Ka ho khomarela maikutlo a hau a "Ho theha litharollo tsa boleng bo holimo le ho etsa metsoalle le batho ba tsoang lefats'eng lohle", re lula re beha takatso ea bareki ho qala ka Carbon Seamless Steel Pipe A 53, Hona joale re na le mohloli o moholo oa thepa le tekanyo ke molemo oa rona. Rea u amohela ho botsa ka thepa ea rona.
Ho khomarela maikutlo a hau a "Ho theha litharollo tsa boleng bo holimo le ho etsa metsoalle le batho ba tsoang lefats'eng lohle", re lula re beha takatso ea bareki ho qala ka eona.Pipe ea tšepe ea A53, Asme Sa106 Low Carbon Steel Seamless Pipe, Pipe ea tšepe e se nang Seam St52, Mechini eohle e tsoang kantle e laola ka nepo le ho netefatsa ho nepahala ha machining bakeng sa lihlahisoa. Ntle ho moo, re na le sehlopha sa basebetsi ba tsamaiso ea boleng bo phahameng le litsebi, ba etsang lihlahisoa tsa boleng bo phahameng 'me ba na le bokhoni ba ho hlahisa lihlahisoa tse ncha ho atolosa lehae la rona la' maraka le linaheng tse ling. Re lebelletse ka tieo hore bareki ba tle bakeng sa khoebo e atlehileng bakeng sa rona ka bobeli.
Kakaretso
Kopo
Haholo-holo e sebelisetsoa ho etsa tšepe ea boleng bo phahameng ea carbon, tšepe ea motsoako oa alloy le lipeipi tsa tšepe tse sa keneleng mocheso bakeng sa khatello e phahameng le ka holim'a lipeipi tsa boiler tsa mouoane.
Kereiti e ka Sehloohong
Kereiti ea boleng bo phahameng ba tšepe ea sebopeho sa carbon: 20g, 20mng, 25mng
Kereiti ea tšepe ea sebopeho sa tšepe15mog, 20mog, 12crmog, 15crmog, 12cr2mog, 12crmovg, 12cr3movsitib, joalo-joalo.
Mophato oa tšepe e sa keneleng mocheso1cr18ni9 1cr18ni11nb
Karolo ea Lik'hemik'hale
牌号 | 质量 等级 | 化学成分(质量分数广小/% | ||||||||||||||
C | Si | Mn | P | S | Nb | V | Ti | Cr | Ni | Cu | Nd | Mo | B | Als” | ||
不大于 | 不小于 | |||||||||||||||
Q345 | A | 0.20 | 0.50 | 1.70 | 0.035 | 0.035 |
|
|
| 0.30 | 0.50 | 0.20 | 0.012 | 0.10 | —- | - |
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 | 0.07 | 0.15 | 0.20 | 0.015 | ||||||||||
D | 0.18 | 0.030 | 0.025 | |||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q390 | A | 0.20 | 0.50 | 1.70 | 0.035 | 0.035 | 0.07 | 0.20 | 0.20 | 0.3. | 0.50 | 0.20 | 0.015 | 0.10 | - | - |
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 | 0,015 | |||||||||||||
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q42O | A | 0.20 | 0.50 | 1.70 | 0.035 | 0.035 | 0.07 | 0.2. | 0.20 | 0.30 | 0.80 | 0.20 | 0.015 | 0.20 | —- | —- |
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 | 0.015 | |||||||||||||
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q46O | C | 0.20 | 0.60 | 1.80 | 0.030 | 0.030 | 0.11 | 0.20 | 0.20 | 0.30 | 0.80 | 0.20 | 0.015 | 0.20 | 0.005 | 0.015 |
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q500 | C | 0j8 | 0.60 | 1.80 | 0.025 | 0.020 | 0.11 | 0.20 | 0.20 | 0.60 | 0.80 | 0.20 | 0.015 | 0.20 | 0.005 | 0.015 |
D | 0.025 | 0.015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
Q550 | C | 0.18 | 0.60 | 2.00 | 0.025 | 0,020 | 0.11 | 0.20 | 0.20 | 0.80 | 0.80 | 0.20 | 0.015 | 0.30 | 0.005 | 0.015 |
D | 0.025 | 0,015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
Q62O | C | 0.18 | 0.60 | 2.00 | 0.025 | 0.020 | 0.11 | 0.20 | 0.20 | 1.00 | 0.80 | 0.20 | 0.015 | 0.30 | 0.005 | 0.015 |
D | 0.025 | 0.015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
1除Q345A、Q345B牌号外,钢中应至少含有细化晶粒元素Al、Nb、V、Ti中的一种,根据需要,供方粒元素晶粒元素,最大值应符合表中规定。组合加入时,Nb+V+Ti<0.22%° * 对于 Q345、Q390、Q420 和 Q46O 牌号,Mo+Cr<0.30%o °各牌号的Cr、Ni作為残余元素时,Cr、Ni含量应各不大于0.30%方协商确定. J如供方能保证氮元素含量符合表中规定,可不进行氮含量分析。如果钢中加入Al Nb,V,Time素,氮元素含量不作限制,固氮元素含量应在质量证明书中注明. '当采用全铝时,全铝含量Ait^0.020%B
|
Thepa ea Mechini
No | Kereiti | Thepa ea Mechini | ||||
|
| Tensile | Khefutsa | Eketsa | Tšusumetso (J) | Handness |
1 | 20G | 410- | ≥ | 24/22% | 40/27 | - |
2 | 20MnG | 415- | ≥ | 22/20% | 40/27 | - |
3 | 25MnG | 485- | ≥ | 20/18% | 40/27 | - |
4 | 15MoG | 450- | ≥ | 22/20% | 40/27 | - |
6 | 12CrMoG | 410- | ≥ | 21/19% | 40/27 | - |
7 | 15CrMoG | 440- | ≥ | 21/19% | 40/27 | - |
8 | 12Cr2MoG | 450- | ≥ | 22/20% | 40/27 | - |
9 | 12Cr1MoVG | 470- | ≥ | 21/19% | 40/27 | - |
10 | 12Cr2MoWVTiB | 540- | ≥ | 18/-% | 40/- | - |
11 | 10Cr9Mo1VNbN | ≥ | ≥ | 20/16% | 40/27 | ≤ |
12 | 10Cr9MoW2VNbBN | ≥ | ≥ | 20/16% | 40/27 | ≤ |
Tlhokahalo ea Teko
Ntle le ho netefatsa sebopeho sa lik'hemik'hale le thepa ea mochini, liteko tsa hydrostatic li etsoa ka bonngoe, 'me ho etsoa liteko tsa ho phatloha le ho bata. . Ho phaella moo, ho na le litlhoko tse itseng bakeng sa microstructure, boholo ba lijo-thollo, le lera la decarburization ea phala ea tšepe e phethiloeng.
Matla a Phepelo
Matla a Phepelo: Lithane tse 2000 ka Khoeli Ka Kreiti ea GB/T5310-2017 Alloy Steel Pipe
Sephutheloana