Ċina tal-karbonju bla xkiel tal-azzar u liga tal-liga tal-manifattur u l-fornitur

Azzar tal-karbonju bla xkiel u tubi mekkaniċi tal-liga

Deskrizzjoni qasira:

Tubi tal-azzar bla xkiel, pajp tal-azzar tal-karbonju u tubi mekkaniċi tal-liga, prinċipalment għal mekkaniċi ġewwaASTM A519-2006Tubi mekkaniċi standard, liga jinkludu prinċipalment

1018.1026,8620.4130,4140 eċċ.

Ħlas:Depożitu ta '30%, 70% L / C jew B / L Kopja jew 100% L / C fil-vista

Kwantità Min.Order:1 pc

Abbiltà tal-Provvista:Inventarju annwali tal-20000 tunnellata tal-pajp tal-azzar

Ħin taċ-Ċomb:7-14 ijiem jekk fl-istokk, 30-45 ġurnata biex tipproduċi

Ippakkjar:Black jisparixxi, ċanfrin u għatu għal kull pajp wieħed; OD taħt il-219mm jeħtieġ li tippakkja fil-mazz, u kull mazz ma jaqbeżx 2 tunnellati.

Ibgħatilna l-email Niżżel bħala PDF

Dettall tal-prodott

Tags tal-prodott

Ħarsa ġenerali

Standard:ASTM A519-2006	Liga jew le: liga jew karbonju
Grupp ta 'Grad: 1018.1026,8620.4130.4140	Applikazzjoni: tubu mekkaniku
Ħxuna: 1 - 100 mm	Trattament tal-wiċċ: bħala l-ħtieġa tal-klijent
Dijametru ta 'barra (tond): 10 - 1000 mm	Teknika: Irrumblat bis-sħana jew irrumblat kiesaħ
Tul: tul fiss jew tul każwali	Trattament tas-sħana: ttremprar / normalizzazzjoni / serħan tal-istress
Forma tat-taqsima: tond	Pajp speċjali: pajp tal-ħajt oħxon
Post tal-Oriġini: iċ-Ċina	Użu: Mekkaniku
Ċertifikazzjoni: ISO9001: 2008	Test: ECT / UT

Applikazzjoni

Jintuża prinċipalment għal mekkaniċi u użat biex isiru ċilindri tal-gass. Inkludi l-karbonju u l-liga ta 'tubi mekkaniċi mingħajr saldatura, u jkopri kemm tubi mekkaniċi bla xkiel bla xkiel u tubi mekkaniċi lesti bla xkiel kiesaħ f'daqs sa u inklużi 12 3⁄4 pulzieri (323.8 mm) barra dijametru għal tubi tondi kif meħtieġ.

Grad prinċipali

1018.1026,8620.4130,4140

Komponent kimiku

Tabella 1 Rekwiżiti kimiċi ta 'azzar b'livell baxx ta' karbonju

Grad	Limiti ta 'Kompożizzjoni Kimika,%
Denominazzjoni	Karbona	Manganieseb	Fosfru, b	Kubrit, b
			massimu	massimu
Mt x 1015	0.10–0.20	0.60–0.90	0.04	0.05
MT 1010	0.05–0.15	0.30–0.60	0.04	0.05
MT 1015	0.10–0.20	0.30–0.60	0.04	0.05
MT 1020	0.15–0.25	0.30–0.60	0.04	0.05
Mt x 1020	0.15–0.25	0.70–1.00	0.04	0.05

Tabella 2 Rekwiżiti kimiċi ta 'azzar ieħor tal-karbonju^BIl-limiti japplikaw għall-analiżi tas-sħana; Ħlief kif meħtieġ minn 6.1, l-analiżi tal-prodott huma soġġetti għat-tolleranzi addizzjonali applikabbli mogħtija fit-Tabella 5.

Grad		Limiti ta 'kompożizzjoni kimika,% a
Denominazzjoni
Denominazzjoni	Karbonju	Manganiż	Fosfru,	Kubrit,
			massimu	massimu
1008	0.10 Max	0.30–0.50	0.04	0.05
1010	0.08–0.13	0.30–0.60	0.04	0.05
1012	0.10–0.15	0.30–0.60	0.04	0.05
1015	0.13–0.18	0.30–0.60	0.04	0.05
1016	0.13–0.18	0.60–0.90	0.04	0.05
1017	0.15–0.20	0.30–0.60	0.04	0.05
1018	0.15–0.20	0.60–0.90	0.04	0.05
1019	0.15–0.20	0.70–1.00	0.04	0.05
1020	0.18–0.23	0.30–0.60	0.04	0.05
1021	0.18–0.23	0.60–0.90	0.04	0.05
1022	0.18–0.23	0.70–1.00	0.04	0.05
1025	0.22–0.28	0.30–0.60	0.04	0.05
1026	0.22–0.28	0.60–0.90	0.04	0.05
1030	0.28–0.34	0.60–0.90	0.04	0.05
1035	0.32–0.38	0.60–0.90	0.04	0.05
1040	0.37–0.44	0.60–0.90	0.04	0.05
1045	0.43–0.50	0.60–0.90	0.04	0.05
1050	0.48–0.55	0.60–0.90	0.04	0.05
1518	0.15–0.21	1.10–1.40	0.04	0.05
1524	0.19–0.25	1.35–1.65	0.04	0.05
1541	0.36–0.44	1.35–1.65	0.04	0.05

A Il-firxiet u l-limiti mogħtija f'din it-tabella japplikaw għall-analiżi tas-sħana; Ħlief kif meħtieġ minn6.1, l-analiżi tal-prodott huma soġġetti għall-tollerazzjonijiet addizzjonali applikabbli mogħtija fit-tabella numru 5.

Tabella 3 Rekwiżiti kimiċi għal azzar tal-liga
Nota	1 - Il-meded u l-limiti f'din it-tabella japplikaw għal azzar li ma jaqbiżx 200 in.2 (1290 cm2) f'żona ta 'sezzjoni trasversali.
Nota	2 - Kwantitajiet żgħar ta 'ċerti elementi huma preżenti fl-azzar tal-liga li mhumiex speċifikati jew meħtieġa. Dawn l-elementi huma kkunsidrati bħala inċidentali
u jista 'jkun preżenti għall-ammonti massimi li ġejjin: ram, 0.35%; Nickel, 0.25%; kromju, 0.20%; molibdenu, 0.10%.
Nota	3 - Il-meded u l-limiti mogħtija f'din it-tabella japplikaw għall-analiżi tas-sħana; Ħlief kif meħtieġ minn 6.1, l-analiżi tal-prodott huma soġġetti għall-applikabbli
Tolleranzi addizzjonali mogħtija fit-Tabella Numru 5.

Grad^A^,^B				Limiti ta 'Kompożizzjoni Kimika,%
Desigta-
Desigta-	Karbonju	Manganiż	Fosfo-	Kubrit,^C^,^D	Silikon	Nickel	Kromju	Molybde-
zjoni								Molybde-
zjoni			rus,^Cmassimu	massimu				numru
								numru
1330	0.28–0.33	1.60–1.90	0.04	0.04	0.15–0.35	...	...	...
1335	0.33–0.38	1.60–1.90	0.04	0.04	0.15–0.35	...	...	...
1340	0.38–0.43	1.60–1.90	0.04	0.04	0.15–0.35	...	...	...
1345	0.43–0.48	1.60–1.90	0.04	0.04	0.15–0.35	...	...	...
3140	0.38–0.43	0.70–0.90	0.04	0.04	0.15–0.35	1.10–1.40	0.55–0.75	...
E3310	0.08–0.13	0.45–0.60	0.025	0.025	0.15–0.35	3.25–3.75	1.40–1.75	...
4012	0.09–0.14	0.75–1.00	0.04	0.04	0.15–0.35	...	...	0.15–0.25
4023	0.20–0.25	0.70–0.90	0.04	0.04	0.15–0.35	...	...	0.20–0.30
4024	0.20–0.25	0.70–0.90	0.04	0.035−0.050	0.15–0.35	...	...	0.20–0.30
4027	0.25–0.30	0.70–0.90	0.04	0.04	0.15–0.35	...	...	0.20–0.30
4028	0.25–0.30	0.70–0.90	0.04	0.035−0.050	0.15–0.35	...	...	0.20–0.30
4037	0.35–0.40	0.70–0.90	0.04	0.04	0.15–0.35	...	...	0.20–0.30
4042	0.40–0.45	0.70–0.90	0.04	0.04	0.15–0.35	...	...	0.20–0.30
4047	0.45–0.50	0.70–0.90	0.04	0.04	0.15–0.35	...	...	0.20–0.30
4063	0.60–0.67	0.75–1.00	0.04	0.04	0.15–0.35	...	...	0.20–0.30
4118	0.18–0.23	0.70–0.90	0.04	0.04	0.15–0.35	...	0.40–0.60	0.08–0.15
4130	0.28–0.33	0.40–0.60	0.04	0.04	0.15–0.35	...	0.80–1.10	0.15–0.25
4135	0.32–0.39	0.65–0.95	0.04	0.04	0.15–0.35	...	0.80–1.10	0.15–0.25
4137	0.35–0.40	0.70–0.90	0.04	0.04	0.15–0.35	...	0.80–1.10	0.15–0.25
4140	0.38–0.43	0.75–1.00	0.04	0.04	0.15–0.35	...	0.80–1.10	0.15–0.25
4142	0.40–0.45	0.75–1.00	0.04	0.04	0.15–0.35	...	0.80–1.10	0.15–0.25
4145	0.43–0.48	0.75–1.00	0.04	0.04	0.15–0.35	...	0.80–1.10	0.15–0.25
4147	0.45–0.50	0.75–1.00	0.04	0.04	0.15–0.35	...	0.80–1.10	0.15–0.25
4150	0.48–0.53	0.75–1.00	0.04	0.04	0.15–0.35	...	0.80–1.10	0.15–0.25
4320	0.17–0.22	0.45–0.65	0.04	0.04	0.15–0.35	1.65–2.00	0.40–0.60	0.20–0.30
4337	0.35–0.40	0.60–0.80	0.04	0.04	0.15–0.35	1.65–2.00	0.70–0.90	0.20–0.30
E4337	0.35–0.40	0.65–0.85	0.025	0.025	0.15–0.35	1.65–2.00	0.70–0.90	0.20–0.30
4340	0.38–0.43	0.60–0.80	0.04	0.04	0.15–0.35	1.65–2.00	0.70–0.90	0.20–0.30
E4340	0.38–0.43	0.65–0.85	0.025	0.025	0.15–0.35	1.65–2.00	0.70–0.90	0.20–0.30
4422	0.20–0.25	0.70–0.90	0.04	0.04	0.15–0.35	...	...	0.35–0.45
4427	0.24–0.29	0.70–0.90	0.04	0.04	0.15–0.35	...	...	0.35–0.45
4520	0.18–0.23	0.45–0.65	0.04	0.04	0.15–0.35	...	...	0.45–0.60
4615	0.13–0.18	0.45–0.65	0.04	0.04	0.15–0.35	1.65–2.00	...	0.20–0.30
4617	0.15–0.20	0.45–0.65	0.04	0.04	0.15–0.35	1.65–2.00	...	0.20–0.30
4620	0.17–0.22	0.45–0.65	0.04	0.04	0.15–0.35	1.65–2.00	...	0.20–0.30
4621	0.18–0.23	0.70–0.90	0.04	0.04	0.15–0.35	1.65–2.00	...	0.20–0.30
4718	0.16–0.21	0.70–0.90	0.04	0.04	0.15–0.35	0.90–1.20	0.35–0.55	0.30–0.40
4720	0.17–0.22	0.50–0.70	0.04	0.04	0.15–0.35	0.90–1.20	0.35–0.55	0.15–0.25
4815	0.13–0.18	0.40–0.60	0.04	0.04	0.15–0.35	3.25–3.75	...	0.20–0.30
4817	0.15–0.20	0.40–0.60	0.04	0.04	0.15–0.35	3.25–3.75	...	0.20–0.30
4820	0.18–0.23	0.50–0.70	0.04	0.04	0.15–0.35	3.25–3.75	...	0.20–0.30
5015	0.12–0.17	0.30–0.50	0.04	0.04	0.15–0.35	...	0.30–0.50	...
5046	0.43–0.50	0.75–1.00	0.04	0.04	0.15–0.35	...	0.20–0.35	...
5115	0.13–0.18	0.70–0.90	0.04	0.04	0.15–0.35	...	0.70–0.90	...
5120	0.17–0.22	0.70–0.90	0.04	0.04	0.15–0.35	...	0.70–0.90	...
5130	0.28–0.33	0.70–0.90	0.04	0.04	0.15–0.35	...	0.80–1.10	...
5132	0.30–0.35	0.60–0.80	0.04	0.04	0.15–0.35	...	0.75–1.00	...
5135	0.33–0.38	0.60–0.80	0.04	0.04	0.15–0.35	...	0.80–1.05	...
5140	0.38–0.43	0.70–0.90	0.04	0.04	0.15–0.35	...	0.70–0.90	...
5145	0.43–0.48	0.70–0.90	0.04	0.04	0.15–0.35	...	0.70–0.90	...
5147	0.46–0.51	0.70–0.95	0.04	0.04	0.15–0.35	...	0.85–1.15	...
5150	0.48–0.53	0.70–0.90	0.04	0.04	0.15–0.35	...	0.70–0.90	...
5155	0.51–0.59	0.70–0.90	0.04	0.04	0.15–0.35	...	0.70–0.90	...
5160	0.56–0.64	0.75–1.00	0.04	0.04	0.15–0.35	...	0.70–0.90	...
52100^E	0.93–1.05	0.25–0.45	0.025	0.015	0.15–0.35	0.25 Max	1.35–1.60	0.10 Max
E50100	0.98–1.10	0.25–0.45	0.025	0.025	0.15–0.35	...	0.40–0.60	...
E51100	0.98–1.10	0.25–0.45	0.025	0.025	0.15–0.35	...	0.90–1.15	...
E52100	0.98–1.10	0.25–0.45	0.025	0.025	0.15–0.35	...	1.30–1.60	...
								Vanadju

6118	0.16–0.21	0.50–0.70	0.04	0.04	0.15–0.35	...	0.50–0.70	0.10–0.15
6120	0.17–0.22	0.70–0.90	0.04	0.04	0.15–0.35	...	0.70–0.90	0.10 min
6150	0.48–0.53	0.70–0.90	0.04	0.04	0.15–0.35	...	0.80–1.10	0.15 min

						Aluminju		Molibdenu

E7140	0.38–0.43	0.50–0.70	0.025	0.025	0.15–0.40	0.95–1.30	1.40–1.80	0.30–0.40

						Nickel

8115	0.13–0.18	0.70–0.90	0.04	0.04	0.15–0.35	0.20–0.40	0.30–0.50	0.08–0.15
8615	0.13–0.18	0.70–0.90	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8617	0.15–0.20	0.70–0.90	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8620	0.18–0.23	0.70–0.90	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8622	0.20–0.25	0.70–0.90	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8625	0.23–0.28	0.70–0.90	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8627	0.25–0.30	0.70–0.90	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8630	0.28–0.33	0.70–0.90	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8637	0.35–0.40	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8640	0.38–0.43	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8642	0.40–0.45	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8645	0.43–0.48	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8650	0.48–0.53	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8655	0.51–0.59	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8660	0.55–0.65	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
8720	0.18–0.23	0.70–0.90	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.20–0.30
8735	0.33–0.38	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.20–0.30
8740	0.38–0.43	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.20–0.30
8742	0.40–0.45	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.20–0.30
8822	0.20–0.25	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.30–0.40
9255	0.51–0.59	0.60–0.80	0.04	0.04	1.80–2.20	...	0.60–0.80	...
9260	0.56–0.64	0.75–1.00	0.04	0.04	1.80–2.20	...	...	...
9262	0.55–0.65	0.75–1.00	0.04	0.04	1.80–2.20	...	0.25–0.40	...
E9310	0.08–0.13	0.45–0.65	0.025	0.025	0.15–0.35	3.00–3.50	1.00–1.40	0.08–0.15
9840	0.38–0.42	0.70–0.90	0.04	0.04	0.15–0.35	0.85–1.15	0.70–0.90	0.20–0.30
9850	0.48–0.53	0.70–0.90	0.04	0.04	0.15–0.35	0.85–1.15	0.70–0.90	0.20–0.30
50B40	0.38–0.42	0.75–1.00	0.04	0.04	0.15–0.35	...	0.40–0.60	...
50b44	0.43–0.48	0.75–1.00	0.04	0.04	0.15–0.35	...	0.40–0.60	...
50b46	0.43–0.50	0.75–1.00	0.04	0.04	0.15–0.35	...	0.20–0.35	...
50B50	0.48–0.53	0.74–1.00	0.04	0.04	0.15–0.35	...	0.40–0.60	...
50B60	0.55–0.65	0.75–1.00	0.04	0.04	0.15–0.35	...	0.40–0.60	...
51B60	0.56–0.64	0.75–1.00	0.04	0.04	0.15–0.35	...	0.70–0.90	...
81B45	0.43–0.48	0.75–1.00	0.04	0.04	0.15–0.35	0.20–0.40	0.35–0.55	0.08–0.15
86B45	0.43–0.48	0.75–1.00	0.04	0.04	0.15–0.35	0.40–0.70	0.40–0.60	0.15–0.25
94B15	0.13–0.18	0.75–1.00	0.04	0.04	0.15–0.35	0.30–0.60	0.30–0.50	0.08–0.15
94B17	0.15–0.20	0.75–1.00	0.04	0.04	0.15–0.35	0.30–0.60	0.30–0.50	0.08–0.15
94B30	0.28–0.33	0.75–1.00	0.04	0.04	0.15–0.35	0.30–0.60	0.30–0.50	0.08–0.15
94B40	0.38–0.43	0.75–1.00	0.04	0.04	0.15–0.35	0.30–0.60	0.30–0.50	0.08–0.15

^BIl-gradi murija f'din it-tabella bl-ittra B, bħal 50B40, jistgħu jkunu mistennija li jkollhom kontroll tal-boron minimu ta '0.0005%.^AIl-gradi murija f'din it-tabella bi prefiss ittra e ġeneralment huma manifatturati mill-proċess bażiku-elettriku tal-funace. L-oħrajn kollha huma normalment manifatturati mill-proċess bażiku-miftuħ tal-qtugħ iżda jistgħu jiġu manifatturati mill-proċess bażiku-elettriku tal-furina b'aġġustamenti fil-fosfru u l-kubrit.

^ĊIl-limitazzjonijiet tal-kubrit tal-fosfru għal kull proċess huma kif ġej:

Forn Elettriku Bażiku 0.025 Max% Aċidu Furnace Electric 0.050 Max%

Basic Open Hearth 0.040 Max% Acid Open Hearth 0.050 Max%

^DIl-kontenut minimu u massimu tal-kubrit jindika azzar mibdula mill-ġdid.

^EIx-xerrej jista 'jispeċifika l-ammonti massimi li ġejjin: ram, 0.30%; aluminju, 0.050%; u ossiġnu, 0.0015%.

Propjetà mekkanika

Propjetajiet tipiċi tat-tensjoni, ebusija u kundizzjoni termali għal uħud mill-aktar gradi komuni ta 'azzar tal-karbonju u tal-liga

CW - Sold ħadem SR - stress meħlus minn N-Normalizeda Annealed dawn li ġejjin huma d-definizzjonijiet tas-simbolu għad-diversi kundizzjonijiet: HR-Hot Rolle

Grad	Kundizzjonijiet	Aħħari		Rendiment		Titwil	Rockwell,
Desig-	zjoni^A	Saħħa,		Saħħa,		f'2 pulzieri jew	Ebusija
nazzjon						50 mm,%	B Skala
		KSI	MPA	KSI	MPA	50 mm,%	B Skala
		KSI	MPA	KSI	MPA

1020	HR	50	345	32	221	25	55
	CW	70	483	60	414	5	75
	SR	65	448	50	345	10	72
	A	48	331	28	193	30	50
	N	55	379	34	234	22	60
1025	HR	55	379	35	241	25	60
	CW	75	517	65	448	5	80
	SR	70	483	55	379	8	75
	A	53	365	30	207	25	57
	N	55	379	36	248	22	60
1035	HR	65	448	40	276	20	72
	CW	85	586	75	517	5	88
	SR	75	517	65	448	8	80
	A	60	414	33	228	25	67
	N	65	448	40	276	20	72
1045	HR	75	517	45	310	15	80
	CW	90	621	80	552	5	90
	SR	80	552	70	483	8	85
	A	65	448	35	241	20	72
	N	75	517	48	331	15	80
1050	HR	80	552	50	345	10	85
	SR	82	565	70	483	6	86
	A	68	469	38	262	18	74
	N	78	538	50	345	12	82
1118	HR	50	345	35	241	25	55
	CW	75	517	60	414	5	80
	SR	70	483	55	379	8	75
	A	50	345	30	207	25	55
	N	55	379	35	241	20	60
1137	HR	70	483	40	276	20	75
	CW	80	552	65	448	5	85
	SR	75	517	60	414	8	80
	A	65	448	35	241	22	72
	N	70	483	43	296	15	75
4130	HR	90	621	70	483	20	89
	SR	105	724	85	586	10	95
	A	75	517	55	379	30	81
	N	90	621	60	414	20	89
4140	HR	120	855	90	621	15	100
	SR	120	855	100	689	10	100
	A	80	552	60	414	25	85
	N	120	855	90	621	20	100

Tolleranza

Tolleranzi ta 'Dijametru ta' Barra għal Tubi l-Isħan Tond^A^,^B^,^C

Firxa ta 'daqs ta' dijametru ta 'barra,	Tolleranza ta 'dijametru ta' barra, pulzieri (mm)
in. (mm)	Fuq	Taħt
Sa 2.999 (76.17)	0.020 (0.51)	0.020 (0.51)
3.000–4.499 (76.20–114.27)	0.025 (0.64)	0.025 (0.64)
4.500–5.999 (114.30–152.37)	0.031 (0.79)	0.031 (0.79)
6.000–7.499 (152.40–190.47)	0.037 (0.94)	0.037 (0.94)
7.500–8.999 (190.50–228.57)	0.045 (1.14)	0.045 (1.14)
9.000–10.750 (228.60–273.05)	0.050 (1.27)	0.050 (1.27)

Tolleranzi tad-dijametru mhumiex applikabbli għal kundizzjonijiet normalizzati u ttemprati jew imkessħa u ttemprati.

B Il-firxa komuni ta 'daqsijiet ta' tubi lesti sħan hija 1¹⁄2 pulzieri (38.1 mm) sa 10³⁄4 pulzieri (273.0 mm) Dijametru ta 'barra bi ħxuna tal-ħajt mill-inqas 3% jew aktar ta' dijametru ta 'barra, iżda mhux inqas minn 0.095 pulzieri (2.41 mm).

Huma daqsijiet ikbar huma disponibbli; Ikkonsulta lill-manifattur għal daqsijiet u tolleranzi.

Tolleranzi tal-ħxuna tal-ħajt għal tond sħun lest

Tubi

Ħxuna tal-ħajt	Tolleranza tal-ħxuna tal-ħajt,^Afil-mija fuq
Ivarjaw bħala fil-mija		u taħt nominali
ta 'barra
ta 'barra	Barra	Barra	Barra
Dijametru	Barra	Barra	Barra
Dijametru	Dijametru	Dijametru	Dijametru
	Dijametru	Dijametru	Dijametru
	2.999 in.	3.000 in.	6.000 in.
	(76.19 mm)	(76.20 mm)	(152.40 mm)
	u iżgħar	sa 5.999 in.	sa 10.750 in.
		(152.37 mm)	(273.05 mm)

Taħt il-15	12.5	10.0	10.0
15 u aktar	10.0	7.5	10.0

Tolleranzi ta 'ħxuna tal-ħajt ma jistgħux ikunu applikabbli għal ħitan 0.199 pulzieri (5.05 mm) u inqas; Ikkonsulta lill-manifattur għat-tolleranzi tal-ħajt fuq daqsijiet ta 'tubi bħal dawn.

Dimensjoni aktar importanti, allura tubi maħduma bil-kesħa għandhom ikunu speċifikati għal dijametru ta 'ġewwa u ħxuna tal-ħajt jew dijametru ta' barra u dijametru ta 'ġewwa.

Tubi mekkaniċi mdawrin mhux maħduma - il-varjazzjoni fid-dijametru ta 'barra u l-ħxuna tal-ħajt m'għandhiex taqbeż it-tolleranza fit-tabella. It-tabella tkopri t-tolleranzi kif applikati għad-dijametru ta 'barra u l-ħxuna tal-ħajt u tapplika għad-daqs speċifikat.

Tubi mekkaniċi mitħunin - il-varjazzjoni fid-djamant ta 'barra m'għandhiex taqbeż it-tolleranzi fit-tabella. Dan il-prodott normalment huwa prodott minn tubu maħdum kiesaħ.

Tulijiet - It-tubi mekkaniċi huma komunement forniti fit-tulijiet tal-mitħna, 5 ft (1.5 m) u aktar. It-tulijiet tal-qatgħa definiti huma forniti meta speċifikati mix-xerrej. It-tolleranzi tat-tul huma murija fit-tabella.

Dritt - It-tolleranzi dritti għal tubi tondi bla xkiel m'għandhomx jaqbżu l-ammonti murija fit-tabella.

Rekwiżit tat-Test

1. Test tal-Hardness
Meta jkunu meħtieġa limiti ta 'ebusija, il-manifattur għandu jiġi kkonsultat. Ebusija tipiċi huma elenkati fit-tabella. Meta speċifikat, it-test tal-ebusija għandu jitwettaq fuq 1% tat-tubi.

2. Testijiet tat-Tensjonijiet
Meta l-proprjetajiet tat-tensjoni huma meħtieġa, il-manifattur għandu jiġi kkonsultat. Propjetajiet tipiċi tat-tensjoni għal uħud mill-gradi l-aktar komuni u l-kundizzjonijiet termali huma elenkati fit-tabella.

3.Testijiet mhux distruttivi
Diversi tipi ta 'testijiet ultrasoniċi jew elettromanjetiċi mhux distruttivi huma disponibbli. It-test li għandu jintuża u l-limiti ta 'spezzjoni għandhom jiġu stabbiliti mill-Ftehim tal-Manifattur u x-Xerrej.

4. Test ta 'flaring