Khamphani ea rona e romella kantle ho naha lipeipi tsa tšepe tsa sebopeho,China Seamless Pipe, China liphaephe tsa sebopeho, phala ea tšepe e se nang moroalo, lipeipi tsa sebopeho. Q345B thepa ke mofuta oa phala ea tšepe ea sebopeho.
Q345 ke mofuta oa thepa ea tšepe. Ke tšepe ea carbon alloy (c <0.2%) e nang le ts'ebetso e ntle ka kakaretso, ts'ebetso e ntle ea mocheso o tlase, ts'ebetso ea ho hatakela e batang, ts'ebetso ea welding le machinability. E sebelisoa haholo ka marokho, likoloi, likepe, mehaho, likepe tsa khatello, joalo-joalo Q e emela lihlahisoa tsa thepa ena, 'me 345 ea ho qetela e bua ka boleng ba lihlahisoa tsa thepa ena, e leng ho pota 345MPa. 'Me ha botenya ba thepa bo ntse bo eketseha, boleng ba eona ba lihlahisoa bo fokotseha.
Matla a tlhahiso:≤16mm:ho feta 345, 16-40mm: ho feta 335, 40-63mm: ho feta 325, 63-80mm: ho feta 315, 80-100m: ho feta 305, 100-150mm: ho feta 285, 150-200mm: ho feta 275.
Matla a matla: 450-630.
Elongation: ho feta 17.
Teko ea tšusumetso: Mocheso oa mocheso: 20°C: tse fetang 34.
Boemo ba tsamaiso
1. Pipe ea tšepe e se nang moeli bakeng sa sebopeho (GB/T8162-2008) ke aphala ea tšepe e se nang moroalobakeng sa sebopeho se akaretsang le sebopeho sa mochini.
2. Peipi ea tšepe e se nang seam bakeng sa lipalangoang tsa mokelikeli (GB/T8163-2008) ke kakaretso.phala ea tšepe e se nang moroalose sebedisoang ho tsamaisa metsi, oli, kgase le maro a mang.
3. Lipeipi tsa tšepe tse se nang seam bakeng sa liboilers tsa khatello e tlase le e mahareng (GB3087-2008) ke liphaephe tsa mocheso tsa tšepe tsa boleng bo holimo tse sebelisetsoang ho etsa lipeipi tsa mouoane tse futhumetseng haholo, lipeipi tse belang tsa metsi bakeng sa likhatello tse tlase le tse mahareng tsa meaho e fapaneng, le liphaephe tsa mouoane tse futhumetseng haholo. lipeipi tsa litene tsa arch bakeng sa li-boilers tsa locomotive. Li-tubes tsa tšepe tse pitikolotsoeng le tse batang (tse phuthetsoeng) tse se nang moroko.
4. Liphaephe tsa tšepe tse sa tsitsang bakeng sa li-boilers tse nang le khatello e phahameng (GB5310-2008) ke tšepe ea boleng bo phahameng ba carbon, alloy steel le liphaephe tsa tšepe tse se nang mocheso tse sa keneleng mocheso bakeng sa mocheso o futhumatsang oa li-boilers tsa metsi a nang le khatello e phahameng le holimo.
Kakaretso
Kopo
Haholo-holo e Sebelisoa ho Etsa Carbon Structural Steel, Alloy Structural Steel le meaho ea mochini.
Kereiti e ka Sehloohong
Mophato oa Tšepe ea Sebopeho sa Carbon: 10,20,35, 45, Q345, Q460, Q490, Q620, joalo-joalo
Mophato oa Alloy Structural Steel: 42CrMo, 35CrMo, joalo-joalo
Karolo ea Lik'hemik'hale
Kereiti ea tšepe | Boemo ba boleng | Sebopeho sa lik'hemik'hale | ||||||||||||||
C | Si | Mn | P | S | Nb | V | Ti | Cr | Ni | Cu | Nd | Mo | B | Als” | ||
ha e kholo ho feta | eseng ka tlase ho | |||||||||||||||
Q345 | A | 0.20 | 0.50 | 1.70 | 0.035 | 0.035 | 0.30 | 0.50 | 0.20 | 0.012 | 0.10 | —- | - | |||
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 | 0.07 | 0.15 | 0.20 | 0.015 | ||||||||||
D | 0.18 | 0.030 | 0.025 | |||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q390 | A | 0.20 | 0.50 | 1.70 | 0.035 | 0.035 | 0.07 | 0.20 | 0.20 | 0.3 | 0.50 | 0.20 | 0.015 | 0.10 | - | - |
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 | 0,015 | |||||||||||||
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q42O | A | 0.20 | 0.50 | 1.70 | 0.035 | 0.035 | 0.07 | 0.2 | 0.20 | 0.30 | 0.80 | 0.20 | 0.015 | 0.20 | —- | —- |
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 | 0.015 | |||||||||||||
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q46O | C | 0.20 | 0.60 | 1.80 | 0.030 | 0.030 | 0.11 | 0.20 | 0.20 | 0.30 | 0.80 | 0.20 | 0.015 | 0.20 | 0.005 | 0.015 |
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q500 | C | 0j8 | 0.60 | 1.80 | 0.025 | 0.020 | 0.11 | 0.20 | 0.20 | 0.60 | 0.80 | 0.20 | 0.015 | 0.20 | 0.005 | 0.015 |
D | 0.025 | 0.015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
Q550 | C | 0.18 | 0.60 | 2.00 | 0.025 | 0,020 | 0.11 | 0.20 | 0.20 | 0.80 | 0.80 | 0.20 | 0.015 | 0.30 | 0.005 | 0.015 |
D | 0.025 | 0,015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
Q62O | C | 0.18 | 0.60 | 2.00 | 0.025 | 0.020 | 0.11 | 0.20 | 0.20 | 1.00 | 0.80 | 0.20 | 0.015 | 0.30 | 0.005 | 0.015 |
D | 0.025 | 0.015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
a.Ho phaella ho limaraka tsa Q345A le Q345B, tšepe e lokela ho ba le bonyane e 'ngoe ea likarolo tsa lijo-thollo tse hloekisitsoeng Al, Nb, V, le Ti. Ho ea ka litlhoko, mofani oa thepa a ka eketsa karolo e le 'ngoe kapa ho feta ea lijo-thollo tse hloekisitsoeng. Boleng bo phahameng bo tla ba joalo ka ha ho boletsoe tafoleng. Ha e kopantsoe, Nb + V + Ti ha e fete 0.22%b. Bakeng sa limaraka tsa Q345, Q390, Q420 le Q46O, Mo + Cr ha e kholo ho feta 0.30%c. Ha Cr le Ni tsa sehlopha ka seng li sebelisoa e le likarolo tse setseng, litaba tsa Cr le Ni ha lia lokela ho ba kholo ho feta 0.30%; ha ho hlokahala ho eketsa, litaba li lokela ho finyella litlhoko tse tafoleng kapa ho khethoa ke mofani oa thepa le moreki ka lipuisano.d. Haeba mofani oa thepa a ka etsa bonnete ba hore naetrojene e finyella litlhoko tse teng tafoleng, tlhahlobo ea litaba tsa naetrojene e ka 'na ea se ke ea etsoa. Haeba Al, Nb, V, Ti le lisebelisoa tse ling tsa alloy tse nang le naetrojene fixation li kenngoa ka tšepe, litaba tsa naetrojene ha li na moeli. Likahare tsa ho lokisa naetrojene li lokela ho boleloa setifikeiting sa boleng.e. Ha u sebelisa aluminium e feletseng, kakaretso ea aluminium content Alt ≥ 0020%. |
Kereiti | E lekanang le khabone CEV (karolo ea boima) /% | |||||
Botenya ba lebota ba lebitso s≤ 16mm | Botenya ba lebota ba lebitso S2>16 mm〜30 limilimithara | Botenya ba lebota ba lebitso S>30mm | ||||
Hot rolled kapa normalized normalized | Ho kokobetsa | Ho chesa kapa ho tloaeleha | Ho kokobetsa | Ho chesa kapa ho tloaeleha | Ho kokobetsa | |
Q345 | <0.45 | - | <0.47 | - | <0.48 | 一 |
Q390 | <0.46 | 一 | W0.48 | - | <0.49 | - |
Q420 | <0.48 | 一 | <0.50 | <0.48 | <0.52 | <0,48 |
Q460 | <0.53 | <0.48 | W0.55 | <0.50 | <0.55 | W0.50 |
Q500 | 一 | <0.48 | 一 | <0.50 | 一 | W0.50 |
Q550 | - | <0.48 | .一 | <0.50 | 一 | <0.50 |
Q62O | - | <0.50 | - | <0.52 | - | W0.52 |
Q690 | - | <0.50 | - | <0.52 | - | W0.52 |
Thepa ea Mechini
Thepa ea mochini ea tšepe ea boleng bo holimo ea tšepe ea khabone le liphaephe tsa tšepe tse matla a tlase.
Kereiti | Boemo ba boleng | Kotulo Matla | Matla a tlhahiso e tlase | Ho lelefatsa ka mora ho robeha | Teko ea tšusumetso | |||
Botenya ba lebota ka lebitso | mocheso | Monya matla | ||||||
<16 limilimithara | > 16 limilimithara | 〉30 limilimithara | ||||||
30 limilimithara | ||||||||
eseng ka tlase ho | eseng ka tlase ho | |||||||
10 | - | >335 | 205 | 195 | 185 | 24 | - | - |
15 | - | >375 | 225 | 215 | 205 | 22 | - | 一 |
20 | —- | >410 | 245 | 235 | 225 | 20 | - | - |
25 | - | > 450 | 275 | 265 | 255 | 18 | - | - |
35 | - | >510 | 305 | 295 | 285 | 17 | 一 | - |
45 | - | 2590 | 335 | 325 | 315 | 14 | - | - |
20Mn | —• | > 450 | 275 | 265 | 255 | 20 | - | 一 |
25Mn | - | > 490 | 295 | 285 | 275 | 18 | - | - |
Q345 | A | 470-630 | 345 | 325 | 295 | 20 | - | 一 |
B | 4 ~ 20 | 34 | ||||||
C | 21 | 0 | ||||||
D | -20 | |||||||
E | -40 | 27 | ||||||
Q39O | A | 490-650 | 390 | 370 | 350 | 18 | ||
B | 20 | 34 | ||||||
C | 19 | 0 | ||||||
D | -20 | |||||||
E | -40 | 27 | ||||||
Q42O | A | 520〜680 | 420 | 400 | 380 | 18 | ||
B | 20 | 34 | ||||||
C | 19 | 0 | ||||||
D | -20 | |||||||
E | -40 | 27 | ||||||
Q46O | C | 550〜720 | 460 | 440 | 420 | 17 | 0 | 34 |
D | -20 | |||||||
E | -40 | 27 | ||||||
Q500 | C | 610〜770 | 500 | 480 | 440 | 17 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 | ||||||
Q550 | C | 670〜830 | 550 | 530 | 490 | 16 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 | ||||||
Q62O | C | 710〜880 | 620 | 590 | 550 | 15 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 | ||||||
Q690 | C | 770〜94. | 690 | 660 | 620 | 14 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 |
Mechanical thepa ea liphaephe tšepe alloy
NO | Kereiti | Tsamaiso ea phekolo ea mocheso e khothalletsoang | Thepa ea tensile | Peipi ea tšepe e halefileng kapa e phahameng ea mocheso Boemo ba thomello Brinell hardness HBW | ||||||
Ho tima (normalizing) | Ho halefisa | Hlahisa MatlaMPa | Tensile Matla MPa | Elongation ka mor'a ho robeha A% | ||||||
mocheso | Se phodileng | Mocheso | Se phodileng | |||||||
Ea pele | Ea bobeli | eseng ka tlase ho | ha e kholo ho feta | |||||||
1 | 40Mn2 | 840 | Oli, metsi | 540 | Oli, metsi | 885 | 735 | 12 | 217 | |
2 | 45Mn2 | 840 | Metsi, oli | 550 | Oli, metsi | 885 | 735 | 10 | 217 | |
3 | 27SiMn | 920 | Metsi | 450 | Oli, metsi | 980 | 835 | 12 | 217 | |
4 | 40MnBc | 850 | oli | 500 | Oli, metsi | 980 | 785 | 10 | 207 | |
5 | 45MnBc | 840 | oli | 500 | Oli, metsi | 1030 | 835 | 9 | 217 | |
6 | 20Mn2BC'f | 880 | oli | 200 | Metsi, moea | 980 | 785 | 10 | 187 | |
7 | 20CrdJ | 880 | 800 | Metsi, oli | 200 | Metsi, moea | 835 | 540 | 10 | 179 |
785 | 490 | 10 | 179 | |||||||
8 | 30Kr | 860 | oli | 500 | Oli, metsi | 885 | 685 | 11 | 187 | |
9 | 35Kr | 860 | oli | 500 | Oli, metsi | 930 | 735 | 11 | 207 | |
10 | 40Kr | 850 | oli | 520 | Oli, metsi | 980 | 785 | 9 | 207 | |
11 | 45Kr | 840 | oli | 520 | Oli, metsi | 1030 | 835 | 9 | 217 | |
12 | 50Kr | 830 | oli | 520 | Oli, metsi | 1080 | 930 | 9 | 229 | |
13 | 38CrSi | 900 | oli | 600 | Oli, metsi | 980 | 835 | 12 | 255 | |
14 | 20CrModJ | 880 | Metsi, oli | 500 | Oli, metsi | 885 | 685 | 11 | 197 | |
845 | 635 | 12 | 197 | |||||||
15 | 35CrMo | 850 | oli | 550 | Oli, metsi | 980 | 835 | 12 | 229 | |
16 | 42CrMo | 850 | oli | 560 | Oli, metsi | 1080 | 930 | 12 | 217 | |
17 | 38CrMoAld | 940 | Oli, metsi | 640 | Oli, metsi | 980 | 835 | 12 | 229 | |
930 | 785 | 14 | 229 | |||||||
18 | 50CrVA | 860 | oli | 500 | Oli, metsi | 1 275 | 1130 | 10 | 255 | |
19 | 2OCrMn | 850 | oli | 200 | Metsi, moea | 930 | 735 | 10 | 187 | |
20 | 20CrMnSif | 880 | oli | 480 | Oli, metsi | 785 | 635 | 12 | 207 | |
21 | 3OCrMnSif | 880 | oli | 520 | Oli, metsi | 1080 | 885 | 8 | 229 | |
980 | 835 | 10 | 229 | |||||||
22 | 35CrMnSiA£ | 880 | oli | 230 | Metsi, moea | 1 620 | 9 | 229 | ||
23 | 20CrMnTie-f | 880 | 870 | oli | 200 | Metsi, moea | 1080 | 835 | 10 | 217 |
24 | 30CrMnTie*f | 880 | 850 | oli | 200 | Metsi, moea | 1 470 | 9 | 229 | |
25 | 12CrNi2 | 860 | 780 | Metsi, oli | 200 | Metsi, moea | 785 | 590 | 12 | 207 |
26 | 12CrNi3 | 860 | 780 | oli | 200 | Metsi, moea | 930 | 685 | 11 | 217 |
27 | 12Cr2Ni4 | 860 | 780 | oli | 200 | Metsi, moea | 1080 | 835 | 10 | 269 |
28 | 40CrNiMoA | 850 | —- | oli | 600 | Metsi, moea | 980 | 835 | 12 | 269 |
29 | 45CrNiMoVA | 860 | - | oli | 460 | oli | 1 470 | 1325 | 7 | 269 |
a. A lumelloa ho fetola mefuta e fapaneng ya mocheso kalafo mocheso tse thathamisitsoeng tafoleng: quenching ± 15 ℃, tlaase mocheso tempering ± 20 ℃, mocheso mocheso tempering mobu 50 ℃.b. Tekong ea tensile, ho ka nkuoa lisampole tse transverse kapa longitudinal. Ha ho na le ho se lumellane, sampole ea longitudinal e sebelisoa e le motheo oa phehisano.c. Tšepe e nang le boron e ka tloaeleha pele e tima, 'me mocheso o tloaelehileng ha oa lokela ho ba o phahameng ho feta mocheso oa oona oa ho tima.d. Ho tsamaisoa ho latela sete ea data e boletsoeng ke motho ea batlang. Ha motho ea batlang a sa hlalose, ho tsamaisoa ho ka etsoa ho latela data efe kapa efe. e. Ho tima tšepe ea pele ea titanium ka Ming Meng ho ka nkeloa sebaka ke ho tloaeleha. f. Ho tima ha Isothermal ho 280 C ~ 320 C. g. Tekong ea tensile, haeba Rel e ke ke ea lekanngoa, Rp0.2 e ka lekanyetsoa sebakeng sa Rel. |
Tlhokahalo ea Teko
Sebopeho sa lik'hemik'hale:
Otlolla,Bothata,Tšonyeho,Squash,Ho Kobeha,Teko ea Ultrasonic,Eddy hajoale,ho lemoha,ho bona ha ho dutla,Mathithi