Hot-selling GB/T 9948 Petroleum Cracking Pipe, 12crmo 15crmog 12cr1mo Seamless Steel Pipe
Commissio nostra debet praebere nostris clientibus et consumers cum idealibus qualitatibus et infestantibus productis digitalibus portatilis pro Hot-venditionis GB/T 9948 Petroleum Cracking Pipe, 12crmo 15crmog 12cr1mo Seamless Steel Pipe, Nunc expectamus etiam maiorem cooperationem cum transmarinis partibus. clientes secundum mutua beneficia. Quaeso libenter contact us pro magis details.
Commissio nostra debet providere nostris clientibus et consumers cum idealibus qualitatibus et infestantibus productos digitales portabiles proChina GB/T9948 Cracking Pipe et Seamless Steel PipeQuisque pretium elit mauris. Diuturnum tempus cum sulum emptoribus cooperationem quaerimus. Ut huic rei, qualitatem nostram tenemus et extraordinariam emptoris servitium praestamus. Grata societas nostra, te exspectat cooperari.
Overview
| Latin:GB9948-2006 | Calor curatio: Annealing / normalizing / Tempering |
| Grade Group: 10、12CrMo、15CrMo, 07Crl9Nil0, etc | Diameter exterior (Round): 10 - 1000 Mm |
| Crassitudo: 1 - 100 mm | Applicationem: calor commutationem fistulae |
| Diameter exterior (Round): 10 - 1000 mm | Superficiem amet, ut Customer opus est |
| Longitudo, certae longitudinis vel incerti longitudinis | Ars: Hot Rolled |
| Sectio Figura: Circum | Specialis Pipe: Densissima Pipe Wall |
| Locus Origin: China | Usus: calor commutationem fistulae |
| Certification: ISO9001:2008 | Test: UT/MT |
Applicationem
Tubus ferri inconsutilem pro petroleum crepuit, inconsutilem tubulam ferream pro tubulis fornacibus, caloris fistulae permutationis et fistulae pressionis in industria petrochemical.
Princeps qualitas structuralis chalybis carbonis gradus sunt 20g, 20mng et 25mng.
Admisceri structurae ferri gradus: 15mog, 20mog, 12crmog
15CrMoG、12Cr2MoG、12CrMoVG, etc
Principalis Gradus
Gradus summus qualitas chalybe carbonis structuralis: 10# -20#
Qualitas carbo carbonis structilis princeps gradus gradus: 20g, 20mng et 25mng
Admisceri structurae ferri gradus: 15mog, 20mog, 12crmog, 15CrMoG、12Cr2MoG, etc.
Chemical Component
| No | Gradus | Chemical Component % | |||||||||||
| C | Si | Mn | Cr | Mo | Ni | Nb | Ti | V | Cu | P | S | ||
| ≤ | |||||||||||||
| High Quality Carbon Structural Steel | 10 | 0. 07-0.13 | 0.17 -0. 37 | 0.35 -0.65 | <0.15 | <0.15 | <0. 25 | - | - | <0. 08 | <0. 20 | 0. 025 | 0. 015 |
| 20 | 0.17-0. 23 | 0.17 -0. 37 | 0.35 -0.65 | <0. 25 | <0.15 | <0. 25 | - | - | <0. 08 | <0. 20 | 0. 025 | 0. 015 | |
| Admisce Structural Ferro | 12CrMo | 0. 08-0.15 | 0.17 -0.37 | 0. 40-0. 70 | 0. 40-0. 70 | 0. 40 -0.55 | <0. 30 | - | - | 一 | <0. 20 | 0. 025 | 0. 015 |
| 15CrMo | 0.12 -0.18 | 0.17-0. 37 | 0.40 -0. 70 | 0. 80-1.1 | 0. 40-0.55 | <0. 30 | - | - | 一 | <0. 20 | 0. 025 | 0. 015 | |
| 12CrlMo | 0. 08 -0.15 | 0.50 -1. 00 | 0. 30-0.6 | 1.00-1. 50 | 0.45 -0.65 | <0. 30 | - | - | - | <0, 20 | 0. 025 | 0. 015 | |
| 12CrlMoV | 0. 08-0.15 | 0.17-0. 37 | 0. 40-0. 70 | 0.90-1.2 | 0. 25 -0.35 | <0. 30 | - | - | 0.15 -0. 30 | <0. 20 | 0.024 | 0. 010 | |
| 12Cr2Mo | 0.08-0.15 | <0. 50 | 0. 40-0. 60 | 2. 00-2. 50 | 0. 90-1.13 | <0. 30 | - | - | 一 | <0. 20 | 0. 025 | 0. 015 | |
| 12Cr5MoI | <0.15 | <0. 50 | 0.30-0.6 | 4. 00-6 | 0. 45 -0. 60 | <0. 60 | - | - | <0. 20 | 0. 025 | 0. 015 | ||
| 12Cr5MoNT | |||||||||||||
| 12Cr9MoI | <0.15 | 0. XXV-1. 00 | 0. 30-0. 60 | 8.00 -10. 00 | 0. 90-1.1 | <0. 60 | - | - | - | <0. 20 | 0. 025 | 0, 015 | |
| 12Cr9MoNT | |||||||||||||
| Aliquam calor resistens Steel | 07Crl9Nil0 | 0. 04-0.1 | <1. 00 | <2. 00 | 18. 00-20. 00 | - | 8. 00-11 | - | - | - | - | 0. 030 | 0. 015 |
| 07Crl8NillNb | 0. 04-0.1 | <1. 00 | <2. 00 | 17. 00-19. 00 | - | 9.00-12. 00 | 8C-1.1 | - | - | - | 0. 030 | 0. 015 | |
| 07Crl9NillTi | 0. 04-0.1 | <0. 75 | <2. 00 | 17.00-20. 00 | - | 9. 00~13. 00 | - | 4C-0. 60 | 一 | 一 | 0.03 | 0. 015 | |
| 022Crl7Nil2Mo2 | <0. 030 | <1. 00 | <2. 00 | 16. 00-18. 00 | 2. 00-3. 00 | 10. 00 -14. 00 | - | 一 | 一 | - | 0.03 | 0. 015 | |
Mechanica Property
| No | Tensile MPa | Cede MPa | Post fracturam A/% | Horrendum effusio industria kv2/j | Brinell duritia numero | ||
| effigies | transver | effigies | transver | ||||
| non minus quam | non magis quam | ||||||
| 10 | 335〜475 | 205 | 25 | 23 | 40 | 27 | |
| 20 | 410〜550 | 245 | 24 | 22 | 40 | 27 | |
| 12CrMo | 410〜560 | 205 | 21 | 19 | 40 | 27 | 156 HBW |
| 15CrMo | 440〜640 | 295 | 21 | 19 | 40 | 27 | 170 HBW |
| 12CrlMo | 415〜560 | 205 | 22 | 20 | 40 | 27 | 163 HBW |
| 12CrlMoV | 470〜640 | 255 | 21 | 19 | 40 | 27 | 179 HBW |
| 12Cr2Mo | 450~600 | 280 | 22 | 20 | 40 | 27 | 163 HBW |
| 12Cr5MoI | 415〜590 | 205 | 22 | 20 | 40 | 27 | 163 HBW |
| 12Cr5MoNT | 480〜640 | 280 | 20 | 18 | 40 | 27 | - |
| 12Cr9MoI | 460〜640 | 210 | 20 | 18 | 40 | 27 | 179 HBW |
| 12Cr9MoNT | 590-740 | 390 | 18 | 16 | 40 | 27 | |
| O7Crl9NilO | 2520 | 205 | 35 | 187 HBW | |||
| 07Crl8NillNb | >520 | 205 | 35 | - | 187 HBW | ||
| 07Crl9NillTi | >520 | 205 | 35 | - | - | 187 HBW | |
| 022Crl7Nil2Mo2 | >485 | 170 | 35 | 一 | - | 187 HBW | |
| Nam chalybea parietis crassitudine minor quam 5mm tubo experimentum duritiem non faciunt | |||||||
Test opus est
HYDRAULICUS test
Expertus hydraulicus pro ferro tibiis singillatim peragendis. Maxime test pressio XX MPa est. Sub pressione experimenti, tempus stabilizationis non minus quam 10 s erit, et lacus ferreae fistulae non permittitur.
test adulatione
Experimentum adulationis agetur pro fistula ferrea cum diametro exteriore major quam 22 mm
Flaring test
Princeps qualitas chalybis carbonis structuralis et incorrupta (calor-repugnans) fistulae ferreae cum diametro exteriore non plus 76 mm et parietis crassitie non plus quam 8 mm sub experimento dilatandi erit. Expertus flagrans in cella temperies exercebitur. Diameter exterior ratis specimen elatans post summum nucleum cereum 60% of flaminium occurret requisitis mensae 7. Nulla rimas vel rimas in specimen post urentem concessum est. Secundum exigentias postulatoris et in contractu notatis, stannum structurale ferrum etiam adhiberi potest ad probationem dilatationem.
Nondestructive teste
Fistulae ferreae vitio detectioni ultrasonicae subicientur singillatim secundum praescripta GB / T 5777-2008. Secundum exigentias postulatoris, aliae probationes non perniciales addi possunt post tractatum inter supplementum et postulatorem et in contractu indicatis.
Erugo test
Testa corrosio intergranuaria agetur ad fistulam chalybem immaculatam (calor repugnans). Methodus probandi erit secundum praescripta methodi Sinensis E in GB/T 4334-2008, et corrosio intergranulare proclivitas post experimentum non licet.
Post tractatum inter supplicem et postulatorem, et notatis in contractu, postulator potest alias methodos testium corrosionis designare.
Product Detail
mechanica/Chemica&Fertilizer Pipes
GB/T8162-2008
ASTM_A519-2006
BS EN 10210-1-2006
ASTM A53A53M-2012
GB9948-2006
GB6479-2013
GB/T 17396-2009
Commissio nostra debet praebere nostris clientibus et consumers cum idealibus qualitatibus et infestantibus productis digitalibus portatilis pro Hot-venditionis GB/T 9948 Petroleum Cracking Pipe, 12crmo 15crmog 12cr1mo Seamless Steel Pipe, Nunc expectamus etiam maiorem cooperationem cum transmarinis partibus. clientes secundum mutua beneficia. Quaeso libenter contact us pro magis details.
Hot-venditionisChina GB/T9948 Cracking Pipe et Seamless Steel PipeQuisque pretium elit mauris. Diuturnum tempus cum sulum emptoribus cooperationem quaerimus. Ut huic rei, qualitatem nostram tenemus et extraordinariam emptoris servitium praestamus. Grata societas nostra, te exspectat cooperari.
Oleum petrochemicum, pressura alta boiler, usus specialis tubo inconsutilem boiler inconsutilem, tubo geologico seamless ferro tubo et tubo olei inconsutilem.
Chemical Component
| notam | Chemical Component（%） | ||||||||
| C | Mn | Si | Cr | Mo | Ni | Nb+Ta | S | P | |
| 15CrMo | 0.12~0.18 | 0.40~0.70 | 0.17~0.37 | 0.80~1.10 | 0.40~0.55 | ≤0.30 | _ | ≤0.035 | ≤0.035 |
Mechanica Property
| notam | Tensile MPa | Cede MPa | Prolongatio% |
| 15CrMo | 440~640 | 295 | 22 |