika digunakake ing medium apa kayata lenga ora nguntungke, wis resistance karat belerang suhu dhuwur apik, lan asring digunakake ing kahanan karat belerang suhu dhuwur saka 288 ~ 550℃.
Proses produksi:
1. Rolling panas (tabung baja mulus extruded): billet tabung bunder → dadi panas → perforasi → rolling salib telung roll, rolling terus utawa ekstrusi → stripping tabung → ukuran (utawa ngurangi) → cooling → straightening → test tekanan banyu (utawa deteksi cacat ) → menehi tandha → panyimpenan
2. Gambar kadhemen (rolling) tabung baja mulus: billet tabung bunder → pemanasan → perforasi → judhul → anil → pickling → oiling (plating tembaga) → gambar kadhemen multi-pass (cold rolling) → tabung kosong → perawatan panas → straightening → banyu tes tekanan (deteksi cacat) → menehi tandha → panyimpenan
Skenario Aplikasi:
Ing piranti atmosfer lan vakum kanggo ngolah minyak mentah belerang dhuwur, tabung baja lancar ASTM A335 P5 utamane digunakake kanggo pipa ngisor menara atmosfer lan vakum, tabung tungku saka tungku atmosfer lan vakum, bagean kacepetan dhuwur saka konversi lenga atmosfer lan vakum garis lan pipa lenga lan gas suhu dhuwur liyane sing ngemot belerang.
Ing unit FCC, tabung baja lancar ASTM A335 P5 utamane digunakake ing pipa slurry suhu dhuwur, katalis lan pipa pemurnian bali, uga sawetara pipa minyak lan gas belerang suhu dhuwur liyane.
Ing unit coking telat, pipa baja lancar ASTM A335 P5 utamane digunakake kanggo pipa feed suhu dhuwur ing ngisor menara coke lan pipa minyak lan gas suhu dhuwur ing ndhuwur menara coke, pipa tungku ing ngisor tungku coke, pipa ing ngisor menara fracking lan sawetara lenga suhu dhuwur lan pipa gas liyane ngemot belerang.