Carbon Steel Pipe et stannum chalybe
Societas nostra versatur in negotiis exportandis chalybis carbonii et mixturae ferri.Alloy Pipe, mixtura ferro tibia, Admisce Steel Pipe China, carbo carbonis, Carbon Steel Pipe, Carbon Steel Pipe China.
Scisne discrimen inter chalybem carbonii et stannum chalybem?
CARBONES FERRUM;principaliter refertur ad proprietates mechanicas dependentes a carbonis contento ferri, et plerumque non multum addunt elementa ferri mixtura, interdum chalybs carbonis vel chalybs plana vocata. Carbo carbonis, quae etiam nota est chalybis carbonis, contentus carbo WC minus quam 2% offensionis ferri carbonis.
Calamus carbonis praeter generaliter continet parvam quantitatem siliconis, manganesi, sulphuris, phosphori secundum usum structurae chalybis carbonis, chalybis carbonis, instrumenti carbonis et liberae structurae chalybis incisis tribus fabricae chalybis carbonis in structuram chalybem divisa est et machina fabrica chalybis, quae in chalybem carbonis demissa dividi potest (WC ≤ 0.25%), medium carbonis (WC 0,25% - 0,6%) et chalybe carbonis altum (WC> 0,6%).
Secundum phosphoro et sulphure contento, chalybei carbonii in fodinas carbonum ordinarias dividi possunt (phosphorus et sulphur altiores sunt), princeps qualitas chalybi carbonis (phosphori et sulphuris inferiora sunt), summus qualitas ferri (phosphorus, sulphur inferior).
Admisce ferro:ex chalybe carbonii, unum vel plura elementa mixtura consulto adduntur ad emendandum usum et processum activitatis ferratae substructio mixturae, quod ferrum mixtura dicitur. Ferrum mixturae refert ad ferrum, continentem pii et manganesum, ut mixtura elementa vel elementa deoxidantia, alia mixtura, ut chromium, nickel, molybdenum, vanadium, titanium, cuprum, tungsten, aluminium, cobaltum, niobium, zirconium et alia elementa, et quaedam praeterea. continent nonnulla elementa non metalla (ut boron, nitrogen, etc.) chalybem.
Secundum quantitatem elementorum in ferro mixturae, sed etiam in mixturam ferri, medium stannum et altam ferro mixturam dividi potest.
Compositio chemica differentia;
(1) Carbon steel: Low carbon steel (C≤0.25%); Medium chalybeum carbonis (C≤0.25~0.60%); Princeps chalybe carbonis (C≤0.60%).
(2) Admiscere chalybem: Minimum offensionis ferrum (summa elementa mixtionis ≤ 5%); Medium offensionis chalybis (omnium mixturae elementorum> 5~10%) ; Princeps offensionis chalybeum (tota contenta elementorum offensionum> 10%.
Carbo ferro commoda;
Ferrum carbonis magnam vim habet, ductilis et duritiem, sumptus parvos, in gravibus machinationibus adhibitis ad partes onus graves fabricandas. Curatio caloris obtineri potest melius proprietates mechanicas eiiciendi.
Admiscere commoda ferro;
Praeter ferrum in ferro, elementa tantum chalybem carbonii, chalybem carbonii, alia pii, sulphur, phosphori et aliae immunditias continentur. Praeter alia elementa chromium, manganesum, molybdenum, titanium, tungstenum, vanadium, niobium, boron, pii et nickel stannum chalybem ad obtinendas proprietates desideratas sicut caliditas, alta elasticitas, abrasio resistentia, magna fortitudo, alta durities et sic reliqua. Admisce ferro duritiem gerunt resistentia, duritia, resistentia corrosio quam chalybe carbonis excellentior.
Hic videre potes quosdam ex communi usuCarbon chalybemateriales gradus in processu limbis.
·For Pipes: ASTM A53 Gr A/B, A106 Gr A/B/C, API 5L Gr B
·ASTM A53 Pipe, Ferro, Nigro et Hot detrito, cadmiae Coated, iunctae et inconsutilae.
·ASTM A106 SeamlessCarbon Steel Pipead Summus Temperature Service
Overview
Applicationem
Maxime adhibetur ad mechanica et ad cylindros gasi faciendos. Includunt carbonem et mixturam ferro inconsutilem mechanicam Tubingam, et tegit utrumque inconsutilem calidum-perfectum mechanica Tubing et inconsutilem frigidum-perfectum mechanica Tubing in magnitudinibus usque ad 12 3/4 in. (323.8 mm) extra diametrum pro tubulis rotundis cum parietibus crassitudinibus necessariis.
Principalis Gradus
1018,1026,8620,4130,4140
Chemical Component
TABLE 1 Chemical Requirements of Low-Carbon Steels
Gradus | Chemical Compositio limites, % | |||||||
Designatio | CarbonA | ManganeseB | Phosphorus;B | Sulphur,B | ||||
max | max | |||||||
MT X 1015 | 0.10-0.20 | 0.60-0.90 | 0.04 | 0.05 | ||||
MT 1010 | 0.05-0.15 | 0.30-0.60 | 0.04 | 0.05 | ||||
MT 1015 | 0.10-0.20 | 0.30-0.60 | 0.04 | 0.05 | ||||
MT 1020 | 0.15-0.25 | 0.30-0.60 | 0.04 | 0.05 | ||||
MT X 1020 | 0.15-0.25 | 0.70-1.00 | 0.04 | 0.05 |
BTermini applicandi ad calefactionem analysis; nisi secundum 6.1, analyses productas subiciuntur applicabilibus toleranciis quae in Tabula 5 data sunt.
Tabella 2 Requisita chemica alia Carbon Steels
Gradus | Chemical Compositio limites, %A | ||||
Designatio | |||||
Carbon | Manganese | Phosphorus; | Sulphur, | ||
max | max | ||||
1008 | 0.10 max | 0.30-0.50 | 0.041 | 0.041 | |
1010 | 0.08-0.13 | 0.30-0.60 | 0.041 | 0.041 | |
1012 | 0.10-0.15 | 0.30-0.60 | 0.041 | 0.041 | |
1015 | 0.13-0.18 | 0.30-0.60 | 0.041 | 0.041 | |
1016 | 0.13-0.18 | 0.60-0.90 | 0.041 | 0.041 | |
1017 | 0.15-0.20 | 0.30-0.60 | 0.041 | 0.041 | |
1018 | 0.15-0.20 | 0.60-0.90 | 0.041 | 0.041 | |
1019 | 0.15-0.20 | 0.70-1.00 | 0.041 | 0.041 | |
1020 | 0.18–0.23 | 0.30-0.60 | 0.041 | 0.041 | |
1021 | 0.18–0.23 | 0.60-0.90 | 0.041 | 0.041 | |
1022 | 0.18–0.23 | 0.70-1.00 | 0.041 | 0.041 | |
1025 | 0.22–0.28 | 0.30-0.60 | 0.041 | 0.041 | |
1026 | 0.22–0.28 | 0.60-0.90 | 0.041 | 0.041 | |
1030 | 0.28-0.34 | 0.60-0.90 | 0.041 | 0.041 | |
1035 | 0.32-0.38 | 0.60-0.90 | 0.041 | 0.041 | |
1040 | 0.37–0.44 | 0.60-0.90 | 0.041 | 0.041 | |
1045 | 0.43-0.50 | 0.60-0.90 | 0.041 | 0.041 | |
1050 | 0.48–0.55 | 0.60-0.90 | 0.041 | 0.041 | |
1518 | 0.15-0.21 | 1.10-1.40 | 0.041 | 0.041 | |
1524 | 0.19–0.25 | 1.35-1.65 | 0.041 | 0.041 | |
1541 | 0.36–0.44 | 1.35-1.65 | 0.041 | 0.041 | |
Circumscriptiones et limites in hac tabula datos applicant ad analysim caloris; nisi quod erat faciendum6.1analyses ductae subiciuntur applicabilibus adiectis patientibus datis in Tabula Numeri 5 .
TABLE III Chemical Requisita ad Alloy Steels | |||||||||
NOTA | 1 — Circumscriptiones et limites in hac tabula applicant ferro non excedentes 200 in.2(1290 cm .)2) In area crucis-Lorem. | ||||||||
NOTA | 2 — Copiae quarundam elementorum in offensionibus ferris insunt, quae nec specificantur nec requiruntur. Haec elementa considerantur ut accidens | ||||||||
et his maximis ponderis adesse potest: aeris, 0,35%; nickel, 0.25%; chromium 0.20%; molybdenum, 0.10%. | |||||||||
NOTA | 3 — Circumscriptiones et limites in hac tabula datos applicant ad analysim caloris; nisi quod erat faciendum6.1, productum analyses subsunt applicabili | ||||||||
additae tolerantiae in Tabula Number V datae. |
GradusA,B | Chemical Compositio limites, % | |||||||
Designa- | ||||||||
Carbon | Manganese | Phospho- | Sulphur,C,D | Pii | Nickel | Chromium | Molybde- | |
tio | ||||||||
rus,Cmax | max | num | ||||||
1330 | 0.28-0.33 | 1.60-1.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | ... |
1335 | 0.33-0.38 | 1.60-1.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | ... |
1340 | 0.38–0.43 | 1.60-1.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | ... |
1345 | 0.43-0.48 | 1.60-1.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | ... |
3140 | 0.38–0.43 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 1.10-1.40 | 0.55-0.75 | ... |
E3310 | 0.08-0.13 | 0.45-0.60 | 0.024 | 0.024 | 0.15-0.35 | 3.25–3.75 | 1.40-1.75 | ... |
4012 | 0.09-0.14 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.15-0.25 |
4023 | 0.20–0.25 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.20-0.30 |
4024 | 0.20–0.25 | 0.70-0.90 | 0.04 | 0.035−0.050 | 0.15-0.35 | ... | ... | 0.20-0.30 |
4027 | 0.25–0.30 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.20-0.30 |
4028 | 0.25–0.30 | 0.70-0.90 | 0.04 | 0.035−0.050 | 0.15-0.35 | ... | ... | 0.20-0.30 |
4037 | 0.35-0.40 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.20-0.30 |
4042 | 0.40-0.45 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.20-0.30 |
4047 | 0.45-0.50 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.20-0.30 |
4063 | 0.60-0.67 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.20-0.30 |
4118 | 0.18–0.23 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.40-0.60 | 0.08-0.15 |
4130 | 0.28-0.33 | 0.40-0.60 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | 0.15-0.25 |
4135 | 0.32-0.39 | 0.65-0.95 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | 0.15-0.25 |
4137 | 0.35-0.40 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | 0.15-0.25 |
4140 | 0.38–0.43 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | 0.15-0.25 |
4142 | 0.40-0.45 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | 0.15-0.25 |
4145 | 0.43-0.48 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | 0.15-0.25 |
4147 | 0.45-0.50 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | 0.15-0.25 |
4150 | 0.48-0.53 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | 0.15-0.25 |
4320 | 0.17–0.22 | 0.45-0.65 | 0.04 | 0.04 | 0.15-0.35 | 1.65–2.00 | 0.40-0.60 | 0.20-0.30 |
4337 | 0.35-0.40 | 0.60-0.80 | 0.04 | 0.04 | 0.15-0.35 | 1.65–2.00 | 0.70-0.90 | 0.20-0.30 |
E4337 | 0.35-0.40 | 0.65-0.85 | 0.024 | 0.024 | 0.15-0.35 | 1.65–2.00 | 0.70-0.90 | 0.20-0.30 |
4340 | 0.38–0.43 | 0.60-0.80 | 0.04 | 0.04 | 0.15-0.35 | 1.65–2.00 | 0.70-0.90 | 0.20-0.30 |
E4340 | 0.38–0.43 | 0.65-0.85 | 0.024 | 0.024 | 0.15-0.35 | 1.65–2.00 | 0.70-0.90 | 0.20-0.30 |
4422 | 0.20–0.25 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.35-0.45 |
4427 | 0.24-0.29 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.35-0.45 |
4520 | 0.18–0.23 | 0.45-0.65 | 0.04 | 0.04 | 0.15-0.35 | ... | ... | 0.45-0.60 |
4615 | 0.13-0.18 | 0.45-0.65 | 0.04 | 0.04 | 0.15-0.35 | 1.65–2.00 | ... | 0.20-0.30 |
4617 | 0.15-0.20 | 0.45-0.65 | 0.04 | 0.04 | 0.15-0.35 | 1.65–2.00 | ... | 0.20-0.30 |
4620 | 0.17–0.22 | 0.45-0.65 | 0.04 | 0.04 | 0.15-0.35 | 1.65–2.00 | ... | 0.20-0.30 |
4621 | 0.18–0.23 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 1.65–2.00 | ... | 0.20-0.30 |
4718 | 0.16-0.21 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.90-1.20 | 0.35-0.55 | 0.30-0.40 |
4720 | 0.17–0.22 | 0.50-0.70 | 0.04 | 0.04 | 0.15-0.35 | 0.90-1.20 | 0.35-0.55 | 0.15-0.25 |
4815 | 0.13-0.18 | 0.40-0.60 | 0.04 | 0.04 | 0.15-0.35 | 3.25–3.75 | ... | 0.20-0.30 |
4817 | 0.15-0.20 | 0.40-0.60 | 0.04 | 0.04 | 0.15-0.35 | 3.25–3.75 | ... | 0.20-0.30 |
4820 | 0.18–0.23 | 0.50-0.70 | 0.04 | 0.04 | 0.15-0.35 | 3.25–3.75 | ... | 0.20-0.30 |
5015 | 0.12–0.17 | 0.30-0.50 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.30-0.50 | ... |
5046 | 0.43-0.50 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.20-0.35 | ... |
5115 | 0.13-0.18 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.70-0.90 | ... |
5120 | 0.17–0.22 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.70-0.90 | ... |
5130 | 0.28-0.33 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | ... |
5132 | 0.30-0.35 | 0.60-0.80 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.75-1.00 | ... |
5135 | 0.33-0.38 | 0.60-0.80 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.05 | ... |
5140 | 0.38–0.43 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.70-0.90 | ... |
5145 | 0.43-0.48 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.70-0.90 | ... |
5147 | 0.46-0.51 | 0.70-0.95 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.85–1.15 | ... |
5150 | 0.48-0.53 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.70-0.90 | ... |
5155 | 0.51-0.59 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.70-0.90 | ... |
5160 | 0.56–0.64 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.70-0.90 | ... |
52100E | 0.93-1.05 | 0.25-0.45 | 0.024 | 0.014 | 0.15-0.35 | 0.25 max | 1.35-1.60 | 0.10 max |
E50100 | 0.98-1.10 | 0.25-0.45 | 0.024 | 0.024 | 0.15-0.35 | ... | 0.40-0.60 | ... |
E51100 | 0.98-1.10 | 0.25-0.45 | 0.024 | 0.024 | 0.15-0.35 | ... | 0.90-1.15 | ... |
E52100 | 0.98-1.10 | 0.25-0.45 | 0.024 | 0.024 | 0.15-0.35 | ... | 1.30-1.60 | ... |
Vanadium | ||||||||
6118 | 0.16-0.21 | 0.50-0.70 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.50-0.70 | 0.10-0.15 |
6120 | 0.17–0.22 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.70-0.90 | 0.10 min |
6150 | 0.48-0.53 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.80-1.10 | 0.15 min |
aluminium | Molybdenum | |||||||
E7140 | 0.38–0.43 | 0.50-0.70 | 0.024 | 0.024 | 0.15-0.40 | 0.95–1.30 | 1.40-1.80 | 0.30-0.40 |
Nickel | ||||||||
8115 | 0.13-0.18 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.20-0.40 | 0.30-0.50 | 0.08-0.15 |
8615 | 0.13-0.18 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8617 | 0.15-0.20 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8620 | 0.18–0.23 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8622 | 0.20–0.25 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8625 | 0.23-0.28 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8627 | 0.25–0.30 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8630 | 0.28-0.33 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8637 | 0.35-0.40 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8640 | 0.38–0.43 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8642 | 0.40-0.45 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8645 | 0.43-0.48 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8650 | 0.48-0.53 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8655 | 0.51-0.59 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8660 | 0.55-0.65 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
8720 | 0.18–0.23 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.20-0.30 |
8735 | 0.33-0.38 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.20-0.30 |
8740 | 0.38–0.43 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.20-0.30 |
8742 | 0.40-0.45 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.20-0.30 |
8822 | 0.20–0.25 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.30-0.40 |
9255 | 0.51-0.59 | 0.60-0.80 | 0.04 | 0.04 | 1.80–2.20 | ... | 0.60-0.80 | ... |
9260 | 0.56–0.64 | 0.75-1.00 | 0.04 | 0.04 | 1.80–2.20 | ... | ... | ... |
9262 | 0.55-0.65 | 0.75-1.00 | 0.04 | 0.04 | 1.80–2.20 | ... | 0.25–0.40 | ... |
E9310 | 0.08-0.13 | 0.45-0.65 | 0.024 | 0.024 | 0.15-0.35 | 3.00–3.50 | 1.00-1.40 | 0.08-0.15 |
9840 | 0.38–0.42 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.85–1.15 | 0.70-0.90 | 0.20-0.30 |
9850 | 0.48-0.53 | 0.70-0.90 | 0.04 | 0.04 | 0.15-0.35 | 0.85–1.15 | 0.70-0.90 | 0.20-0.30 |
50B40 | 0.38–0.42 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.40-0.60 | ... |
50B44 | 0.43-0.48 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.40-0.60 | ... |
50B46 | 0.43-0.50 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.20-0.35 | ... |
50B50 | 0.48-0.53 | 0.74–1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.40-0.60 | ... |
50B60 | 0.55-0.65 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.40-0.60 | ... |
51B60 | 0.56–0.64 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | ... | 0.70-0.90 | ... |
81B45 | 0.43-0.48 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.20-0.40 | 0.35-0.55 | 0.08-0.15 |
86B45 | 0.43-0.48 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.40-0.70 | 0.40-0.60 | 0.15-0.25 |
94B15 | 0.13-0.18 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.30-0.60 | 0.30-0.50 | 0.08-0.15 |
94B17 | 0.15-0.20 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.30-0.60 | 0.30-0.50 | 0.08-0.15 |
94B30 | 0.28-0.33 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.30-0.60 | 0.30-0.50 | 0.08-0.15 |
94B40 | 0.38–0.43 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | 0.30-0.60 | 0.30-0.50 | 0.08-0.15 |
B Gradus in hac tabula cum littera B, qualia 50B40 ostensi, expectari possunt 0.0005% minimum boron imperium habere. AGradus in hac tabula cum praepositione litterae E ostensae plerumque per processum fornacem fundamentalem-electricam fabricantur. Cetera omnia normaliter per processum focialem basic-patens fabricari possunt, sed per processum electrico-furnacum fundamentali cum adaptationibus in phosphoro et sulphure confici possunt.
CLimitationes phosphori sulphuris in singulis processibus sunt hae;
Basic fornax electrica 0.025 max % Acidula fornax electrica 0.050 max %
Acidi focum apertum 0.040 max % Acidulum focum apertum 0.050 max %
D Minimum et maximum contentus sulphuris ferros resulfurizatas indicat.
EEmptor haec maxima ponderis potest nominare: aeris, 0,30%; aluminium, 0.050%; et dolor, 0.0015%.
Mechanica Property
Typical Tensile Properties, Hardness and Thermal Condition for some of more Common Grades of Carbon and Alloy Steels
CW-Cold Operatus SR-Stus Sublevatus A-Annealed N NormalizedA Haec sunt symbola definitiones pro variis conditionibus: HR-Hot Rolle
Gradus | Condi- | Ultima | Cede | Prolongatio | Rockwell, | ||||
Desig- | tioA | Fortitudo, | Fortitudo, | in 2 in. or * | duritia | ||||
gens | 50 mm, % | B Scale | |||||||
ksi | MPa | ksi | MPa | ||||||
1020 | HR | 50 | 345 | 32 | 221 | 25 | 55 | ||
CW | 70 | 483 | 60 | 414 | 5 | 75 | |||
SR | 65 | 448 | 50 | 345 | 10 | 72 | |||
A | 48 | 331 | 28 | 193 | 30 | 50 | |||
N | 55 | 379 | 34 | 234 | 22 | 60 | |||
1025 | HR | 55 | 379 | 35 | 241 | 25 | 60 | ||
CW | 75 | 517 | 65 | 448 | 5 | 80 | |||
SR | 70 | 483 | 55 | 379 | 8 | 75 | |||
A | 53 | 365 | 30 | 207 | 25 | 57 | |||
N | 55 | 379 | 36 | 248 | 22 | 60 | |||
1035 | HR | 65 | 448 | 40 | 276 | 20 | 72 | ||
CW | 85 | 586 | 75 | 517 | 5 | 88 | |||
SR | 75 | 517 | 65 | 448 | 8 | 80 | |||
A | 60 | 414 | 33 | 228 | 25 | 67 | |||
N | 65 | 448 | 40 | 276 | 20 | 72 | |||
1045 | HR | 75 | 517 | 45 | 310 | 15 | 80 | ||
CW | 90 | 621 | 80 | 552 | 5 | 90 | |||
SR | 80 | 552 | 70 | 483 | 8 | 85 | |||
A | 65 | 448 | 35 | 241 | 20 | 72 | |||
N | 75 | 517 | 48 | 331 | 15 | 80 | |||
1050 | HR | 80 | 552 | 50 | 345 | 10 | 85 | ||
SR | 82 | 565 | 70 | 483 | 6 | 86 | |||
A | 68 | 469 | 38 | 262 | 18 | 74 | |||
N | 78 | 538 | 50 | 345 | 12 | 82 | |||
1118 | HR | 50 | 345 | 35 | 241 | 25 | 55 | ||
CW | 75 | 517 | 60 | 414 | 5 | 80 | |||
SR | 70 | 483 | 55 | 379 | 8 | 75 | |||
A | 50 | 345 | 30 | 207 | 25 | 55 | |||
N | 55 | 379 | 35 | 241 | 20 | 60 | |||
1137 | HR | 70 | 483 | 40 | 276 | 20 | 75 | ||
CW | 80 | 552 | 65 | 448 | 5 | 85 | |||
SR | 75 | 517 | 60 | 414 | 8 | 80 | |||
A | 65 | 448 | 35 | 241 | 22 | 72 | |||
N | 70 | 483 | 43 | 296 | 15 | 75 | |||
4130 | HR | 90 | 621 | 70 | 483 | 20 | 89 | ||
SR | 105 | 724 | 85 | 586 | 10 | 95 | |||
A | 75 | 517 | 55 | 379 | 30 | 81 | |||
N | 90 | 621 | 60 | 414 | 20 | 89 | |||
4140 | HR | 120 | 855 | 90 | 621 | 15 | 100 | ||
SR | 120 | 855 | 100 | 689 | 10 | 100 | |||
A | 80 | 552 | 60 | 414 | 25 | 85 | |||
N | 120 | 855 | 90 | 621 | 20 | 100 |
d
tolerantia
Diameter extra tolerances in Tubing-Calida circumA,B,C
Extra Diameter Location Range, | Extra diametri tolerantia, m. | |||
in. (mm) | Plus | Sub | ||
Usque ad 2.999 (76.17) | 0.00 (0.51) | 0.00 (0.51) | ||
3.000–4.499 (76.20–114.27) | 0.024 (0.64) | 0.024 (0.64) | ||
4.500–5.999 (114.30-152.37) | 0.031 (0.79) | 0.031 (0.79) | ||
6.000–7.499 (152.40-190.47) | 0.038 (0.94) | 0.038 (0.94) | ||
7.500–8.999 (190.50–228.57) | 0.041 (1.14) | 0.041 (1.14) | ||
9.000–10.750 (228.60-273.05) | 0.041 (1.27) | 0.041 (1.27) | ||
Patientiae diametri non applicandae sunt conditionibus normalizatis et temperatis vel extinctis et temperatis.
B Communis range magnitudinum calidis tubis perfecti est 11⁄2 in. (38.1 mm) ad 103⁄4 in (273.0 mm) crassitudine parietis extra diametrum cum diametro saltem 3% vel plus, sed non minus quam 0.095 in.
C Maiores magnitudinis in promptu sunt; consulere fabrica magnitudinis et tolerantiae.
Murus Crassitudo tolerantiae ad circum Hot-Finished
Tubing
Murus Crassitudo | Muri Crassitudo Tolerantia;Apercent Plus | |||
Ut range sentio | et sub nominali | |||
de foris | ||||
Foris | Foris | Foris | ||
Diameter | ||||
Diameter | Diameter | Diameter | ||
2.999 in. | 3.000 in. | 6.000 in. | ||
(76.19 mm) | (76.20 mm) | (152.40 mm) | ||
et minor | ad 5.999 in. | ad 10.750 in. | ||
(152.37 mm) | (273.05 mm) | |||
Sub 15 | 12.5 | 10.0 | 10.0 | |
XV et supra | 10.0 | 7.5 | 10.0 | |
Crassitudo parietis tolerantiae ad parietes 0,199 in. (5.05 mm) et minus applicari non potest; consulere fabricam sustinentiae parietis in talibus tubulis magnitudinum.
dimensio maioris momenti, deinde Tubing-frigida operata debet dari intra diametrum et parietem crassitudinis vel extra diametrum et intra diametrum.
Aspera Tubing Mechanica - Variatio extra diametri et parietis crassitudinem tolerantiam in Tabula non excedunt. Mensa tolerantias operit ut crassitudines parietis extra diametrum applicata et ad certam magnitudinem applicata.
Humus Mechanica Tubing-Variatio extra diameterum tolerantias in Tabula non excedat. Productum hoc ex tubo frigido operato normaliter producitur.
Longitudines—Mechanicae Tubingae plerumque in molendinis longi- tudinibus, 5 ft (1,5 m) instructae sunt. Certae longitudinum incisae sunt, cum ab emptore specificatae. Longitudo tolerantiae in Tabula monstrantur.
Rectitudo — Recta tolerantiae inconsutilem rotundum Tubingae quantitates in Tabula exhibitas non excedunt.
Test opus est
1.Hardness Test
Cum duritiei limites exiguntur, consulatur fabrica. Duritiae typicae in Tabula recensentur. Cum denotatur, durities experimentorum in 1% fistularum exercebitur.
2. Tension Tests
Cum distrahentes proprietates requirantur, fabrica consulatur. Typicalis possessiones distrahentes pro aliquibus gradibus communioribus et condicionibus thermarum in tabula recensentur.
3.Nondestructive Test
Variae rationes testium ultrasonicarum vel electromagneticorum non destructivorum praesto sunt. Probatio adhibenda et inspectio limitum a fabrica et emptore conventione constituetur.
4.Flaring Test
Cum speciales requiruntur ad munditiem ferri, modi experimenti et limites acceptationis a fabrica et emptore conventione constituentur.